There are 296 objects for which Condition contains → from
13.10.13 Intact, missing only small chips from the interior of the lip and the foot. White and black deposits in patches all over.
13.10.2 Fragment. Single piece from the centre of the blade of the knife, missing the tip and the lower part, where it would have been attached. Worn and abraded all over, especially on the upper left of the ridged surface. Lighter coloured deposits on the other surface.
13.10.26 Intact, but missing a chunk from the rim. There is a substantial amount of greyish deposit on the rim and interior, and smaller surface chips on both the interior and the exterior. The exterior is worn in several places.
13.10.27 Intact, small piece missing from one side of the wick rest. White deposit in places, blackening around the wick rest, probably from use. Unglazed.
13.10.4A-B Two pieces, each intact, seemingly not missing any parts. The mirror is in better condition, with only a few worn and/or green patches, while the lid is damaged at the edges and is covered on the underside with whitish-green deposits. The lid has one cracked, running from the edge toward the centre.
14.9.109 Part of the body and the rim mended from a rejoining fragment. Part of one handle and two parts of rim missing. Lustre remains. White deposits around the stem. Chips to the rim. Parts of the gloss scratched off the remaining handle. The gloss on the interior is not lustrous. On the larger part of the interior thinly applied and fired red. More shiny on the stem and the underside of the foot. Noted in pencil: 'BM' and '26'
14.9.110A Very fragmentary. Part of the body, rim and one handle preserved, pieced together from fragments. Chips around the rim and the body Gloss worn on handle. On the interior gloss is not lustrous, on the exterior is still shiny.
14.9.118 Intact, a small section from the left eye to the nose is missing, chips around left arm, right arm broken. Chips on legs.
14.9.12 Paint wearing off from topside. Large chip to surface of underside - perhpas caused by an air bubble. Evidence of charring (?) on underside. No finished edges.
14.9.31 The red and white colour from the exterior surface are badly faded to only traces remain. Dot of black paint on edge and also touching exposed clay at fracture - possibly modern.
14.9.33 The white areas are almost all gone leaving only a shadow of where they were on the black background. The black is wearing from the exterior surface. Some small deposits on the interior surface.
14.9.38 Small areas of paint have flaked away from the surface allowing reserved clay to show through. Larger flake from rim. Streaky red inside. Free from deposits.
14.9.40 Streaky black paint on the underside but also covered with pink deposit. Paint has worn completely from rim. Dull black on the outer surface with some parts thinning considerably.
14.9.42 The paint on the exterior surface is in bad condition having eroded away and become dull in the places where it remains. The middle swirl of the pattern is nearly lost completely. Reasonably free from deposits.
14.9.43 Extremely streaky black paint on interior surface. Some black is wearing from the exterior surface but only towards the lower end of the fragment.
14.9.48 Red paint nearly entirely worn from rim. Some surface damage to the outer surface as paint has flaked away. Some dark deposits on the outer surface too.
14.9.49 Surface chips have taken away some paint and the part that has suffered most has the main design. Hardly any deposits apart from some dusty parts on the fractured edges.
14.9.50 Band around rim on top and both sides is fading. Paint faded red from black on the outer surface. Very sharply fracture from vessel. Many surface cracks. The fracture is in two layers and is not a clean break.
14.9.56 Eight joined fragments, with two sections of restored pattern. Black paint fading to red inplaces. Free from deposit.
14.9.73 Paint wearing and fading from exterior surface although the odd area of red detail remains. Some flakes of black missinfrom the underside.
14.9.84 Small flakes of paint worn from underside. Not at all a clean break. The colour and design on front remains in good condition.
2002.9.4 Intact and complete; wood is slightly stained and sticky (from previous adhesive) at the right side of the crossbar; the ‘leather’ drum is brittle, as are the strings, which are loose; the velvet fillet is in dissaray, with some torn stitches.
2005.3.7 Decoration on fragment is worn, fragment is from the base of the vase
2007.10.2.20 Quite a lot missing from edges of scene
2007.10.2.3 Small crack running from the top right side
2007.10.2.301 Intact, apparent damage possible from original gem stone
2008.7.113 Complete except for two small pieces, one from the base and the other from the body. Several pieces glued back together. "MN6 648" written on the bottom of the base.
2008.7.115 Rim fragment broken on four sides, possibly from a bowl/dish/tile; exterior: "5-1" written in pen; interior: "[Theta symbol] IV-V" written in pen
2008.7.170 Fragment; decoration worn throughout, worse on exterior; significant chip missing from one corner; dirt deposits throughout.
2008.7.28 Fragment. Decoration worn and chipped on both exterior and rim. "Aig Aphr" (transliterated from Greek) handwritten in pencil on the interior; indicates the Sanctuary of Aphrodite at Aegina (see Provenance).
2008.7.32 Fragment. Badly worn, especially on the exterior. "Aegina Aphrodite" (transliterated from Greek) handwritten in pencil on the interior.
2008.9.118b Good overall condition; missing one or two bits of brown foam from the top.
2014.3.1 Fragment. Patches missing from glaze/slip.
22.3.22 Single fragment. There are two spots that have been chipped off from the bottom of the exterior and ca. 5.0 cm from the top of the interior. There are also small bits that have been peeled off from the interior, which is almost covered with white plaster. Traces of plaster are also apparent on the external surface.
22.3.23 Reconstructed from many fragments, some that have fallen off.
22.3.25 Part of rim from the knob has broken. Paint is in good condition and the glaze on the black parts is still shiny.
22.3.33 Only one spot has been peeled off from the exterior, while at the interior there are four bits that are chipped off and slight scratches on the reserved band.
22.3.36 Fragmentary with numerous chips across the edges of the exterior and interior of the artefact, the face of the object and its handle. Countless, small chunks of paint are missing from both the outer and inner faces of the artefact.
22.3.37 Fragmentary with several large chunks having been chipped off from several points including the outisde's upper right section, left part, and bottom, and the inside's bottom and left parts.
22.3.38 Fragmentary and slightly chipped on the sides, with numerous patches of paint having been chipped off from the exterior. Interior of object is in much better condition.
22.3.7 One handle and part of rim missing, as is a large chip from the rim. Large piece missing from the inside. Two large marks are also on the outside of the kylix where the handle used to be.
23.11.31BB The head of the figure has broken off, as has the top of the spear. There is a section missing from the right of the shield, and the central boss has almost become detached. Te right foot is also missing. There are further fracture-lines extending at nine o'clock from the top of the figure and across the shield from the centre.
23.11.31K Slightly fragmented, but still in good condition (e.g. face visible), despite chipped-off spear; thin legs visible from beneath shield. Colour whitish-grey.
23.11.31K1 The left arm is broken off at the shoulder, and the right arm is missing from the elbow. The right leg is missing from the ankle, and the left leg is broken off at mid-thigh.
23.11.31QQQQ In good condition where preserved. The figure is missing a large part from the helmet's crest. The lower body is broken off irregularly from below the bottom edge of the shield.
23.11.31RR The top of the headdress is damaged. The left arm is missing from wrist level, and the right from just below the shoulder. The left foot is absent. The right foot is bent and slightly damaged at the tip.
23.11.31V There is a large notch-shaped section missing from the crest and top of the helmet. The arm extending to the right of the shield is bent upwards, and is missing the hand. The left leg is broken off above the knee; and the right leg is warped to the right, and is missing a foot.
23.11.31X1 The top of the headdress has broken away, and the bottom half of the figure is missing from just beneath the waistband.
23.11.31XXXX The top of the figure has broken away. The right arm is absent from just below the shoulder, and the feet are missing.
25.6.3 Intact. Streaky glaze. Paint cracking from handle. White deposits under handle and base.
25.8.1 Much repaired and restored and some re-painting at joins. Surface is very soft and dusty. Paint is nearly compleetly worn off from mouth and foot. Design is still distinguishable.
25.9.1 One handle missing, the other repaired. Badly damaged all over, with paint flaking badly from the mouth area, body and foot having been repaired extensively and the glaze is a bad condition leaving the clay exposed. Plaster inserted in base to increase stability.
25.9.4 Black paint has worn on base and mouth. Main design remains clear. Colour varies on back from pink to cream.
26.12.10 Complete but repaired from fragments, repainting at joins. Plentiful modern incisions. Colours remain apart from the white of the women's flesh.
26.12.11 Incomplete and repaired. Large area missing from side and smaller fragments missing elsewhere. White deposits inside. One handle missing. Paint remains clear and colourful on the parts that remain.
26.12.15 Repaired from many fragments and joins have been painted. Design on the outer surface remains clear and the glaze is still shiny.
26.12.17 Part of one handle missing and restored from ca. 15 fragments, with some portions filled in with plaster on both sides, and some repainting. Small chips on rim and slightly worn on foot. Interior surface remains shiny and picture remains clear.
26.12.18 Restored in two places at rim. Paint worn from handles. Design on the outer surface remains clear. Band on base worn badly. 7 drill holes in bottom of foot (taken by conservator Fred 214 for researcher)
26.12.26 The vessel has been repaired from ca. 10 fragments, however, part of the lip and three pieces from the shoulder are missing. There is also accumulation of deposits, especially in the interior, as well as some spots that have been pitted off.
26.12.2A-B Base is comprised of five pieces, rejoined. Chips from rim. Lid has large chip from edge. Paint on both parts has faded.
26.12.7 Repaired from sixteen pieces, although missing a large fragment (6.0) from one side, including one handle. Decoration very worn. Fabric roughened on one side, where it is more orange than on the rest of the vessel. Interior blackened with dirt.
26.2.19 Underside has badly worn paint as it has flaked off, although traces of white can be seen. On the topside some of the paint has discoloured to brown. Paint has worn away from rim.
26.2.27 Bands on underside badly faded to light brown. Chip missing from surface. Similar fading on black paint on topside.
26.2.28 Painted bands on underside are wearing away considerably compared to the topside which has retained most of its colour apart from some white but it is now a little dull. Surfaces are all still smooth with no significant damage.
26.2.66 Single fragment from the floor of the bowl. Slight chips and scratches.
26.2.87 Single fragment, roughly rectangular, from the shoulder. Light brownish-grey deposits on interior, slightly scratched on exterior.
26.4.1A-B Much repair to lid which was in fragments but now almost complete apart from small piece of rim from underside. Paint dull on lid but remains clear on bottom piece. Two feet have been repaired and repainted and small part of lower rim is missing.
26.4.2 Complete but stuck back together from eight(?) seperate pieces. The glaze both inside and out is very worn, and the rim shows chipping and flaking. The inside of the pot is not completely smooth and there is a grey/white deposit, especially around the inner rim. Both of the handles have a lot of the same grey/white deposit on them, as well as big worn patches on the glaze. There is more deposit on the outside, especially around the foot. The surface outside is also in fairly bad condition, the surface revealing lots of small scratches and chips. The top of the foot has two significant chips in it but other than that it is in good condition, showing only small cracks running through the glaze in the well on the underneath of the foot.
26.4.3 Lid restored from three chipped fragments (lid). Stamnos-pyxis also restored: both handles have been reattached.
26.4.4 Restored from many separate pieces. Glaze on the rim is slightly worn, as are the handles. The outer surface is worn. There is a greyish-white deposit in patches all over the surface, especially around the spurs and the reserved area of the main zone, as well as the top of the foot. On the top ridge of the foot, there is a hole. Colour on the inside of the pot has mostly worn away, leaving only more of the same grey deposit. Lid missing.
26.7.1 Intact. Small crack forming at one handle. Streaky paint on bottom of body, showing red through black/brown. Paint is wearing from outside of body on one side particularly. Dusty white deposits on exterior surface as well as uneven lumps in the walls.
26.7.10 Incomplete. Apart from the head missing, there is little damage. There are small holes and scratches on the surface, front and back. The white slip has almost completely worn away, evident now only in small areas.
26.7.14 Fragment. The gloss on the rim of the fragment is a little worn and the surface on both sides shows small scratches. On the handle, there are a couple of flakes missing, and a small hole, possibly from an air bubble. The gloss on the inside is much more worn, with big flakes missing, with a couple of substantially longer scratches. There is also a yellow/grey deposit all over the inside of the fragment.
26.7.2 The vessel consists of two pieces and is repaired. The stem and part of the body are joined together. There are five bits missing from the rim and upper body, as well as bits from the joining parts, where there is also a gouge. In few spots the colour has been peeled off (body of bull, handles).
26.7.6 Two parts of mouth missing. Design still clear. Some flakes from body.
26.7.7 Comprised of two rejoined pieces; join still visible across the back and belly, crack running from right ear to join. Body covered by white and grey depoit, feet are brown and shiny.
27.4.1 Comprised of four or more fragments, rejoined, with two large fragments missing from the rim. The surface is weathered, with chipped glaze on the exterior and the handles, worn glaze on the rim and body, and slight pinkish-red deposits on the underside.
27.4.11 Repaired from many fragments, but heavily restored in the lower part.
27.4.12 Complete; repaired from seven pieces. The rim is uneven, and contains two small but definite chips. All over the surface are small scratches and patches of wear. The pattern on the rim contains few subtle patches of red, the same colour as patches on the handles. Patterns in the centre of the bowl appear to have rubbed away in patches. Underneath, the patterns remain more prominant, but again small patches of wear are evident, especially around the rim. Inside the foot are greyish white deposits, that are also found underneath the rim in small patches near the handles.
27.4.13 Complete and intact. Slight chip on lip, colour of decoration faded from black to red.
27.4.5 Intact. The rim, inside of the bowl and handles, all show evidence of wear, and there are considerable patches where all of the glaze has been removed. There are also small chips to be found on the handles, and on the inside of the rim. Where the glaze has been rubbed away, it has revealed a grey colour. There is also a thin crack running from the edge of the rim, to half way down the first black band. The well in the centre of the bowl is also slightly worn, to reveal a whitish grey colour, as well as a small crack running across the side. On the underside of the bowl, there is more evidence of general wear, including a chip just under the rim next to one of the handles. The bottom rim of the foot also reveals small chips, as well as a crack running across the middle.
28.6.1 Intact. Crack around the base of the neck. Small chips of paint from lip and mouth and handle. Main design is clear and the glaze remains.
28.6.6 Damage to one handle almost breaking the circle. Complete handle has deposits (perhaps from burial). Paint is very worn and in most places only staining remains. For such a fragile rim it is in excellent condition with no chips.
28.9.1 Large fragment missing from figured panel, and many also from plain black parts. Much repainting and restoration. At least one handle and the foot are alien. Handles do not make direct join.
29.11.13 Missing (part of) head. Large areas of brownish-grey deposit all over body, with areas of white slip showing through in some places and chipped off elsewhere. On stomach, in between two front legs, is a small hole, perhaps from the firing process.
29.11.3 The neck and handle have been repaired and rejoined to the body. There is a scratch on the upper body surface and two tiny bits that been chipped off. The vessel looks burnt (apparently from a burnt grave).
29.11.6 Reconstructed by many fragments, there are a few gouges and many small bits of colour have fallen off, especially from the interior.
29.5.1 Intact. Large flake from surface taken from towards base. Colours remain strong. Black paint at bottom of body has suffered the worst.
33.4.1 Complete, but not intact. One handle and part of rim restored. Stuck back together from six/seven pieces. Decoration around rim and handles is worn in patches, with small chips in the surface. Small gaps where the pieces have been rejoined. A few scratches are evident in surface of main zone. Top of stem is rough to touch. Resting edge of foot has chips in it, inside the foot has some sandy deposit and a crack across the centre. Inside the body, the gloss looks silvery, with small scratches on it.
33.4.3 There are some bits that have been pitted off and some spots that have been chipped off, especially from the rim (exterior and interior), the neck and the handle. There are also some scratches on the white colour area, whereas the foot has been repaired and rejoined to the body.
34.8.1 Neck has been repaired. Object is complete. Surface is badly damaged and paint has suffered from age on all areas. Nike herself, remains clear and undamaged.
34.8.12 The handle has been rejoined to the lid, whose colour has been peeled off from many spots (underneath). The body has been reconstructed by 6 fragments. There are some bits missing at the joining points of the fragments, as well as from the incurved surface of the rim. Few bits have been chipped off from the base. The colour is wearing off from many spots, especially at the body. The deposits under the lid and inside the body almost obscure the glaze.
34.8.9 Slightly chipped around rim, especially one large part missing from the upper edge; decoration worn and scratched in places; some light gray deposits on the inside and by the handle attachment; slight white deposits on the bottom.
35.4.2 Complete but comprised of rejoined pieces from the neck, mouth and handle.
35.4.4 The handle has been repaired (rejoined with the body at its spring). There are many bits that have been pitted off from the vessel, especially at the lip and handle, as well as a scratch below the handle. Approximately one third of the vessel (lip, neck, handle and left side of almost half the body) is silvery glossy. The rest is glazed.
35.4.6 Chips from rim and a crack runs down one side. Glaze worn in small areas on handles.
35.5.15-19 Six fragments, which may not all be from the same cup
37.11.5 Handle has been repaired; rim chipped; Gloss flaked off at places on the body, handles and the resting surface; small crack in centre of underside. Intact but assembled from 2 pieces. One handle, part of rim and body assembled.
37.11.8 Only few bits pitted off at the body and two bits chipped off from the base. Many sediments and salts.
37.7.2 Intact but base of handle coming away slightly from the shoulder. Good condition design of siren and clearly incised lines. Some areas of red on handle ande below, possibly where darker paint has worn away. Some chips to underside of the mouth.
38.12.1 Glaze remains shiny and the paint has only worn away in small sections at the back. Large chips taken from the front of the object obscuring parts of the picture.
38.4.5 Incomplete: neck of jug is missing from the shoulder upwards; the handle is missing; detail slightly faded. Some white deposit.
39.1.1 Most of black glaze flaked off from upper part of vase.
39.9.7 In two places, part of the rim has broken away. There is also a deep crack in side A, from the part of the rim next to one handle, almost up to the part where the other handle springs from. Colour has peeled off in some places, especially the interior. The body of the satyr to the right of the amphora was a bit damaged when paint was still wet.
42.9.1 Almost half of stephane missing on side B, while the decoration of its remaining part is scraped off almost completely.No decoration on the neck. Deep crack from the beginning of the missing stephane down to the Krater's shoulder. Body pitted over entire surface, although side A is in better condition, with the exception of a gouge under the right arm of the left maenad. Incrustations around the chipped base.
43.11.2 Intact but worn and missing a large chip from the rim.
44.1.1 Intact (tiny bits have chipped off from the rim). There is large loss of paint on the whole of the vessel (parts of the top surface, as well as the greater part of the lion design is lost, as paint has worn away).
45.10.1 Spout has been rejoined, and rim has been chipped. Gloss has faded from red decoration.
45.10.10 Sixteen fragments that belong to the same kylix. There are parts of the rim and body (a,b,g,k,l,m,n) of the body (c,h,i,j,o) of rim, body and part of the handles (d,e,f), and the base (p). a) Should be rejoined to b. Interior: Layer of white plaster and small bits that have been pitted off. Exterior: Traces of white plaster and a spot that has been chipped off. b) Should be rejoined to a and c. Interior: White plaster and a large spot that has been chipped off. Exterior: Traces of white plaster and small spots that have been chipped off from the left and bottom edge of the fragment. c) Should be rejoined to b. Interior: White plaster and two areas that have been chipped off from the top edge of the fragment. Exterior: White plaster and two small spots that have been chipped off. d) Should be rejoined to e. There are two spots that have been chipped off from the rim and bottom part, as well as some pitting off (rim). Exterior: White plaster and a large spot that has been chipped off from the upper part of the body. The handle is also missing, apart from its lowest part. e) Should be rejoined to d. Interior: There are two spots (rim, bottom) that have been chipped off. Exterior: Traces of white plaster and a spot on the left that has been chipped off. Most of the handle is also missing. f) Should be rejoined to g and h. Interior: There is a layer of white plaster, few tiny bits that have been pitted off and a spot on the left that has been chipped off. Exterior: There is white plaster, a spot that has been chipped off from the top right side and some peeling off of the colour on the handle, whose largest part is also missing. g) Should be rejoined to f and h. Tiny bits that have been pitted off from the exterior. h) Should be rejoined to f and g. Traces of white plaster on the exterior. i) Interior: Layer of white plaster. Exterior: Traces of white plaster. j) White plaster on the interior. k) Interior: Layer of white plaster. Exterior: tiny bits that have been pitted off and slight traces of plaster. l) Could be rejoined to n. Interior: White plaster and a spot that has been pitted off. Exterior: White plaster and some bits that have been pitted off. m) Interior: Layer of plaster and a large spot that has been chipped off from the bottom left edge. Exterior: Traces of white plaster and a spot that has been chipped off from the bottom right edge. n) Could be rejoined to l. Interior: White plaster. Exterior: Traces of white plaster, some pitting off and a large spot that has been chipped off from the decorated area. o) Traces of white plaster on both sides. p) Slightly faded, with a few surface chips on interior and on foot.
45.10.14.1 Fragment from the rim and neck. There is white plaster on both surfaces. Colour has been pitted off, especially on the external surface of the rim, and peeled off from several spots. The decoration is fadded away on some areas.
45.10.14.2 Single fragment from the rim and neck of an amphora. There is white plaster on the rim and side surfaces of the fragment, while a thick layer was applied on the external surface of the neck. The decoration is damaged.
45.10.2 One handle missing and large sections missing from rim. Large sections of grey deposits covering up the black paint.
45.10.20 There are six fragments probably from the body of the same closed-shape vase (amphora). i) Small bits of the colour have been peeled off and few small spots have been pitted off. ii) The fragment has been burnt. Tiny bits are pitted off. iii) The colour has faded away and has been peeled off from spots. Chips are missing from the edges. iv) The colour has faded away on the contour of the motives. v) The fragment is burnt. Bits of colour have been pitted off. vi) Bits of the colour have been pitted off, especially at the top and right side of the fragment.
45.10.21 Two small fragments that Annie Ure has catalouged as coming from same vessel.i) chips along the edges of the exterior of the fragment as well as on black decoration, White deposits on both external and inrternal sides. ii) exterior shows damage and places where the decoration has rubbed off
45.10.22 There are only 18 fragments preserved from this vessel. These consist of parts of the rim, neck, shoulder and body. a: It is repaired from two fragments, rejoined. Part of the rim (the smallest part of two), neck (including the spring of a triple handle) and shoulder (these consist the second part of this fragment). The fragment is chipped off in many areas (rim: ca. 5 spots/ interior of neck: ca. 10 spots/ neck: ca. 4 spots. There are also gouges on the joining points of the two parts. The upper part (bigger part) of the handle is missing. Apart from tiny bits that have been peeled off from the interior and few deposits, the glaze and colour are preserved in a good condition. b: It consists of three rejoined parts from the vessel's neck. Few bits are missing on the joining point and a spot has even been chipped off, there are deposits and cracking of the colour on the interior, as well as another spot that has been chipped off. Three shallow carvings are also apparent. c: It consists of three parts joined together (two big ones and a small one). Deposits on the interior, three scratches on the exterior, tiny bits that have pitted off and spot that has chipped off from the lower left end. d: Part of the body, colour has fadded away in some spots, and a part has been peeled off. Deposits. e: Part of the body. Deposits but in very good condition, apart from two areas that are chipped off and small bits that are pitted off. f: Part of the body. Apart from deposits in a very good condition. g: Part of the body. Deposits, otherwise in a very good condition. h: Part of the body. Few, tiny bits have been peeled off, also few deposits. i: It consists of two parts of the body. ca. 5 bits have been pitted off and three spots are chipped off; deposits. j: Small fragment in very good condition. k: Small fragment from the body; deposits. l: Small fragment from the body; deposits.
45.10.23 Thirteen fragments from the shoulder, the body, the foot and the base of the same vessel.
45.10.31 very damaged. Came from a lot that had been bombed during the Blitz in 1945
45.10.4 Incomplete and repaired. Chips removed from rim. Glaze lost.
45.10.9 Ten fragments that probably belong to the same vessel. a) Tiny bit of the vessel's lower neck, part of the shoulder and the spring of the handle, which is missing. There are scratches on the exterior and two bits that have been chipped off. Deposits and plaster? on the interior. (The rest of the fragments are from the vessel's body) b) Should be rejoined to c. White plaster on the exterior and traces of it on the interior. A small bit has been chipped off. c) Should be rejoined to b. White plaster on the exterior and traces f it on the interior d) Few deposits on both sides and a small bit that has been pitted off from the exterior. e) Few deposits on the interior and traces of white plaster. A tiny bit has been chipped off from the exterior. f) White plaster and deposits on the interior. Two bits have been chipped off from the exterior. g) The decoration appears as if it has been scraped off and there is a spot that has been chipped off from the exterior. h) A small spot has been chipped off. Deposits and traces of plaster on the interior. Added white colour has fadded away. i) There are adhesives on both sides and white plaster on the exterior. The decoration looks as if it has been scraped off, a tiny bit has been pitted off and a small spot has been chipped off. j) Traces of white plaster, especially on the interior. There is a small spot that has been pitted off.
45.6.10 Intact but missing a small chip on the rim and a large chip from the foot. One further very small chip on the rim. Surfaces are slightly pitted with red showing through black surfaces.
45.6.16 Black gloss is still shiny at parts. Large flakes of clay have come away from the lower part of the body. Paint flaked off on mouth, handle, on a large part of the body decoration, shoulder and foot.
45.6.18 Large chip taken from body but not creating a hole. Paint around mouth and handle has flaked off. Bad quality glaze fired brown on the top of the rim, handle and neck.
45.6.38 Intact, but missing two chips from rim. There are some deposits on the lower part of the rim.
45.6.47 Small chip on rim. Glaze worn completely apart from in two very small areas. Areas of grey deposit over surface.
45.6.57 Complete and intact. Black glaze worn away apart from on neck.
45.8.1 Small parts pitted off from the whole of the surface.
46.5.1A-B Complete. Large missing from the edge of the lid, and two large chips on the body, as well as smaller ones. Some scratching and weathering to the body. Decoration faded.
47.10.3A-B Lid intact and complete except for a large chip missing from the rim. Lekanis comprised of three or more rejoined pieces, rejoined with some plaster restorations, preserving one handle, most of the foot, and approximately 2/3 of the body of the bowl. The surface on both parts is somewhat worn, with whitish-gray patches, chips and scratches, and some black glaze eroded.
47.2.31 Intact, although left arm missing and a section from base. Facial features well preserved.
47.2.5 Assembled from 3 fragments. Missing one handle, some of the rim adjacent to that handle, and a large patch of the bottom of the bowl, adjacent to and slightly overlapping the stamped decoration. The other handle, previously broken off, with another rim fragment, has been rejoined. Some patches missing and scratches around the body on the interior and exterior, rim, handles over; slight deposits on the exterior.
47.2.6 Intact and mended from 6 fragments. Small part of the ring of the base is broken off. Small chips on rim. Glaze worn off at a spot on the interior. Gloss is not lustrous especially on the interior and the lower part of the body of the exterior. Deposits on the underside of the foot.
47.2.7 Mended from a number of joining fragments. Small parts filled in with plaster (especially on left side. Gloss flaked off on part of the handle,rim and body. It is not lustrous. Towards the foot, thinly applied gloss that leaves parts of the clay to be seen.
47.2.8 Rim and side of bowl comprised of three rejoined pieces, although lustre and stamped design remain clear. White deposition on the ring foot. Gloss flaked off from part of the rim and the body. Gloss is not lustrous.
47.6.2A-B About two thirds of the top rim of the lid are missing, while one third of its side surface has been reconstructed. The rest of the lid has been repaired through the joining of three fragments; the figural scene has faded. The body is almost intact, only a small bit has been chipped off from the rim, three tiny bits have been pitted off and a small part of it has been reconstructed. The rim of the base also has some pitted off parts.
47.7.2 Almost intact apart from a chip to the mouth; slightly chips on the surface, and worn on the top of the handle and the mouth. Animals remain clear and the gloss is shiny apart from around base which is a little streaky.
48.12.1 Intact but gloss very badly worn inside and out. Air bubble type holes, perhaps from firing.
48.12.10 Mouth missing. Some flakes of paint from body have left a rough surface. Part of the white paint flaked off. Gloss is silvered on the lower part of the body. A small chip on shoulder. Gloss flaked off the handle and part of the decoration on the body.
48.12.11 Half of mouth is missing. Paint worn on handle, but remaining iridescent and lustrious on body. Small chip from base. Repaired on back of body and cracks on front at shoulder.
48.12.12 Intact. Paint badly worn on mouth and handle. Small chips from body towards foot.
48.12.3 Intact but missing several large chips from the rim, one from the handle joint, from the foot. Interior pitted so red fabric shows through. White deposits on the interior in the area under one handle.
48.2.2 Nine rejoined fragments, pitted on interior and exterior; decoration missing from interior of handles.
48.4.1 Complete, but stuck back together from six seperate pieces. The rim shows one definite chip, and several small ones. The leaves on top of the rim have worn away in patches. The main zone also shows patches of wear, the surface revealing different colours, some paler clay, and some more orange. A white deposit is evident on the thick black band above the foot as well as some small scratches. The thin black band around the rim of the foot has mostly worn away. Inside, the black has scratches and flaked away to reveal the reserved clay. There is also more white deposit on the inside walls of the pot.
48.5.2 Major repair work done on one side and to neck consisting of nine pieces. Large chip to foot. Small chips to body. On most part of the figure decoration, handles, foot and mouth, black is fired to brownish. The gloss has flaked off from part of the figures, mouth and neck. White deposits around the mouth.
49.10.1 intact, decoration almost completly lost apart from small patch showing a broken or hook meander.
49.4.1 The mouth is a little chipped and the neck has been repaired. There are bits missing from the shoulder, too. The largest part of the white bands has worn away, as has some of the paint on the foot. There are white and gritty deposits in the mouth and under the handle. The glaze below the meander is streaky. There is also colour loss on the back of the body but this appears to be due to firing.
49.4.2 The vessel is repaired but incomplete, since a large part (1/4) of foot is missing. The lip is also repaired (from two fragments), but a small part is still missing. There is also a cracking on the interior of the rim. Many small bits have been pitted off from the vessel and a few small spots have been chipped off. Additionally, part of the paint on side A is wearing off. There is plaster on the interior of the mouth, as well as plaster and adhesives on other surfaces ((area underneath the rim and on the one handle) and resting surface bears traces of plaster as well and deposits?
50.10.1 Complete but the neck and the body have been mended from a number of joining fragments. Some repainting. Deposits inside. Large part of the painted decoration fired brownish-reddish. Worn on many parts. Small chips and scraches on the body and a chip on the resting surface.
50.10.4 The rim has been reconstructed from 2 fragments repaired. The handle has also been rejoined with the vessel and the whole of the upper part (from rim to end of shoulder) has been reattached to the body. The glaze is shiny in places but has begun to crack in others. There are also deposits on the rim, neck, shoulder and foot / base. Several bits have pitted off from the body.
50.10.5 Intact. White deposits on base and underside of body, rim. Some paint chipped from rim, handles, interior of the body. On the exterior, gloss remains lustrous at parts, but on the interior is worn.
50.10.6 Intact. Large piece rejoined from side A, but doesn't obscure decoration. Some pitting and chipping all over body. Small chip in rim by one of the handles.
50.12.50 Single fragment preserving the upper part, from the head to the lower part of the chest. Chipped at the top. Decoration is almost rubbed off in many places.
50.4.10 Broken across bowl in transit from Leicester, and repaired. Gloss remains shiny and silvery. Bowl assembled form 2 fragments. On the exterior, it is not at parts lustrous, while at parts it is fired to dark brown.
50.4.16 Comprised of two pieces, rejoined at stem; missing a large chip from the top of the foot. Gloss eroded on rim, top of stem, and foot, but retains lustre.
50.4.22 Clay is suffering from corrosion, many deposits over surface. Detail lost on some of the features of the ram. Part of left ear broken. Handle broken and rejoined.
50.4.23 Intact, slight anomaly on the left hand side of the nozzle, ware all over the lamp with considerable amounts of wash missing. Outer ring around the discus is misshapen in one place, probably happened in manufacture. Protruding form on the discus has been broken off. Grey deposit in places, blackening at the end of the nozzle, probably from use.
50.4.4 Comprised of four fragments, rejoined. Gray adhesions on the surface, much gray and white flaking off from inside and outside. No other traces of colour remain.
50.4.6 Mended from a number of joining fragments. Small fragment from the body is missing. Gloss is quite lustrous on the exterior, but rough and worn on the interior and the underside of the foot. Chips around the rim and the body. Deposits on the underside.
50.4.7 Mouth and upper part of the neck assembled from a number of small fragments (repaired by Cameron Hahn, 17.08.2005). Large chip on shoulder, smaller on neck and small chip on foot. Quite ggod quality of glaze that retians its shine. Net pattern designe dcarefully although the maendar is quite rough. Scratces on the body.
50.4.9 Mended from a number of joining fragments but incomplete; noticeable piece missing from front of vessel. Lustre remains. Deposits on base. Interior worn with small amounts of grey deposit. Slight wear and small chips on the body and the resting surface.
50.5.6 Intact. Paint appears extremely dull and matt despite being badly worn. Flaked off from most part of the decoration. Peach colour on small areas inside and corresponding exterior surface. A number of chips on the lower part of the base. The larger allows the clay inclusions (white stones) to show through.
51.4.2 Five fragments of the rim have been pitted off, ca. 5 smaller ones from the interior of the neck and one from the body.
51.4.3 Two parts have been peeled off from the joining point of the neck to the body, one bit has been chipped off from the bottom of the body and four from the interior.
51.4.4 Chips missing from the rim (ca. 7, including damage on the meander pattern) and the neck (ca. 5). There are also small bits missing at the joining point of the two parts of the fragment.
51.4.6 Two fragments, rejoined, from the body and rim of the cup, in the shape of an elongated hexagon. Chipped on the breaks; slightly worn on the interior; slight gray adhesions on the upper left corner of the exterior and the lower part of the interior.
51.4.8 Complete. The body mended from a number of joining fragments. Glaze flaked off on the top of the rim, body and handles. Small chip on one of the horizontal handles. The main zone decoration remains similarly intact, except for a few scratches on the surface, and in small patches, a misty light grey deposit. There is also some of this deposit around the ends of all three handles. Thinly applied glaze, especially on the back side of the vessel, allowing for the colour of the clay to be seen. On the resting surface of the foot is a chalky white deposit.
51.7.12 One handle lost. Paint chipped at handle and inside. Glaze lost from interior walls.
51.7.3 Intact. The rim mended from 2 fragments. Small chips to rim. Lustre remains although some paint has chipped away around rim, handle. Slight scratches and chips on body. White deposits on the underside of the foot.
52.3.1 Complete and repaired. Glaze remains. Body and neck mended from a number of pieces. Small chips around the neck. White deposits on the underside of the foot and on the top of the rim.
52.3.2 Body and base surfaces are terribly damaged with large chunks missing although these do not go all the way through. Paint worn from inside mouth. Glaze and paint remain relatively undamaged on areas that have not been chipped away.
52.3.3 Incomplete but cleaned and restored at the Ashmolean by Rickard. Body is compiled of fragments with missing parts filled in with plaster. Five separate unattached fragments. Large chip from foot. Neck, mouth and rim are largely restored but some loose fragments remain. Ruddled areas worn and black paint is scratched.
52.3.4 Comprised of 40 or more pieces, rejoined, with some restroations, but missing handle and lugs on one side. Much repainting on handle, rim, and interior, but animal details are largely original. Complete apart from one of the handles. It has been reconstructed from many pieces and parts are modern fillings.The contours of the black bands inside are fired red. Badly restored.
54.8.1 Piece missing from lip and restored with plaster. Some flakes of the surface are missing resulting in exposing the clay and leaving an uneven surface. Hole in bottom of cup. Black faded or fired to light brown in places. Scratches on the underside.
56.8.5 Piece broken off rim and one or two chips from edge. Small chip on the top of the knob. Decoration is excellent condition. Handle appears to have been reattached. Browny-black deposit (?) in rough circle on underside beneath knob handle. Gloss of good quality, still lustrous.
56.8.8 The vase is reconstructed from many fragments. Bits have peeled and pitted off, and there are a few gouges. Gloss is lustreless, parts flaked off on the interior, handles, foot. At parts of the rim and the handles fired brownish.
58.2.4 Intact apart from a section of the spur which seems to have broken off. There is a deep crack on the inner side of the handle at the bottom. Also a dent in the body by the base of the handle, and the base is misshapen, both of which may have been done before firing (?). In a few areas the paint has been worn, and there are minor chips.
59.2.7 All that remains of the mummified cat is the head and neck, from which most wrappings have been removed. The head is in a good state of preservation, showing whiskers & teeth. Enclosed note written in pencil on the back of a printed piece of paper is also well preserved and legible. Cork stopper, seemingly original to the 1890s acquisition of the head, is covered in newspaper which is also well preserved and legible.
60.1.1 Two large chips on the rim; glaze missing from edges of lip and foot; terracotta worn and grainy.
61.6.5 Lid: complete and intact, with slight chips to rim; surface inside and out marred with small white deposits, dark stains, and scratches and chips. One-handler: intact and complete except for a chip missing from the lower part of the exterior body, just to the right of the handle. Black-glaze pitted and scratched on interior, with slight white deposits.
68.12.1 Single fragment from foot
71.12.2 Fragment. Broken at the edges, bronze slightly corroded. Green with some rust on the underside. The colour varies from red, to reddish brown and green.
71.12.6 Large parts of bronze have broken away from the sides of the curved section. The most important aspect to note is the deterioration in colour to blue, green, black and brown. Only in a couple of areas does the true colour of the bronze show through. Deposits under the handle where it joins the body. Small hole to one side of the curved section.
73.9.23 The surface of the fragment appears to be in fairly good condition, except for a few small areas of grey deposit. The back of the fragment varies in colour, moving from red to black and then grey. The surface however is again in fairly good condition with no real evidence of wear except for a few small scratches.
74.7.5 Complete. Has been glued back together from two pieces. Is entirely covered by dark deposit, possibly from the action of fire. Thought to be from a burnt grave. There is a lot of flaking, revealing white. The features of the face are distinguishable, but are worn in places. The back is much lighter in colour, but still covered in brown/green deposit and feels rough to the touch.
76.6.1 Lip and frontal part of the neck is chipped. Handle assempled from three fragments. Black paint is dull and has been flaked off largely. The surface has a 'dusty' appearance.
78.12.11 Intact, handle is missing the top half, decoration is very worn. Wash is mostly intact with a white deposit in areas. Very slight darkening around the tip of the nozzle probably from use.
78.12.13 Intact, part of the base is missing, hairline fracture radiating from this damage. Wash is worn, especially on the decoration and base. Large amount of grey deposit all over, interior and exterior.
78.12.17 Intact, small chip on rim, blackening at the end of the wick rest, probably from use. Large amount of white deposit all over.
78.12.19 Intact , hairline cracks on the surface of the shoulder, wash worn on the discus. Folds of clay still apparent from the joining of the upper and lower discus. Small amount of discolouration and blackening on the nozzle, probably due to use.
78.12.21 Intact, upper right half of nozzle is missing, long hairline crack reaching down into the centre of the base from ths damage. Signs of use visible on nozzle. Fracture around the edge of the discus continuing along the nozzle to the wick hole. Brownish red wash is worn, large amount of white-grey deposit
78.12.5 Intact, wash is worn and there are slight chips on the shoulder. Slight blackening at the tip of the nozzle, probably from use.
79.1.12 Intact, small chip to the end of the spout. Wash is wearing, especially at the back of the lamp. large amount of deposit visible through the wick hole. Small amount of deposit on the exterior, more on the base. Nozzle tip blackened, possibly from use.
79.1.17 Complete and intact but surface very worn. Handle and nozzle blackened possibly from burning. White deposit in places. Slight depression on left hand side of the nozzle shaft.
79.1.2 Intact, small section missing from the surface of the lamp on the left hand side causing hairline cracks. White and grey deposits over much of the surface of the interior and the exterior.
79.1.4 Intact, chipped on the moulded ring around the discus, decoration worn. Wash is fading especially on the underside. Tip of nozzle blackened, probably from use.
79.1.8 Complete, decoration very worn, filling hole is irregular; this may be due to it's production. Nozzle tip is blackened; probably from usage. nozzle end is scored with many lines. White deposit in places.
83.2.3 Fragment covered with black deposit, clearly broken off from another object, and is rough and bumpy, likely owing to damage caused over time.
83.9.6 Single fragment. The reserved areas on the base of the foot are chipped. The black gloss from the interior is flaking around the edges.
84.5.1 Complete but reconstructed from three parts, joins visible (adhesive visible on reverse). Chip on top edge between horse and riders three and four.
84.8.1 a) There are some spots that have been pitted off, especially at the edge of the rim, as well as some shallow scratches. There is a bit that has been chipped off from the neck and few deposits. b) Many small spots have been pitted off from the edge of the rim, few bits have been chipped off from the neck and there are traces of deposits. c) Should be rejoined to d. Few parts have been chipped off and there are deposits. d) Should be rejoined to c and e. Tiny bits have been peeled off, there is a cracking on the internal surface and traces of deposits. e) Should be rejoined to d. There are some scratches on the exterior and some parts have been chipped off from both sides. f) Should be rejoined to c. Some spots have been chipped off and at some areas the colour has been peeled off. g) Tiny bits have been pitted off, two spots have been chipped off. h) Traces of plaster, especially on the interior. The colour has been peeled off from some areas and there are spots that have been chipped off. i) Traces of white plaster, streaky black on the interior andtwo small spots that have been chipped off. j) White plaster on both sides, streaky black on the interior and many spots that have been pitted off from the exterior. k) Should be rejoined to l. Traces of white plaster on the exterior. l) Should be rejoined to k, m and n. Few, small bits have been pitted off. m) Should be rejoined to l, n, p and o. There are some scratches on the external surface, as well as some bits that have been pitted off from both sides. Two spots have also been chipped off from the interior. n) Should be rejoined to l, m and o. Many shallow, small scratches and few, tiny bits that have been pitted off. Also, a spot that has been chipped off from the external surface and a smaller one from the internal. o) Should be rejoined to m,n and p. There are some scratches on the external surface, some tiny bits have been pitted off and a spot has been chipped off. p) Should be rejoined to m, o and q. Few tiny, shallow bits have been pitted off. q) Should be rejoined to p and r. Two small spots have been chipped off from the interior. r) Should be rejoined to q and possibly s? s) Could be rejoined to r? t) Should be rejoined to o. There are some tiny bits that have been pitted off from the exterior,as well as a shallow gouge and two scratches. u) Should be rejoined to v. White plaster on the interior. v) Should be rejoined to u and w. There are some scratches, some bits have been pitted off and few spots have been chipped off. w) Should be rejoined to v and possibly x? Some scratches on the exterior and a shallow gouge. x) Could be rejoined to w? There is a shallow gouge and three spots that have been chipped off from the exterior. y) Tiny bits have been pitted off. z) Small bit has been pitted off. aa) Should be rejoined to ab. Bits have been pitted off and surface seems to have been scraped off? on the top. ab) Should be rejoined to aa and ac. Bits have been pitted off and colour seems to be scraped off? on the top. ac) Should be rejoined to ab. Bits have been pitted off and colour seems to have been scraped off on the top. ac) Should be rejoined to ab. Bits have been pitted off and the top seems to have been scraped off? ad) Small spots have been pitted off.
E.23.1 Intact, some detail missing from the carving. Several chips throughout, some large, i.e. on both bottom corners.
E.23.10 The actual pallete is covered with many small scratches, which, combined with the reside of pigments, have left it a light grey colour. There are chips missing from two corners of the base, one larger than the other, with two other chips in diagonal corners of the trapazoid.
E.23.12 There is quite a large chip on one corner, and a chip removed from the same side. There is quite a large amount of black deposit all over the object obscuring it's natural colour.
E.23.17 A large amount of skin coloured paint has chipped of, particularly around the bottom and edges of the object. The paint on the chest is quite well preserved. There is a large fragment missing from the right shoulder which also removes part of the lower right hand side of the pace. The nose and eye work has been removed or fallen off. A large amount of black paint has chipped of the top of the object. There is also a hole in top of the head and a large crack originating on the lefthand side of 'hair' and ending near the base of the face.
E.23.18 Intact if not complete. The areas where parts of the headdress has fallen off is quite worn. There are three deep holes in the headress that are symetrical about a crack that goes from the top of the headdress to the mouth. There is also a second crack on the right hand side from top to the base of the head, going through the eye.
E.23.2 Single fragment, preserving the top of the stele, chipped at the top, with several shallow scratches on the surface. One crack extends from the edge into the uraeus of Re-Horakhty.
E.23.22 Intact, there is a large chip in the lip and several much smaller ones also. The surface is very coarse and covered in shallow scratches. There is also a noticeable chip missing from the foot. There is a deposit in the bottom of the orifice.
E.23.28 Intact and complete, with a large chip missing from the lip. There are two noticable stresses near the foot, one which forms a hole the other a shallow chip.
E.23.3 Intact, although figures likely from other boat models. The paint on all figures has degraded and does not merit individual description. Detail is missing from the bow and stern of the boat where the wood has degraded so much. There is also fissures in the wood of the deck of the boat.
E.23.37 Complete but not intact. Small chips in the lid. The lip and mouth are detatched from the body. Large crack in the lip, deposit on the shoulder, small chips in the base.
E.23.38 Intact, it is clear from the top and bottom part of the artefact that it has been removed from a larger object, since they appear to be thinner than the rest of the object and therefore look like 'connectors' of some kind. There appears to be very little degradation of the wood. There are some remnants of a white pigment on the lower half.
E.23.43.2 Intact and copmplete, there are several impurities in the glaze, most notably a long line of black substance that appears to be stuck to the bead as it very raised from the surface.
E.23.43.7 Intact, but there is a large chip missing from one of the ends. Also the glaze is highly worn leading to a rough surphace.
E.23.52 Intact and complete apart from chip off the corner of the base. Much of the glaze remains but in areas where it has rubbed of the green pigment is also missing.
E.23.55 Intact and complete, the glaze is gone leaving a rough surgace, a large amount of the green pigment is missing and some details from the mouth, also the inscription is incomplete.
E.23.61 Intact and complete. The only detail missing is the curl from the end of the line originating from the underside of the eye. The glaze has totally rubbed away.
E.62.10 Intact if fragmentary, the wood is somewhat degraded and there are three large chips, two at the top and one running along the side of the main body. It is clear from the state of the state of the foot that it has been snapped off a larger object.
E.62.16 Intact and complete. Some of the black pigment has gone and several edges have slight scratches. The most significant damage is a scratch on the side with twelve dots that goes from one side in a straight line to the other.
E.62.22 The gaps between some teeth have become adhered by deposits. Others have warped out of shape. There is black discolouration, perhpas due to damp, on one face of the comb. A part has broken from the side but is due to be repaired.
E.62.24 Intact and complete, missing a large chip from the lip. There is several shallow scratches.
E.62.28 Intact and complete. There is one long chip missing from the lip.
E.62.38 Very large chip out of the lip, crack going from edge of that crack, to and along base and then back up the other side of the vase. Another crack joins this crack together along the shoulder. The crack can be seen on the inside of the pot.
E.62.39 Intact, but a large chip is missing from the lip, approximately one quarter missing. There is a crack going from one side to the other, starting and terminating at the shoulder, it goes around the base. Very little deposit.
E.62.43 Intact, but with a large chip missing from the lip. Several shallow scratches in the body, several small chips in the rim of the base.
E.62.44 Almost complete but a foot is missing from the base. The neck and flat rim have been reattched. Some discolouration on the lid and around the opening.
E.62.45 Intact, including top lid and pot. The lid has a about 1/4 of the rim missing, a large chip and several smaller chips around the lip. There is dark deposit around the shoulder and there is a large chip missing from the rim of the base.
E.62.50 Intact and complete. There is a large chip missing from the lip from which a small crack eminates. Several other smaller cracks also begin at the lip. Base is pitted.
E.62.54 Not whole, stuck back together from two pieces, resulting in a large crack. The lip is also stuck back together from three pieces. Little or no deposit.
E.62.55 Intact and complete, there is no damage aside from some imperfections on the base. There is also a few areas of black deposit on the inside of the vase.
E.62.61 Intact and complete, there are several small chips missing from the lip. There is some discolouration of the Alabaster.
E.63.13A Single fragment from the rim of a dish or bowl. The blue glaze is well preserved. There is a large malformation in the top right hand side of the fragment, and there are several shallow scratches in the surface.
E.63.13D Single fragment. The blue glaze is well preserved. There are several very shallow scratches on the surface and one large chip missing from the lower of the sculpted lines.
E.63.26 Repaired from two pieces, leaving several large cracks on the pot originating from the base. Large chip on the lip.
E.63.29 Intact. Several large chips on the lip, large amounts of light deposit, more prominant on base. Elongated verticle hole at widest point of body. Two smaller but shallower holes to the right of the larger. Blackened from use.
E.63.5 Intact and complete, with a large crack half way down the body, and several chips missing from the base, a small crack originates here, the blue glaze is intact.
E.63.9 Intact and complete, the glaze is still present although the light green colour is somewhat faded. Aside from one crack and two small chips on the facade no detail has been lost.
E.65.14 Intact but a fragment, the glaze is gone as has much of the colour, there is an obvious crack near the foot of the fragment and it is clear from both ends of the fragment it has been snapped off.
E.65.2 Intact and complete. The pot is covered with small, shallow scratches and small amounts of white deposit. There is also a large scratch going from the mouth down one side, accross the base, and terminating near the base on the other side.
E.65.8 Condition is excellent except the leather is stiff and therefore delicate. Left: point is missing from toe, leather straps are broken and incomplete. Right: leather straps complete but broken on the left hand side.
E.79.2 Intact and complete, there is a large chip missing from the edge of the bowl opposite the channel described above. The surface of the artefact is very rough and there is a large amount of grey deposit on large portions of the plate.
L.2011.1.44 fragmentary, worn, slightly scratched, discolouration from scorching and covered in a light grey sediment
L.2011.1.58 Pipe fragment with a large section missing from the bottom half and some small cracks, with ridges around the inside of the pipe.
L.2016.3.26 Well preserved, not purged from deposit.
REDMG:1926.99.50 Complete except for a chip missing from the mouth; comprised of three rejoined fragments (two of which are small rim pieces); surface slightly gouged
REDMG:1926.99.59 Intact, apart from small scratches on rim and base.
REDMG:1934.26.1 Comprised of ten or more rejoined fragments, missing only slight chips from the joins; stained, with iridescence on interior and exterior surfaces and adhesions, especially on the base.
REDMG:1935.87.1 Missing large chip from right side of mouth; grayish-whie deposits, especially on mouth, top of handle, and lower part of body; decoration faded.
REDMG:1935.87.11 Large chip missing from rim on one edge. Some gloss worn inside the cup where portions have flaked.
REDMG:1935.87.29 Intact. Paint worn from rim and edge of one handle. Some damage to inside near to stamped palmettes. Glaze remains silvery.
REDMG:1935.87.30 Large wedge-shaped piece missing from rim down to body. Decoration has eroded slightly. Deposits inside.
REDMG:1947.13.1 The mouth has been repaired from five or more fragments, each handle from three fragments (with some parts missing and restored on the left handle). The body is reconstructed from 15 or more fragments and the foot has been restored in wood. There is a hole (perhaps original). In the base. Slightly chipped on the mouth, pitted, and scratched; traces of white plaster on the external surface, while the interior and bottom are covered with plaster. Faded decoration in patches.
REDMG:1951.113.3 Comprised of 10 or more rejoined pieces, missing slight chips from joins; slight yellowish-white deposit on interior of one hande; lower body slightly eroded on right side; underside slightly scratched.
REDMG:1951.130.1 Intact, but with two cracks across the center. Missing surface chips from the body, and underside. Decoration eroded, especially on lip.
REDMG:1951.132.1 Missing a small chip from the base. Light grey (lime) deposits on mouth, handle, stem, and foot, with build-up of tan deposits on the underside; resting surface stained grey in places.
REDMG:1951.158.1 Large chip missing from the right side of the mouth. Slight iridescence on the right side of the mouth; grey deposits on interior and on the right side of the exterior.
REDMG:1953.25.1 Comprised of three rejoined fragments, missing only three small chips from the rim; one superficial crack emerges from one of these chips; glazed surfaces slightly pitted, especially on interior; whitish-grey deposits on underside.
REDMG:1953.25.102 Intact. Small scratch on top of lion's head, and cracks running from top of back, down through back right foot into base. Crack in front right foot. Front shows traces of white slip. Back shows areas of grey deposit on remaining white slip.
REDMG:1953.25.32 Missing two chips from the base, and cracked on the underside; glaze dulled in places and cracking around the handle attachments; light grey deposits on side B; added colour very well preserved.
REDMG:1953.25.38 Lekanis: Seven rejoined fragments (including RM.1687.64), missing part of one handle and a chip of the flange from the opposite handle. Lid: missing a large chip on the knob. White deposits on lekanis rim and handles, as well as underside of lid.
REDMG:1953.25.40 Comprised of five rejoined pieces, missing only a small chip from the rim; grayish-white deposits on rim, under handle, and resting surface.
REDMG:1953.25.46 Part of the rim, above one handle, has been rejoined. Glaze retains lustre except where it is pitted and has eroded, on the interior and around handles; glaze eroded from decoration on underside. White deposits around one handle and on the exterior
REDMG:1953.25.73 Large rim fragment missing from one side; large side fragment, including part of base missing from the other side; some grayish-white deposits.
REDMG:1953.25.77 Both nozzles mainly missing, handle missing. Left hand nozzle volute has been restored, small hole from missing fragment, from this hole are radiating hairline fractures to the base. glaze is worn in places, large amount of deposit covering the entirety of the interior and the back portion of the exterior as well as other areas.
REDMG:1953.25.83 Intact if fragmentary. The facial features, especially the nose and right ear, have worn down quite considerably although it is still clear what they are meant to be. The line of breakage is straight, falling from the right ear to the middle of the left side of the neck.
REDMG:1953.25.95 Section missing from side at face level. Deposits on front and more on reverse side. Facial features worn.
REDMG:1953.25.98 Fragment broken off from a larger item. There is a large amount of white pigment remaining on the suface; this suggests that it was originally white in colour. The nose is quite short, perhaps because it has been worn down.
REDMG:1953.41.1 Intact. Accretions from river sediment (light greyish brown, with some reddish brown in areas) cover most of the vase, especially the handles and foot, where the deposits have built up. The interior surface is pitted on reserved areas, and glazed surfaces are scratched and eroded, especially on the interior of the bowl and the lip.
REDMG:1958.111.1 Comprised of 9 rejoined fragments (8 of which comprise the upper part of the handle), missing a chip from the outside of the rim; slightly worn on the lip and darkened (stained) on red surfaces.
REDMG:1958.13.1 Some chipping around handle, pitting on the body, black and white deposit on the interior surface. One point missing from the rim.
REDMG:1964.1610.1 Intact, many small chips in the surface, grey deposit over large amounts of the exterior and interior. Large amount of blackening around the nozzle, probably from use. Remains of a modern candle in the reservoir.
REDMG:1964.1613.1 Missing most of the nozzle, small amount of wick hole visiably blackened, probably from use. Large amount of white - grey deposit on the interior, small amount on the exterior, concentrated mostly around the discus.
REDMG:1964.1615.1 complete and intact, handle is restored from three pieces. small amount of scratching and pitting on the body. filling hole is chiped, Wick hole is blackened from use and air hole is filled in.
REDMG:1964.1616.1 Intact, small anomily at the tip of the nozzle. Relief is worn and indistinguishable. Wick hole and nozzle ar both blackened from use.
REDMG:1964.1617.1 Handle is missing, rejoined from two main pieces. Glaze mostly intact, small amount of deposit on the interior.
REDMG:1964.1619.1 Intact, large chip on the left side of the nozzle, score from the rim to the filling hole, large number of small chips. Grey deposit in areas, small amount of blackening around the nozzle, probably from use.
REDMG:1964.1630 Almost complete but missing one large and one small fragment from the rim. The surface almost entirely worn away.
REDMG:1964.1638 In good condition overall, though inner rim has clearly been scratched a lot, and bottom parts of handles have clearly been broken off, with a large chunk from the outer side missing from one.
REDMG:1964.1648 Surface worn and wash/glaze eroded, especially from lip and shoulder.
REDMG:1964.1671 Large fragment missing from upper wall, comprising 1/4 of the rim; yellow stains, grey deposits.
REDMG:1964.1697.1 Mouth, handle and neck all missing. Large flakes missing from body. Foot badly chipped and dented.
REDMG:1998.153.4 Missing a large chip from the front of the mouth; decoration worn and surface pitted. Yellowish-brown stains and white deposits on lower part of body and underside.
TEMP.2002.7.1 Intact. The rim suffers from several chips, one in particular quite large, opposite one of the handles. There is also evidence of wear on the glaze, as there is on the inside of the bowl. On the band inside the bowl can be found three deeper scratches, as well as the occasional small hole. The handles of the bowl also reveal small chips on their glaze, as well as small scratches. The band which leads down to and envelops the top of the foot, contains small scratches, and where it meets the foot are lots of small cracks in the glaze. There is also some yellowy/grey deposit, which we can also see on the base of the foot. The base is chipped slightly in places and there are small scratches in the glazed bands.
TEMP.2002.9.16 Nose is missing (as it probably is from the original). Hair is uneven as parts of the cast are missing from one side. Cast is placed on a black stand, also made of plaster.
TEMP.2002.9.28 Large flake missing from topside over zigzags. Thin deposits on edges. Black fading to red.
TEMP.2002.9.29 The paint on the underside is in very bad condition; streaky, dull and flaking away at the edges. The paint on the topside is dull but not flaking. Paint has worn badly from rim. Deposits are on the edges.
TEMP.2002.9.3 Glaze is extremely shiny. Underside has many deposits and remains of glue residue from a previous repair.
TEMP.2003.6.10 Three fragments of the same vessel's base. It appears that the body has mostly been scraped off around the joining point at the upper parts of the fragments, apart from a bit on b and two bits on c. a) There are adhesives on the interior and few spots have been chipped off. There are three tiny spots on the interior and a spot on the central part of the base, where there are also three cracks. b) Two tiny bits have been chipped off from the interior and a spot looks flaked off from the inner side surface of the foot. There are also traces of adhesives. c) Four very small parts have been chipped off from the interior. There are also traces of adhesives, especially on the interior, as well as two cracks on the central part of the base.
TEMP.2003.6.12 Four fragments that belong to the same vessel. a) Part of the rim, body and the handle (intact). There is white plaster on the inner surface of the handle and many bits and spots have been pitted off and colour appears peeled off, especially from the back of the handle. b)Should be rejoined to c. Part of the rim and body. Four small bits have been pitted off from the rim (exterior) and there is a bit of plaster. c) Should be rejoined to b. Part of the rim and tiny part of the body. Part of the decoration of the rim has been peeld off. d) Part of the body.
TEMP.2003.6.14 Two joining fragments of the lower part of the body of an amphora. White plaster on both sides (thicker on the interior). There are areas where the colour has been peeled off, as well as some pitting off from the left edge of the fragment. There are also adhesives.
TEMP.2003.6.17 Fifteen fragments that belong to the same kylix. There are parts of the rim and body (a,b,g,k,l,m,n) of the body (c,h,i,j,o) and of rim, body and part of the handles (d,e,f). a) Should be rejoined to b. Interior: Layer of white plaster and small bits that have been pitted off. Exterior: Traces of white plaster and a spot that has been chipped off. b) Should be rejoined to a and c. Interior: White plaster and a large spot that has been chipped off. Exterior: Traces of white plaster and small spots that have been chipped off from the left and bottom edge of the fragment. c) Should be rejoined to b. Interior: White plaster and two areas that have been chipped off from the top edge of the fragment. Exterior: White plaster and two small spots that have been chipped off. d) Should be rejoined to e. There are two spots that have been chipped off from the rim and bottom part, as well as some pitting off (rim). Exterior: White plaster and a large spot that has been chipped off from the upper part of the body. The handle is also missing, apart from its lowest part. e) Should be rejoined to d. Interior: There are two spots (rim, bottom) that have been chipped off. Exterior: Traces of white plaster and a spot on the left that has been chipped off. Most of the handle is also missing. f) Should be rejoined to g and h. Interior: There is a layer of white plaster, few tiny bits that have been pitted off and a spot on the left that has been chipped off. Exterior: There is white plaster, a spot that has been chipped off from the top right side and some peeling off of the colour on the handle, whose largest part is also missing. g) Should be rejoined to f and h. Tiny bits that have been pitted off from the exterior. h) Should be rejoined to f and g. Traces of white plaster on the exterior. i) Interior: Layer of white plaster. Exterior: Traces of white plaster. j) White plaster on the interior. k) Interior: Layer of white plaster. Exterior: tiny bits that have been pitted off and slight traces of plaster. l) Could be rejoined to n. Interior: White plaster and a spot that has been pitted off. Exterior: White plaster and some bits that have been pitted off. m) Interior: Layer of plaster and a large spot that has been chipped off from the bottom left edge. Exterior: Traces of white plaster and a spot that has been chipped off from the bottom right edge. n) Could be rejoined to l. Interior: White plaster. Exterior: Traces of white plaster, some pitting off and a large spot that has been chipped off from the decorated area. o) Traces of white plaster on both sides.
TEMP.2003.6.23 Nine fragments of the same vessel's shoulder (a and b) and body. a) Interior: The upper part seems to have been left reserved, but glazed?, but the lower part is streaky black. There are some bits that have been pitted off. Exterior: Traces of white plaster. There are two small spots that have been chipped off from the bottom of the fragment and some bits that have been pitted off from the joining point of the neck to the shoulder. b) Should be rejoined to c. Interior: Streaky black and two small spots have been chipped off. There are many bits that have been pitted off at the bottom of the fragment. Exterior: Traces of white plaster. There are tiny bits that have been pitted off. c) Should be rejoined to b. Interior: Streaky black, and a spot that has been chipped off. Exterior: Two small spots have been chipped off from the left bottom of the fragment. d) Interior: Has been scraped off. e) Interior: There are spots that have been chipped off. Exterior: There are two large spots that have been chipped off. f) Interior: Streaky black and several bits have been pitted off. g) Interior: Half of the surface has been scraped off and on the rest there are several bits that have been pitted off. Exterior: One small spot has been pitted off. h) Interior: There are large areas that have been scraped and few bits that have been chipped off. i) Interior: Part of the surface has been scraped off and there are bits that have been pitted off on the rest of the surface. Exterior: Two deep, short scratches?
TEMP.2003.6.3 Two fragments probably from the same vessel. (a) Many spots have been pitted off and there are remains of adhesives after some form of restoration. (b) A thick layer of white plaster (after some form of restoration) has been peeled off from some areas and it is cracked, deposits, remains of adhesives and accumulation of residue, especially on the interior.
TEMP.2003.6.6 a) Should be rejoined to b. It consists of part of the rim, one handle (the other one is missing) and body of the vessel. Small bits have been pitted off, as well as parts of the colour on some areas. The glaze also seems to be scraped off, apart from the surfaces decorated with palmettes. There are traces of white plaster (on the exterior), especially at the upper part of the handle's springs. b) Should be rejoined to a and c. Part of the rim and body of the vessel. The area above the decoration on the body seems scraped off. c) Should be rejoined to b. It consists of part of the rim, one of the springs of the other handle (that is missing) and part of the vessel's body. White plaster is apparent on most of the external surface. Traces of adhesives? exist on the internal surface of the rim d) Part of the rim and body of the vessel. Adhesives on the rim (interior and exterior). e) Part of the vessel's lower body. Tiny bits have been pitted off from both sides and colour has fadded away on some areas. f) Part of the vessel's resting surface. The foot is missing and there are adhesives and white plaster on the joining point of the foot with the base.
TEMP.2003.6.8 Seven fragments that belong to the same vessel. There is white plaster on both sides of each fragment. b) Adhesives on the exterior. The black gloss has been peeled off at some areas. e) Adhesives, especially on the external left side of the fragment. f) Small bits have been pitted off, and a shallow scratch on the lowest part of the body and a cracking on the central part of the resting surface. g) Looks like it has been flaked off from the vessel.
TEMP.2007.2.30 Fragment, possibly from base or rim
TEMP.2007.2.41 Fragment of a rim, white plaster on exterior and interior, probably from an earlier restoration
TEMP.2012.11.29 broken into 10 pieces and glued. Small part missing from lip