| 11.10.13
|
Fragment. The leaves on the inside and outside of the rim are slighlty worn, with a small chip and crack evident on the outside. The front surface is smooth, the back feels rougher, and has areas of white/yellow deposit.
|
|
| 11.10.3
|
Complete and intact. There are tiny air bubbles over the surface, as well as small areas of brownish deposit. Detailed markings on face and hands are slightly worn away. The left eyebrow, left eye, nose and mouth however, are all still clearly visible. Material on the resting surface has flaked away in areas. Originally painted red all over.
|
|
| 13.10.17
|
Intact, half of neck and rim missing, on one side by the cross there is a section which has been chipped away. There are various chips on the body, and the paint has faded significantly on the handle and around the shoulder.
|
|
| 13.10.19
|
Mostly intact with restoration to rim with a section each side of restoration still missing. There are some chips and pits on the inside and outside of the vase.
|
|
| 13.10.21
|
Complete and intact. There are wheel marks on the body of the vase and some deposits on the base, above the handle, and on the lip.
|
|
| 13.10.9
|
Large hole in one side, and hole at base of neck neck, part of handle missing. The vase has been repaired in several places including the body and the region where the neck of the vase connects to the shoulder. There are some yellow inclusions.
|
|
| 14.9.1
|
Intact and complete. There are stresses in the pottery throughout body and base, numerous pits and deposits. One crack starts at the mouth and terminates just before the base, and is visible on the interior and exterior. There is a fingerprint near the base.
|
|
| 14.9.110B
|
Both handle and most of spout are missing. Messy glaze around foot ring. Glaze remains shiny.
|
|
| 14.9.22
|
Creamy coloured deposits on edges. Dark spots of deposit on top surface. Red lines are irregular.
|
|
| 14.9.25
|
The stripes are irregularly spaced. White deposit on underside and exposed edges. Darker deposits on topside.
|
|
| 14.9.3
|
Good, but missing two-thirds of the rim. There are wheelmarks and fingerprints on the surface of the body.
|
|
| 14.9.31
|
The red and white colour from the exterior surface are badly faded to only traces remain. Dot of black paint on edge and also touching exposed clay at fracture - possibly modern.
|
|
| 14.9.33
|
The white areas are almost all gone leaving only a shadow of where they were on the black background. The black is wearing from the exterior surface. Some small deposits on the interior surface.
|
|
| 14.9.37
|
Thickness of clay is irregular and thickest at bottom of fragment. The black paint is dull and streaky. On the outer surface the areas between the black are creamy-yellow at top but become pinker towards the bottom.
|
|
| 14.9.39
|
There are sharp points where the fragment has broken away. The black on rim is eroding and some red is showing through. Some small chips to the rim.
|
|
| 2002.9.4
|
Intact and complete; wood is slightly stained and sticky (from previous adhesive) at the right side of the crossbar; the ‘leather’ drum is brittle, as are the strings, which are loose; the velvet fillet is in dissaray, with some torn stitches.
|
|
| 2003.6.18
|
Single fragment, slightly worn, although black pattern and lines on the fragment are still clearly visible.
|
|
| 2004.10.1
|
There are cracks on the body of the flask and on the foot where repair marks are visible. The black slip is worn. Fingerprint marks are still visible in the wash.
|
|
| 2004.8.3
|
Single fragment of four sides (kite shaped). The reserved background has an incision (L. 1.6) which cuts into the sixth palmette. Five palmettes are partially faded in colour. On the reverse of the fragment, the black paint has been eroded along the edges of breakage.
|
|
| 2005.3.23
|
fragment, incisions are well preserved, black is worn
|
|
| 2005.3.28A-B
|
Condition isn't good on both fragments, interior is faded and and has some deposits of white visible, exterior is discoloured, faded, stratched and chipped. small holes are visible on A, possibly due to air bubbles during firing.
|
|
| 2005.3.30
|
Reasonable, exterior decoration is worn and there are some white deposits
|
|
| 2005.3.36
|
reasonable, exterior has dark brown discolouration under handle, and there are numersou stratches over the zigzag
|
|
| 2005.3.41
|
Two of the handles and the stem and foot are missing, red is visible although worn and there are dark brown and white deposits on the piece
|
|
| 2005.7.8
|
Fragment. Poor-fair, although threads are not brittle
|
|
| 2007.10.2.8
|
Only centre of gem remains, edges of the scene are missing
|
|
| 2007.7.1A-S
|
All pieces are chipped with designs partly faded. A-F, H, L-N, P-Q, S: Evidence of later restoration; O-P, R: Fire damaged
|
|
| 2008.7.123
|
Fragment, chipped at edges. Wash on exterior is heavily scratched. Interior is chipped and scratched. On interior are illegible handwritten pencil marks and 'III' handwritten in ink.
|
|
| 2008.7.131
|
Fragment, chipped at edge. There are some small chips to the wash. There are some small intersecting lines hand-drawn in pencil on interior.
|
|
| 2008.7.145
|
Fragment, chipped. Cream wash and greyish-black overpaint are heavily chipped.
|
|
| 2008.7.147
|
Fragment. Wash on interior and exterior is heavily chipped. Both ridges are chipped away at one end.
|
|
| 2008.7.158
|
Fragment, edges are chipped. Deoration on interior and exterior is heavily worn. On exterior there is spotting of a darker colour. Below the handle is handwritten in pencil 'Hernion'. On interior is written '13 Argive Hernion'.
|
|
| 2008.7.16
|
Fragment broken on five edges very scratched and worn glaze, edges are worn smooth
|
|
| 2008.7.178
|
Fragment; worn heavily and so covered in dirt that establishing the Munsell color and decoration are practically impossible.
|
|
| 2008.7.185
|
Fragment; badly worn, deocration faded and discolored, but patterns are fairly clear; large chip on the exterior; interior worn and chipped too.
|
|
| 2008.7.80
|
Interior: some of the black overpaint on the fragment edges is chipped; exterior: there are some chips to the surface of the fragment and some of the detail is worn away
|
|
| 2008.9.111
|
Fairly good; plastic shelves are no longer on their supports.
|
|
| 2008.9.112
|
Fairly good; pieces are not secured to the rest of the model in some cases.
|
|
| 2008.9.113
|
Rather poor; several of the wooden shelf supports are missing or broken, all but one of the plastic shelves is broken.
|
|
| 2008.9.114
|
Moderately good condition; plastic shelves are missing and one of the model amphorae has lost its support.
|
|
| 2008.9.115
|
Fairly good; some of the model objects have lost their supports and are no longer attached to the model.
|
|
| 2008.9.117
|
Decent; most of the model objects are in good condition, but the stand for the model itself is half missing.
|
|
| 2008.9.12
|
Fragment, wash on interior and decoration on exterior are faded.
|
|
| 2018.6.1
|
The holes along the edge may have been made to bind the tablet to a lid or another tablet with cord. The grooves may be where excess wax was scraped off the stylus. There are several perforations down one edge, which would have allowed several such tablets to be strung together to form a book. One of the raised edges has been broken off. Some surface wear and staining.
|
|
| 22.3.22
|
Single fragment. There are two spots that have been chipped off from the bottom of the exterior and ca. 5.0 cm from the top of the interior. There are also small bits that have been peeled off from the interior, which is almost covered with white plaster. Traces of plaster are also apparent on the external surface.
|
|
| 22.3.26
|
Part of rim (about 1/4) is missing. Several very small chips and scratched areas can be found on the top surface of the plate, as well as one larger part that is gouged out. Also very small chips are visible on the underside of the plate and a patch near the missing rim is unevenly fired (red instead of black).
|
|
| 22.3.27
|
If there were handles then they are both missing along with the whole of one side and parts of other side of body missing. Small section of rim remains.
|
|
| 22.3.33
|
Only one spot has been peeled off from the exterior, while at the interior there are four bits that are chipped off and slight scratches on the reserved band.
|
|
| 22.3.36
|
Fragmentary with numerous chips across the edges of the exterior and interior of the artefact, the face of the object and its handle. Countless, small chunks of paint are missing from both the outer and inner faces of the artefact.
|
|
| 22.3.4
|
Incomplete as one handle and part of rim are missing. Heavy deposits inside and white, thinner ones on mouth and handle. Base damaged so object does not sit properly.
|
|
| 22.3.5A-B
|
Intact. Three small chips on the body of the lid. Also there are patches of wear particulary on the lid and also there are scratch marks on the lid marking the decorative patterns and inside the pot. Paint has worn off of handle and areas of lid.
|
|
| 22.3.7
|
One handle and part of rim missing, as is a large chip from the rim. Large piece missing from the inside. Two large marks are also on the outside of the kylix where the handle used to be.
|
|
| 22.9.5
|
Currently in 9 fragments. Main body of cup has had one fragment glued back into place. Does not appear that all pieces of cup are present. Needs to be reconstructed. Base has large chip. Bad condition however, black glaze seems to be in a good condition.
|
|
| 23.11.31A2
|
The head is missing. The left arm has broken off below the wrist, and the feet are missing. There are two small holes in the lower skirt.
|
|
| 23.11.31B
|
Slightly chipped; spear has broken off completely; head and some of helmet are missing.
|
|
| 23.11.31BB
|
The head of the figure has broken off, as has the top of the spear. There is a section missing from the right of the shield, and the central boss has almost become detached. Te right foot is also missing. There are further fracture-lines extending at nine o'clock from the top of the figure and across the shield from the centre.
|
|
| 23.11.31K2
|
The points of two of the triangular elements are missing. There is a break in the circle of the wreath, where one end has pushed up over the other.
|
|
| 23.11.31KK
|
The legs have broken off at mid-thigh level, and there is some chipping to the extremities of the pipe and draperies. There are broken edges at top and bottom of the right fist.
|
|
| 23.11.31Q
|
There are breaks at the top left and bottom right of the shield rim (indicating a missing spear). The left leg has broen off at the top of the thigh, and the right at knee level.
|
|
| 23.11.31XXX
|
The head is missing. Both arms are broken off at the shoulder. The left foot is missing below the ankle, and the right foot is entirely absent.
|
|
| 23.11.31XXXX
|
The top of the figure has broken away. The right arm is absent from just below the shoulder, and the feet are missing.
|
|
| 23.11.31Z
|
The head, top of the spear, and left leg are missing, but otherwise in good condition.
|
|
| 25.4.2
|
Incomplete. The surface condition is not very good, there are small holes and scratchs all over the surface, in and out, as well as fading on the decoration. The rim shows several chips, and the handles are very uneven. The resting surface of the foot is very chipped and uneven.
|
|
| 25.6.2
|
Intact except for the edge of the rim which is missing on one side. The inside show small areas of general wear, as well as a small patch of what looks like yellow varnish near the broken rim. There is also some white deposit in the reserved disk in the centre, and on one of the handles. The black glaze on the handles has been rubbed away in patches, as has the decoration on the main zone. There is more white deposit on the main zone, some of which runs in circles, showing the gradient of the material. There are cracks on the glaze around the top of the foot, below which are some denser patches of white deposit. This deposit is also evident on the base of the foot and inside it.
|
|
| 25.9.3
|
At the reverse side the glaze has declined. A big part of the rim has been chipped off and some bits have been pitted off. There are also many deposits especially at the interior.
|
|
| 26.12.19
|
Mouth and upper part of neck missing. Foot badly damaged making pot stand unevenly. Chips to shoulder. Colours on main design are worn and the black stem ahs faded to red.
|
|
| 26.12.20
|
Missing handle, but we can see the remains of where it should have been. There are small chips on the rim of the neck, and the black has begun to rub away. At the base of the neck is a small amount of white deposit, which we can also see on the main zone. The main zone has been worn away in the middle and near one edge. There are small scratches and flaking decoration at the top of the foot.
|
|
| 26.12.24A-B
|
The flat surface of the knob on the lid has a white deposit on it, which can also be found at the base of the stem, and around one side of the rim. Small cracks in the glaze are evident around the the base of the stem, and small scratches are clear around the surface of the rim. The very edge of the rim has some small chips in it. On the inside of the lid, there is one deep scratch, and a hole, as well as more of the same white deposit. The rim and inside of the main body has got more deposit on it, but this is a brighter white. The gloss also shows signs of wear with scratches and flakes in the surface. Near one handle, there is a chip on the rim. One handle is covered in a yellowish/white deposit. More pale white deposit can be found on the foot and on the black band above it. There are several small scratches and chips in the base of the foot.
|
|
| 26.12.26
|
The vessel has been repaired from ca. 10 fragments, however, part of the lip and three pieces from the shoulder are missing. There is also accumulation of deposits, especially in the interior, as well as some spots that have been pitted off.
|
|
| 26.12.28
|
Complete. The rim of the neck is chipped and underneath one side of the rim, there is a hole in the neck. There are small holes and scratches over the surface, some deeper scratches around the base. Inside the mouth and on the resting surface of the base is some white deposit.
|
|
| 26.12.30
|
Intact. Flakes of glaze are missing all over the surface, both inside and out, especially around the edge of the handles and the rim. A white deposit is clear not only on the inside of the Kantharos, but also in large quantities on the outside, including the base of the foot.
|
|
| 26.12.8
|
Incomplete. Most of neck and all of mouth are missing. The decoration all over is very faded, especially on the body, leaving the surface very smooth. There is a large hole in one side just at the bottom of the main zone. The top and edge of the foot is chipped, on the inside of the resting surface is a small hole. There is a small amount of orange deposit on the resting surface of the foot.
|
|
| 26.2.2
|
Fragment with small chip on one edge, otherwise edges are smooth.
|
|
| 26.2.26
|
Underside has slight patches of discolouration and bands are starting to fade. The topside has lost the white decoration so that only traces remain. No surface damage or deposit.
|
|
| 26.2.28
|
Painted bands on underside are wearing away considerably compared to the topside which has retained most of its colour apart from some white but it is now a little dull. Surfaces are all still smooth with no significant damage.
|
|
| 26.4.3A-B
|
One handle is missing entirely and the other one is only part there. There are orange and white deposits on the underside of the body and the black on the inside has worn to a dark brown color. The rim of the lid has a large fragment missing.
|
|
| 26.4.4
|
Restored from many separate pieces. Glaze on the rim is slightly worn, as are the handles. The outer surface is worn. There is a greyish-white deposit in patches all over the surface, especially around the spurs and the reserved area of the main zone, as well as the top of the foot. On the top ridge of the foot, there is a hole. Colour on the inside of the pot has mostly worn away, leaving only more of the same grey deposit. Lid missing.
|
|
| 26.7.10
|
Incomplete. Apart from the head missing, there is little damage. There are small holes and scratches on the surface, front and back. The white slip has almost completely worn away, evident now only in small areas.
|
|
| 26.7.14
|
Fragment. The gloss on the rim of the fragment is a little worn and the surface on both sides shows small scratches. On the handle, there are a couple of flakes missing, and a small hole, possibly from an air bubble. The gloss on the inside is much more worn, with big flakes missing, with a couple of substantially longer scratches. There is also a yellow/grey deposit all over the inside of the fragment.
|
|
| 26.7.15
|
Intact. All over shows small areas of wear, on the main zone there are small chips around the base of the handles. Above the stem, on the top of the foot, and inside the handles, there is a small amount of white deposit, including one large patch (which looks like it could have been used to fix a hole).
|
|
| 26.7.2
|
The vessel consists of two pieces and is repaired. The stem and part of the body are joined together. There are five bits missing from the rim and upper body, as well as bits from the joining parts, where there is also a gouge. In few spots the colour has been peeled off (body of bull, handles).
|
|
| 26.7.7
|
Comprised of two rejoined pieces; join still visible across the back and belly, crack running from right ear to join. Body covered by white and grey depoit, feet are brown and shiny.
|
|
| 27.4.12
|
Complete; repaired from seven pieces. The rim is uneven, and contains two small but definite chips. All over the surface are small scratches and patches of wear. The pattern on the rim contains few subtle patches of red, the same colour as patches on the handles. Patterns in the centre of the bowl appear to have rubbed away in patches. Underneath, the patterns remain more prominant, but again small patches of wear are evident, especially around the rim. Inside the foot are greyish white deposits, that are also found underneath the rim in small patches near the handles.
|
|
| 27.4.2
|
Incomplete and repaired in seven pieces. The band on the rim, has mostly been rubbed away and on the inside there is a lot of greyish/white deposit. There are lots of small scratches all over the surface, including one long, deeper one at the base of the pot on the inside. On the outside, the glaze has also been rubbed away in patches, and on the leaves there are patches where it has come away in flakes. The foot is in pretty good condition, except for a white/cream deposit.
|
|
| 27.4.5
|
Intact. The rim, inside of the bowl and handles, all show evidence of wear, and there are considerable patches where all of the glaze has been removed. There are also small chips to be found on the handles, and on the inside of the rim. Where the glaze has been rubbed away, it has revealed a grey colour. There is also a thin crack running from the edge of the rim, to half way down the first black band. The well in the centre of the bowl is also slightly worn, to reveal a whitish grey colour, as well as a small crack running across the side. On the underside of the bowl, there is more evidence of general wear, including a chip just under the rim next to one of the handles. The bottom rim of the foot also reveals small chips, as well as a crack running across the middle.
|
|
| 28.9.1
|
Large fragment missing from figured panel, and many also from plain black parts. Much repainting and restoration. At least one handle and the foot are alien. Handles do not make direct join.
|
|
| 29.11.11
|
Incomplete. The sides of the mask have broken away, and the slip is covered in patches of grey/brown deposit. Detail of the face are still evident, but the nose shows areas of wear on the tip. The inside is a pinkish colour, with little evidence of deposit, though the surface feels rough to touch.
|
|
| 29.11.6
|
Reconstructed by many fragments, there are a few gouges and many small bits of colour have fallen off, especially from the interior.
|
|
| 29.5.5
|
Complete but not intact it has been pieced back together. On the inside, there are small scratches on the surface and patches where the glaze has faded to red or even its reserved colour. The glaze has also faded on the handles, and the edge of the rim is chipped. There is evidence of a greyish/white deposit on the inside of the rim. On the outside, the decoration is much more worn and faded, and the surface has small chips and flakes. The resting surface of the foot is chipped and in the centre of the foot has been scratched the letters T and I.
|
|
| 30.11.4
|
Complete but repaired. The paint has become very faded on the exterior more than the interior surface. The handles are intact, but the paint is lost. Material is very soft and fine.
|
|
| 33.4.1
|
Complete, but not intact. One handle and part of rim restored. Stuck back together from six/seven pieces. Decoration around rim and handles is worn in patches, with small chips in the surface. Small gaps where the pieces have been rejoined. A few scratches are evident in surface of main zone. Top of stem is rough to touch. Resting edge of foot has chips in it, inside the foot has some sandy deposit and a crack across the centre. Inside the body, the gloss looks silvery, with small scratches on it.
|
|
| 33.4.3
|
There are some bits that have been pitted off and some spots that have been chipped off, especially from the rim (exterior and interior), the neck and the handle. There are also some scratches on the white colour area, whereas the foot has been repaired and rejoined to the body.
|
|
| 34.10.15
|
Intact. The surface of the rattle is very rough, scratched, with peeling slip and dark grayish-white adhesions. There are three large cracks at the top of the ovoid part.
|
|
| 34.10.16
|
Comprised of two rejoined pieces. Decoration on the front has faded, and resting surface is very uneven, as is the back. There are small scratches all over the surface and small holes at the top of the head. The back reveals lots of small cracks and holes. There is a white deposit on the chest area, which can also be found inside the base, as well as running along the cracks on the back.
|
|
| 34.10.17
|
Complete. The white slip has worn away in places, and there is a smooth grey deposit evident in patches. Also, the munsell colour shows through. The features of the face are still fairly clear, but the eyes seem worn. The surface all over feels smooth, but the base of the neck is slightly uneven and a bit chipped.
|
|
| 34.10.18
|
Complete and intact. The surface is uneven all over, and the red glaze has been rubbed away in areas of prominance; for example, knees, stomach, chest and features of the face. There are indentations and air bubbles around the chest area, and on the back of the figurine. Here, there are also lots of scratches on the surface.
|
|
| 34.10.26
|
Intact but not complete. Detail of the hair remains very clear, but the features on the face are less so. The eyes have been worn almost completely away, and the nose has a chip in one side. At the top of the forhead, just where the hair begins, is a hole. The top and back are uneven and show small holes on the surface. There is a small amount of dirty deposit at the base of the neck, and inside the hollow of the head.
|
|
| 34.2.1
|
Intact. There are four noticeable chips in the rim, as well as evidence of wear over the black surface. All over the Kylix are patches of wear and small scratches. The reserved disk in the centre has a lot of grey deposit on it, as does the inside of the rim. This deposit is also evident around the handles, and in small patches along the main zone. At the top of the stem, leading to the base, are lots of cracks and some flaking. There is a chip in the side of the foot, and the well in the base of the foot contains a lot of grey/white deposit.
|
|
| 34.8.12
|
The handle has been rejoined to the lid, whose colour has been peeled off from many spots (underneath). The body has been reconstructed by 6 fragments. There are some bits missing at the joining points of the fragments, as well as from the incurved surface of the rim. Few bits have been chipped off from the base. The colour is wearing off from many spots, especially at the body. The deposits under the lid and inside the body almost obscure the glaze.
|
|
| 34.8.14
|
Intact and complete. Much of the glaze remains but in areas where it has rubbed of the green pigment is also missing. The painted detail remains in good condition, the face detail however was not painted and has greatly worn away. It would also seem that the left arm has worn down since the pigment is missing and the arm seems stunted cvompared to its companion. There are several obvious cracks around the feet.
|
|
| 34.8.2
|
this small lekytos is not intact, it is composed of five big fragments and five very small fragments, some flakes of clay are preserved in a little plastic bag. Bigger fragments are composed of more fragments brought together with glue. The paint is not uniform, is discolored and it is missing in some points. On the inside, in the upper part of the belly, there is a clay excrescence.
|
|
| 34.8.8
|
Black has largely faded to red. Mouth and stem are faded badly. Scratches to back of pot. Base has been repaired.
|
|
| 35.4.3
|
Intact. The rim of the pot shows two chips on the inside and three on the outside. As well as this, there is a grey deposit, which is evident in small areas all over the piece. The glaze on the inside is worn and there are small scratches all over. The outside also shows signs of wear, with small scratches all over the glaze. At the base of the foot, there is more deposit, but this is a white/cream clolour.
|
|
| 35.4.4
|
The handle has been repaired (rejoined with the body at its spring). There are many bits that have been pitted off from the vessel, especially at the lip and handle, as well as a scratch below the handle. Approximately one third of the vessel (lip, neck, handle and left side of almost half the body) is silvery glossy. The rest is glazed.
|
|
| 35.5.34A-Q
|
The decoration and pattern on all are in good condition and still very visible. The smaller parts are a bit more worn and the black gloss of fragment (e) is patchy in places.
|
|
| 37.7.3
|
Intact. Some glaze flaked off of handles. White deposits are wide spread over exterior surface.
|
|
| 38.4.3
|
Complete, appears intact. Paint extremely faded. Inside of mouth has over three small chips. There is one noticeable chip on the outside of the lip. The paint on the neck appears to have been worn away, because a pinkish clay is showing which does not appear to be a fading of the black decoration. There are at least two hairline cracks on the shoulder, with some of the clay worn away. The handles are in good condition with no noticeable chips, whereas the body has several chips and cracks. The base has a few small chips but is in very good condition.
|
|
| 39.8.1
|
Comprised of six fragments, rejoined, missing one and a half handles. The surface is worn, especially on reserved figures, which are otherwise stained. Some tan adhesions on rim and foot.
|
|
| 39.9.1
|
Mouth of jug appears to be missing its lip. Handle appears to have originally been black glazed, however now it is very worn. All decoration and figures on jug are quite worn. There is a large chip on the rim of the base, of the jug.
|
|
| 45.10.10
|
Sixteen fragments that belong to the same kylix. There are parts of the rim and body (a,b,g,k,l,m,n) of the body (c,h,i,j,o) of rim, body and part of the handles (d,e,f), and the base (p). a) Should be rejoined to b. Interior: Layer of white plaster and small bits that have been pitted off. Exterior: Traces of white plaster and a spot that has been chipped off. b) Should be rejoined to a and c. Interior: White plaster and a large spot that has been chipped off. Exterior: Traces of white plaster and small spots that have been chipped off from the left and bottom edge of the fragment. c) Should be rejoined to b. Interior: White plaster and two areas that have been chipped off from the top edge of the fragment. Exterior: White plaster and two small spots that have been chipped off. d) Should be rejoined to e. There are two spots that have been chipped off from the rim and bottom part, as well as some pitting off (rim). Exterior: White plaster and a large spot that has been chipped off from the upper part of the body. The handle is also missing, apart from its lowest part. e) Should be rejoined to d. Interior: There are two spots (rim, bottom) that have been chipped off. Exterior: Traces of white plaster and a spot on the left that has been chipped off. Most of the handle is also missing. f) Should be rejoined to g and h. Interior: There is a layer of white plaster, few tiny bits that have been pitted off and a spot on the left that has been chipped off. Exterior: There is white plaster, a spot that has been chipped off from the top right side and some peeling off of the colour on the handle, whose largest part is also missing. g) Should be rejoined to f and h. Tiny bits that have been pitted off from the exterior. h) Should be rejoined to f and g. Traces of white plaster on the exterior. i) Interior: Layer of white plaster. Exterior: Traces of white plaster. j) White plaster on the interior. k) Interior: Layer of white plaster. Exterior: tiny bits that have been pitted off and slight traces of plaster. l) Could be rejoined to n. Interior: White plaster and a spot that has been pitted off. Exterior: White plaster and some bits that have been pitted off. m) Interior: Layer of plaster and a large spot that has been chipped off from the bottom left edge. Exterior: Traces of white plaster and a spot that has been chipped off from the bottom right edge. n) Could be rejoined to l. Interior: White plaster. Exterior: Traces of white plaster, some pitting off and a large spot that has been chipped off from the decorated area. o) Traces of white plaster on both sides. p) Slightly faded, with a few surface chips on interior and on foot.
|
|
| 45.10.13
|
Thirteen fragments that belong to the same amphora. i Traces of white plaster (exterior) and adhesives (interior). ii) It has been burnt. iii) There are traces of adhesives and added white colour has fadded away. iv) Should be rejoined to xiii Traces of adhesives (interior). v) Should be rejoined to iv and ix. Adhesives inside. vi) Traces of adhesives. vii) Should be rejoined to ix. White plaster (exterior) and adhesives (interior). viii) Plaster on the exterior. ix) Should be rejoined to v, vii and x. Plaster (exterior) and adhesives (interior). Part of the slip has been peeled off and shallow bits have been pitted off. x) Should be rejoined to ix. Plaster on the exterior. xi) Plaster on the exterior. xii) Adhesives on the interior. xiii) Should be rejoined to iv. Plaster on the exterior. xiv) Plaster on the exterior, some scratches and few tiny bits that have been pitted off. xv) Plaster on the exterior.
|
|
| 45.10.18
|
Both fragments are badly damaged with i)small section of decoration missing, white deposit possibly material used to glue fragment back together. Cross section shows that the vessel was not fired all the way through. ii) Same as other fragment
|
|
| 45.10.20
|
There are six fragments probably from the body of the same closed-shape vase (amphora). i) Small bits of the colour have been peeled off and few small spots have been pitted off. ii) The fragment has been burnt. Tiny bits are pitted off. iii) The colour has faded away and has been peeled off from spots. Chips are missing from the edges. iv) The colour has faded away on the contour of the motives. v) The fragment is burnt. Bits of colour have been pitted off. vi) Bits of the colour have been pitted off, especially at the top and right side of the fragment.
|
|
| 45.10.22
|
There are only 18 fragments preserved from this vessel. These consist of parts of the rim, neck, shoulder and body. a: It is repaired from two fragments, rejoined. Part of the rim (the smallest part of two), neck (including the spring of a triple handle) and shoulder (these consist the second part of this fragment). The fragment is chipped off in many areas (rim: ca. 5 spots/ interior of neck: ca. 10 spots/ neck: ca. 4 spots. There are also gouges on the joining points of the two parts. The upper part (bigger part) of the handle is missing. Apart from tiny bits that have been peeled off from the interior and few deposits, the glaze and colour are preserved in a good condition. b: It consists of three rejoined parts from the vessel's neck. Few bits are missing on the joining point and a spot has even been chipped off, there are deposits and cracking of the colour on the interior, as well as another spot that has been chipped off. Three shallow carvings are also apparent. c: It consists of three parts joined together (two big ones and a small one). Deposits on the interior, three scratches on the exterior, tiny bits that have pitted off and spot that has chipped off from the lower left end. d: Part of the body, colour has fadded away in some spots, and a part has been peeled off. Deposits. e: Part of the body. Deposits but in very good condition, apart from two areas that are chipped off and small bits that are pitted off. f: Part of the body. Apart from deposits in a very good condition. g: Part of the body. Deposits, otherwise in a very good condition. h: Part of the body. Few, tiny bits have been peeled off, also few deposits. i: It consists of two parts of the body. ca. 5 bits have been pitted off and three spots are chipped off; deposits. j: Small fragment in very good condition. k: Small fragment from the body; deposits. l: Small fragment from the body; deposits.
|
|
| 45.10.7A-B
|
Comprised of many rejoined piecesby (ca. 10 for the body and 25 for the lid), with some patches reconstructed. One of the legs and large areas of the base, body and lid are restored and repainted. The surface decoration on original pieces is largely intact, with faded white details, and some dark deposits. Decoration worn on the lower flange and the rim of the body, as well as the lower edge of the lid.
|
|
| 45.10.9
|
Ten fragments that probably belong to the same vessel. a) Tiny bit of the vessel's lower neck, part of the shoulder and the spring of the handle, which is missing. There are scratches on the exterior and two bits that have been chipped off. Deposits and plaster? on the interior. (The rest of the fragments are from the vessel's body) b) Should be rejoined to c. White plaster on the exterior and traces of it on the interior. A small bit has been chipped off. c) Should be rejoined to b. White plaster on the exterior and traces f it on the interior d) Few deposits on both sides and a small bit that has been pitted off from the exterior. e) Few deposits on the interior and traces of white plaster. A tiny bit has been chipped off from the exterior. f) White plaster and deposits on the interior. Two bits have been chipped off from the exterior. g) The decoration appears as if it has been scraped off and there is a spot that has been chipped off from the exterior. h) A small spot has been chipped off. Deposits and traces of plaster on the interior. Added white colour has fadded away. i) There are adhesives on both sides and white plaster on the exterior. The decoration looks as if it has been scraped off, a tiny bit has been pitted off and a small spot has been chipped off. j) Traces of white plaster, especially on the interior. There is a small spot that has been pitted off.
|
|
| 45.6.10
|
Intact but missing a small chip on the rim and a large chip from the foot. One further very small chip on the rim. Surfaces are slightly pitted with red showing through black surfaces.
|
|
| 45.6.38
|
Intact, but missing two chips from rim. There are some deposits on the lower part of the rim.
|
|
| 45.6.5
|
Intact but clay has flaked on one side of body where there are also white and grey deposits. Paint has worn badly on handle and sides.
|
|
| 45.6.67
|
Intact. Chipped at mouth of nozzle, small chips and areas of glaze missing are now showing white.
|
|
| 46.9.2
|
Base has been reattached, has holes, and is chiped along the resting surface. One fragment is missing and there are large cracks in the body. Chips along the rim with one major chip which is 8.0 cm long.
|
|
| 47.2.4
|
Part of the rim and upper body has been chipped off. The one of the handles has been rejoined to the body and so is the one of the two springs of the other handle. The rest of the second handle is missing. The gloss is greenish and streaky at some areas. There are deposits, especially on the area above the foot and on the base. Some remains of adhesives? at the one handle.
|
|
| 47.6.2A-B
|
About two thirds of the top rim of the lid are missing, while one third of its side surface has been reconstructed. The rest of the lid has been repaired through the joining of three fragments; the figural scene has faded. The body is almost intact, only a small bit has been chipped off from the rim, three tiny bits have been pitted off and a small part of it has been reconstructed. The rim of the base also has some pitted off parts.
|
|
| 47.6.5
|
Complete, but the rim, base and mouth are slightly chipped. The vertical handle, once broken off, has been rejoined. The surface is quote worn, and the left side is covered with a large white deposit around the handle; there are similar deposits on the foot and base.
|
|
| 49.1.2
|
Intact, with only slight chips on the base. The design remains very clear and the glaze is shiny and complete. Only the white paint has suffered a little. There are deposits inside the rim.
|
|
| 49.4.1
|
The mouth is a little chipped and the neck has been repaired. There are bits missing from the shoulder, too. The largest part of the white bands has worn away, as has some of the paint on the foot. There are white and gritty deposits in the mouth and under the handle. The glaze below the meander is streaky. There is also colour loss on the back of the body but this appears to be due to firing.
|
|
| 49.8.3
|
Intact and very well preserved. Paint remains clear and there are very few chips in the rim.
|
|
| 50.10.4
|
The rim has been reconstructed from 2 fragments repaired. The handle has also been rejoined with the vessel and the whole of the upper part (from rim to end of shoulder) has been reattached to the body. The glaze is shiny in places but has begun to crack in others. There are also deposits on the rim, neck, shoulder and foot / base. Several bits have pitted off from the body.
|
|
| 50.12.43
|
Single fragment. The lines at the bottom of the circle are more faded, the thicker paint at the centre is less faded but has been chipped.
|
|
| 50.12.6
|
Black bands are mostly rubbed off.
|
|
| 50.5.3
|
Mouth and upper part of neck modern and intact handle. Most of the black has faded to a light brown color. The neck and mouth has been rebuilt by modern material. The surface appears in fairly good condition, except for some deep scratches around the neck. Left swan scratched face, right swan intact face. There are other small scratches on the surface and bit of flaking and chipping, especially around the edge of the foot.
|
|
| 51.1.2
|
The vessel is reconstructed by many fragments and has been repaired (it has been conservated and parts of the shoulder and body have been filled in). Some bits of the colour have been peeled off (rim, handle, neck, body) and there are some small spots that are pitted off (rim, body). Lastly, there is a gouge under one of the side handles and another one on the central part of the base.
|
|
| 51.1.3
|
Chips on both the exterior and the interior of the rim. Chips on the body. Cracks are apparent on the body of the krater and two large fragments on the body have been filled in. The gloss is not lustrous and was flaked off the rim, on the top of one of the handles and part of the body and the foot.
|
|
| 51.4.4
|
Chips missing from the rim (ca. 7, including damage on the meander pattern) and the neck (ca. 5). There are also small bits missing at the joining point of the two parts of the fragment.
|
|
| 51.7.13
|
Intact, with the exception of some spots that have been pitted off and few small gouges (on the interior of the mouth and on the body). Added white details are dirty.
|
|
| 52.3.2
|
Body and base surfaces are terribly damaged with large chunks missing although these do not go all the way through. Paint worn from inside mouth. Glaze and paint remain relatively undamaged on areas that have not been chipped away.
|
|
| 52.3.3
|
Incomplete but cleaned and restored at the Ashmolean by Rickard. Body is compiled of fragments with missing parts filled in with plaster. Five separate unattached fragments. Large chip from foot. Neck, mouth and rim are largely restored but some loose fragments remain. Ruddled areas worn and black paint is scratched.
|
|
| 52.3.4
|
Comprised of 40 or more pieces, rejoined, with some restroations, but missing handle and lugs on one side. Much repainting on handle, rim, and interior, but animal details are largely original. Complete apart from one of the handles. It has been reconstructed from many pieces and parts are modern fillings.The contours of the black bands inside are fired red. Badly restored.
|
|
| 53.8.1
|
Complete but slightly chipped on the rim. There is a crack around the base of the omphalos. The relief decoration and gloss are worn.
|
|
| 54.8.1
|
Piece missing from lip and restored with plaster. Some flakes of the surface are missing resulting in exposing the clay and leaving an uneven surface. Hole in bottom of cup. Black faded or fired to light brown in places. Scratches on the underside.
|
|
| 56.8.8
|
The vase is reconstructed from many fragments. Bits have peeled and pitted off, and there are a few gouges. Gloss is lustreless, parts flaked off on the interior, handles, foot. At parts of the rim and the handles fired brownish.
|
|
| 58.2.3B
|
Intact, slightly chipped on knob of lid. Lustre has faded. What are pink smears inside lid?
|
|
| 58.2.4
|
Intact apart from a section of the spur which seems to have broken off. There is a deep crack on the inner side of the handle at the bottom. Also a dent in the body by the base of the handle, and the base is misshapen, both of which may have been done before firing (?). In a few areas the paint has been worn, and there are minor chips.
|
|
| 61.6.1.5
|
Complete and intact, but orifice and base are slightly scratched.
|
|
| 61.6.1.7
|
Intact; but part of the body of the container have broken away, and there are small chips on the rim
|
|
| 64.7.1
|
One handle and the attached part of the rim are missing. The black colour misfired to red in certain places (e.g. at the handle and at the external side of the rim, underside of the foot, tongues, below the tongues, where the thin line is now reddish-yellow). There are deposits on the exterior of the body and the underside of the foot. Small chips to the rim.
|
|
| 65.6.1
|
Many spots have been pitted off, especially on the mouth, handle and neck. There are also some bits (shallow) that have been chipped off, especially on the shoulder and upper body, however, the vessel is intact.
|
|
| 65.6.2
|
Broken off at the shoulders; small white deposit at fracture. Highly polished with no surface damage. The scratches caused through production are still visible.
|
|
| 67.7.1
|
Incomplete. The figure has broken in half and been glued back together, however, at the back, there is a chip missing still. The grey colour is interspersed with deposit of a dark brown colour, which is even more prominant on the back. The features of the face have almost all worn away, except for the nose. Around the front and sides of the base are white and dark grey deposits.
|
|
| 68.12.3
|
Complete and intact. Yellowish-red accretions on the knob and top of lid as well as the underside mar the surface. The outer part of the lid is worn. The handle of the lid shows areas of wear, especially on the leaves. The stem and underside of the rim are covered in pinky/beige deposit. A white deposit occupies most of the underside.
|
|
| 73.9.1
|
Fragments, three seperate pieces glued back together. The handle areas are missing and nearly half of side B. The inside shows areas of grey deposit, as well as scratches, chips and cracks.
|
|
| 73.9.4
|
Single, five sided fragment, with surface scratches and patches of wear, especially on the figure of the dog/goat. Through the black band and circle are patches of red showing through the black glaze. White deposits visible on the reverse of the fragment.
|
|
| 73.9.5
|
Fragment. Both the inside and outside edges of the rim are worn, and there is a small chip. The outside surface is chipped slightly, and has a few small areas of a grey deposit.
|
|
| 73.9.7
|
Incomplete, only a small amount of the cup remains, including one handle. Two pieces are glued back together. The glaze on the outside edge of the rim has completley worn away, and there are small scratches all over the surface. Both inside and out, there are traces of a whitish deposit, except on the foot where the deposit is more of a pinky colour.
|
|
| 73.9.8
|
Two fragments. (a)The glaze on the rim and the inside of the fragment shows a few small scratches. On the rim and the outside of the fragment there are a few small areas of milky/white deposit. The black blob reveals an area which may have been the base of a handle. The colour of the clay inside here, is a more pink colour. Like the first fragment, fragment (b) shows evidence of small scratches on the glaze, both inside and out, but seems in fairly good condition, with no evidence of deposit.
|
|
| 74.7.5
|
Complete. Has been glued back together from two pieces. Is entirely covered by dark deposit, possibly from the action of fire. Thought to be from a burnt grave. There is a lot of flaking, revealing white. The features of the face are distinguishable, but are worn in places. The back is much lighter in colour, but still covered in brown/green deposit and feels rough to the touch.
|
|
| 78.12.5
|
Intact, wash is worn and there are slight chips on the shoulder. Slight blackening at the tip of the nozzle, probably from use.
|
|
| 78.12.6
|
Intact and complete, Wash and some of the decoration is very worn. ther area around the nozzle has largly lost most of its wash, however there are traces of black indicating usage. Some white deposit on the base and a small amount on the discus.
|
|
| 79.1.5
|
intact, chipped at the tip of the nozzle. Joind of the handle and the nozzle are rough, small ammount of white deposit.
|
|
| 83.10.1
|
Quite badly worn. It has been glued back together using three fragments. There seems to be a fragment missing at the bottom of the statue, therefore the figurine is incomplete. Most of the features of the statue are badly worn. There are many soil deposits all over the figure. Inside the hollow figurine there appears to be some sort of plant.
|
|
| 83.9.14
|
The plate is not intact, multiple pieces are missing with two parts glued together. The paint is not homogeneous, there are numerous points where it is absent and the small hollow in the middle is punctured
|
|
| 83.9.15
|
The plate is not intact, multiple pieces are missing and existing parts are fractured. It consists of two fragments that have been glued together.
|
|
| 83.9.16.a
|
The plate is not intact, there are two separate fragments with the larger fragment made up of four rejoined pieces.
|
|
| 83.9.16.b
|
plate is not intact, multiple pieces are missing and existing parts are fractured. It consists of two fragments that were bound together. The paint is not homogeneous, there are numerous points where it is absent
|
|
| 83.9.5
|
Seven fragments have been glued together, but four fragments are missing inbetween. A chip to thick black ring outlining base of foot. Sides of foot are heavily soiled. Slight discoloration revealing a warm red undertone.
|
|
| 83.9.6
|
Single fragment. The reserved areas on the base of the foot are chipped. The black gloss from the interior is flaking around the edges.
|
|
| 84.8.1
|
a) There are some spots that have been pitted off, especially at the edge of the rim, as well as some shallow scratches. There is a bit that has been chipped off from the neck and few deposits. b) Many small spots have been pitted off from the edge of the rim, few bits have been chipped off from the neck and there are traces of deposits. c) Should be rejoined to d. Few parts have been chipped off and there are deposits. d) Should be rejoined to c and e. Tiny bits have been peeled off, there is a cracking on the internal surface and traces of deposits. e) Should be rejoined to d. There are some scratches on the exterior and some parts have been chipped off from both sides. f) Should be rejoined to c. Some spots have been chipped off and at some areas the colour has been peeled off. g) Tiny bits have been pitted off, two spots have been chipped off. h) Traces of plaster, especially on the interior. The colour has been peeled off from some areas and there are spots that have been chipped off. i) Traces of white plaster, streaky black on the interior andtwo small spots that have been chipped off. j) White plaster on both sides, streaky black on the interior and many spots that have been pitted off from the exterior. k) Should be rejoined to l. Traces of white plaster on the exterior. l) Should be rejoined to k, m and n. Few, small bits have been pitted off. m) Should be rejoined to l, n, p and o. There are some scratches on the external surface, as well as some bits that have been pitted off from both sides. Two spots have also been chipped off from the interior. n) Should be rejoined to l, m and o. Many shallow, small scratches and few, tiny bits that have been pitted off. Also, a spot that has been chipped off from the external surface and a smaller one from the internal. o) Should be rejoined to m,n and p. There are some scratches on the external surface, some tiny bits have been pitted off and a spot has been chipped off. p) Should be rejoined to m, o and q. Few tiny, shallow bits have been pitted off. q) Should be rejoined to p and r. Two small spots have been chipped off from the interior. r) Should be rejoined to q and possibly s? s) Could be rejoined to r? t) Should be rejoined to o. There are some tiny bits that have been pitted off from the exterior,as well as a shallow gouge and two scratches. u) Should be rejoined to v. White plaster on the interior. v) Should be rejoined to u and w. There are some scratches, some bits have been pitted off and few spots have been chipped off. w) Should be rejoined to v and possibly x? Some scratches on the exterior and a shallow gouge. x) Could be rejoined to w? There is a shallow gouge and three spots that have been chipped off from the exterior. y) Tiny bits have been pitted off. z) Small bit has been pitted off. aa) Should be rejoined to ab. Bits have been pitted off and surface seems to have been scraped off? on the top. ab) Should be rejoined to aa and ac. Bits have been pitted off and colour seems to be scraped off? on the top. ac) Should be rejoined to ab. Bits have been pitted off and colour seems to have been scraped off on the top. ac) Should be rejoined to ab. Bits have been pitted off and the top seems to have been scraped off? ad) Small spots have been pitted off.
|
|
| 84.8.2
|
Fragment. Upper word on the stamp has almost worn away. There are a few chips and scratches. Black and white deposits on the surface.
|
|
| 85.3.1
|
30+ fragments rejoined, but missing at least 7 more. Most of neck and mouth missing, as are both handles. Surface decoration worn, especially on side B.
|
|
| E.23.10
|
The actual pallete is covered with many small scratches, which, combined with the reside of pigments, have left it a light grey colour. There are chips missing from two corners of the base, one larger than the other, with two other chips in diagonal corners of the trapazoid.
|
|
| E.23.18
|
Intact if not complete. The areas where parts of the headdress has fallen off is quite worn. There are three deep holes in the headress that are symetrical about a crack that goes from the top of the headdress to the mouth. There is also a second crack on the right hand side from top to the base of the head, going through the eye.
|
|
| E.23.27
|
Intact, missing some small chips on the lip. There is a large amount of brown deposit all over the body and there are remnants of a Liverpool label.
|
|
| E.23.28
|
Intact and complete, with a large chip missing from the lip. There are two noticable stresses near the foot, one which forms a hole the other a shallow chip.
|
|
| E.23.30
|
The mouth is badly chipped with the entire lip missing. The handle has been glued back on. Half of the upper body, and the handle are covered in a dark grey deposit. There is a deep scratch on the main body.
|
|
| E.23.31
|
Intact and complete, the pottery is very blackened in areas, particulary in one area around the base. There are shallow chips throughout the surface.
|
|
| E.23.32
|
Intact, there are several chips on the lip and a small hole in the lower body of the jar.
|
|
| E.23.37
|
Complete but not intact. Small chips in the lid. The lip and mouth are detatched from the body. Large crack in the lip, deposit on the shoulder, small chips in the base.
|
|
| E.23.38
|
Intact, it is clear from the top and bottom part of the artefact that it has been removed from a larger object, since they appear to be thinner than the rest of the object and therefore look like 'connectors' of some kind. There appears to be very little degradation of the wood. There are some remnants of a white pigment on the lower half.
|
|
| E.23.39
|
Nine fragments of possibly three bracelets. Three fragments are shell, the other six are ivory or bone
|
|
| E.23.43.2
|
Intact and copmplete, there are several impurities in the glaze, most notably a long line of black substance that appears to be stuck to the bead as it very raised from the surface.
|
|
| E.23.43.4
|
Intact, altough the ends are rough and distorted suggesting they have been damaged. The glaze has completey worn away.
|
|
| E.23.47.1
|
Most of the beads have lost their original sheen and several of them have a brown deposit on them. Since there are very few details on any of the beads/amulets it is difficult to say if any have been lost. Several of the objects have lost some of their original colour but all remain intact and complete.
|
|
| E.23.53
|
Complete but the feet have been reattatched, the crack is evident. Most if the glaze is gone, as has most of the green colour. The hieroglyphs are incomplete as are most of the other black details.
|
|
| E.23.57
|
Intact and complete, most of the glaze and a large portion of the green pigment is gone. The are several large cracks on the body underneath the head. A large amount of detail is missing particularly the inscription and the shoulder decoration.
|
|
| E.47.6.9
|
Intact, although there are several chips on the lip.
|
|
| E.62.10
|
Intact if fragmentary, the wood is somewhat degraded and there are three large chips, two at the top and one running along the side of the main body. It is clear from the state of the state of the foot that it has been snapped off a larger object.
|
|
| E.62.11
|
Intact if fragmentary, the wood is in good condition although there are some deep grains in the wood.
|
|
| E.62.17
|
Intact and complete. The details are still clear and there is no obvious damage to the artefact.
|
|
| E.62.37
|
Intact and complete. There are several small chips around the rim. There appear to be several water marks on the inside of the bowl. The base and some parts of the body are covered in an encrusted light brown deposit.
|
|
| E.62.4
|
Intact not complete (the head is missing). The detail is becoming less desinite and the underside has become dirty with what appears to be watermarks. There are small amounts of black deposit sparcely placed around the artefact.
|
|
| E.62.47
|
The coulouring (perhaps a wash)has worn off in some small patches, particularly around the edges. There are some shallow cracks around the details of Hat-Hor.
|
|
| E.62.48
|
Intact if only a fragment. The glyphs are still very clear, except one of the right hand side, the fourt glyph down, that has been rubbed away. There is also a white deposit at the bottom of the object on the right. Overall there has been very little degredation of the wood.
|
|
| E.62.52
|
Intact. There are chips all over the object, some that just remove paint others that take some wood as well, particularly on the the left side of the beetle its self. There is a large white deposit on the right wing whcih has collected where some paint has chipped away.
|
|
| E.62.53
|
Intact, but missing what is stated above. There is some degredation of the wood and alot of the detail is missing. There are holes on the head and base where extra detail has disapperared.
|
|
| E.62.59
|
Broken in three (previously written as two) places and a fragment missing. The cracks are very evident and the sealant used has left a glaze on the underside of the pot. There are also several scratches on the base gained through general ware and tear.
|
|
| E.62.61
|
Intact and complete, there are several small chips missing from the lip. There is some discolouration of the Alabaster.
|
|
| E.62.8
|
Intact and the surface remains smooth although discoloured to red, green, yellow, black, brown and orange. There is still lustre on the surface and the incised lines are still clear except for the two on the outer surface. Two small holes have formed in the folded over rim.
|
|
| E.62.9
|
Teeth are all different lengths and there are deposits caught between teeth. The bottom of the comb appears darker in colour, perhaps slightly damp.
|
|
| E.63.1
|
Fragmentary but intact. There are no major cracks, but there is a large amount of muddy deposit all over the artefact.
|
|
| E.63.13A
|
Single fragment from the rim of a dish or bowl. The blue glaze is well preserved. There is a large malformation in the top right hand side of the fragment, and there are several shallow scratches in the surface.
|
|
| E.63.13D
|
Single fragment. The blue glaze is well preserved. There are several very shallow scratches on the surface and one large chip missing from the lower of the sculpted lines.
|
|
| E.63.15
|
Intact and complete. There are slight areas of bronze discolouration.
|
|
| E.63.18
|
The fragment is intact. The ends of the fragment are tainted by a brown deposit. The inscription is very scratched on one side, with one particularly large scratch.
|
|
| E.63.24
|
Three chips on the lip. Several defects all around the artefact, one has been filled in. Only a few of the defects are deep enough to show the inside of the pot: it is circular patch of grey discoloration approximately two-thirds of the way down.
|
|
| E.63.4
|
Intact and complete. Much of the glaze and colour has rubbed away particularly on the right side of the front. There is also some dark miscolouration at the top of the head-dress. Compared to it's partner the details of the face are much more vague.
|
|
| E.65.16
|
Intact and complete, the glaze has gone abd there is no more painted detail. There are areas of white deposit all over the artefact.
|
|
| E.65.3
|
Complete, but repaired. There three large breaks in the pot that have been repaired but are still very evident near the rim. Although the surphace is still smooth a large amount of the red pigment on the out side has worn away while similar occurances inside have meant that some of the decoration has been lost.
|
|
| E.65.8
|
Condition is excellent except the leather is stiff and therefore delicate. Left: point is missing from toe, leather straps are broken and incomplete. Right: leather straps complete but broken on the left hand side.
|
|
| L.2013.10.7
|
Intact but deposits on the surface make seeing the iconography very difficult. Poor condition makes it impossible to see if there are any inscriptions. The coin edge is very uneven.
|
|
| L.2016.3.9
|
Fragment; broken off at ca. 2/3 of foot. Grey-brownish deposits on foot and older fracture edges, which are limited to two sides at the foot section. The other fracture edges are younger. The black paint is slightly worn but well preserved for the most part.
|
|
| REDMG:1926.99.50
|
Complete except for a chip missing from the mouth; comprised of three rejoined fragments (two of which are small rim pieces); surface slightly gouged
|
|
| REDMG:1935.87.25
|
Side A is intact by side B, once broken in, has had two large pieces rejoined, while one piece is missing. The rim and one handle are chipped. Decoration worn, especially on handles and side A.
|
|
| REDMG:1935.87.34
|
Complete but foot has been repaired. Ruddled figures are fading and now orange. Paint around foot is eroding. Deposits at mouth and inside and especially under base.
|
|
| REDMG:1935.87.35
|
Incomplete. Only head remains, no body. Lots of detail on both face and head, but both are marred by whitish deposit. Detail at tip of the head has broken off.
|
|
| REDMG:1947.13.1
|
The mouth has been repaired from five or more fragments, each handle from three fragments (with some parts missing and restored on the left handle). The body is reconstructed from 15 or more fragments and the foot has been restored in wood. There is a hole (perhaps original). In the base. Slightly chipped on the mouth, pitted, and scratched; traces of white plaster on the external surface, while the interior and bottom are covered with plaster. Faded decoration in patches.
|
|
| REDMG:1951.140.1
|
The black surface, slightly iridescent, is slightly chipped at the back. The red surfaces are eroded, especially on the woman's face, and stained, especially on the upper surface of the rim, the laurel wreath, and some of the figural scene.
|
|
| REDMG:1951.144.1
|
Rim and foot are cracked once and twice, respectively, but remain intact. There is a gouge on the rim, as well as some smaller chips on the base. Decoration damaged with cracks and reddish-brown stains. White deposits on lower part of rim and underside, as well as foot.
|
|
| REDMG:1951.159.1
|
Mouth missing, broken off at the top of the neck, where the joins to handles and body are cracked and scratched. The lower part of the amphora has been restored, using wood (for the foot) and plaster (still visible on the interior and around the joint between handles and neck). Some pitting on body, surface abrasion on stem.Parts of original base in 4.2.7
|
|
| REDMG:1951.1716
|
Surface slightly stained; one chip on lip. One side of the vase is lower than the other. There are wheel marks on the underside and body.
|
|
| REDMG:1951.1718
|
Surface slightly stained on interior, where much of the surface has eroded away; white deposits around lip on interior and on exterior. There are fingerprints on the base and one side of the vase is lower than the other.
|
|
| REDMG:1953.25.101
|
Deposits all over. Small, elongated hole in back of head with a white stone in clay above. Features are worn.
|
|
| REDMG:1953.25.105
|
Good amount of paint remains. Features are still distinguishable. Broken below belt and left side (arm area) missing.
|
|
| REDMG:1953.25.188
|
Intact. Relief features are worn. Pink and grey deposits all over, but mostly on back and base.
|
|
| REDMG:1953.25.23
|
Mouth missing. The surface has flaked away on much of the object, and it is pitted at the back; base and top of foot are chipped.
|
|
| REDMG:1953.25.25
|
Handle, mouth and most of neck are missing. The surface is cracked, and has peeled off in some parts at the back; only ghosts remain of the white details.
|
|
| REDMG:1953.25.43
|
One third of the rim is missing and the right side of the handle is chipped. The black glaze has chipped away, and there are tan deposits, especially around the mouth and the lower body.
|
|
| REDMG:1953.25.77
|
Both nozzles mainly missing, handle missing. Left hand nozzle volute has been restored, small hole from missing fragment, from this hole are radiating hairline fractures to the base. glaze is worn in places, large amount of deposit covering the entirety of the interior and the back portion of the exterior as well as other areas.
|
|
| REDMG:1953.25.81
|
Single fragment preserving some of a foot. The marble is rough, and there are a number of brown dirt stains, especially around the big toe, and the side opposite to the toes, where the foot has been broken off.
|
|
| REDMG:1953.25.83
|
Intact if fragmentary. The facial features, especially the nose and right ear, have worn down quite considerably although it is still clear what they are meant to be. The line of breakage is straight, falling from the right ear to the middle of the left side of the neck.
|
|
| REDMG:1953.41.1
|
Intact. Accretions from river sediment (light greyish brown, with some reddish brown in areas) cover most of the vase, especially the handles and foot, where the deposits have built up. The interior surface is pitted on reserved areas, and glazed surfaces are scratched and eroded, especially on the interior of the bowl and the lip.
|
|
| REDMG:1958.112.1
|
Comprised of ten or more rejoined fragments (breaks are concentrated around the neck, handle, and foot); stained all over, with pitting and scratches.
|
|
| REDMG:1958.37.1
|
Intact and complete. Wash and paint are worn in places, some white deposit on the body.
|
|
| REDMG:1964.1607.1
|
Intact, wash is worn and there are numerous chips. Tip of nozzle is slightly blackened, due to use. Small amount of pale deposit.
|
|
| REDMG:1964.1614.1
|
Nozzle tip missing, wash and decoration are both worn. Small amount of deposit all over, blackening around the wick hole may have been produced though use.
|
|
| REDMG:1964.1637.1
|
On the reserved side of the handle are some deposits as there are on one part of exposed clay at fracture. Lustre remains on black areas.
|
|
| REDMG:1964.1639.1
|
Handle is unchipped and in good condition. Paint has worn away and there are small traces of deposits on handle.
|
|
| REDMG:1964.1657.1
|
Complete and intact; areas of deposit around the foot and the main body. There are also scratch marks on the body and a very small chip on the rim.
|
|
| REDMG:1964.1664.1
|
Intact. Paint has been chipped in places. mostly around the rim. Both handles are missing completely.
|
|
| REDMG:1964.1668.1
|
Part of the rim and foot are missing, surface of the body is uneven, and most of the wash is worn.
|
|
| REDMG:1964.1681.1
|
White deposits have collected inside the object. Some areas of exterior surface are uneven.
|
|
| REDMG:1964.1688.1
|
Repaired in two pieces. Paint has faded on exterior surface and there are white deposits on the exposed clay at fracture. Small chips to rim.
|
|
| REDMG:1964.1710.1
|
Body undamaged but handle is missing leaving protrusions where it was attached. Deposits inside and out. There are faint fingerprints on the body.
|
|
| REDMG:1964.1712.1
|
Crack in base on the inside. Deposits make surface rougher. Stands lopsided and walls of body are not uniform.
|
|
| REDMG:1964.1716
|
Surface slightly stained; one chip on lip. One side of the vase is lower than the other. There are wheel marks on the underside and body.
|
|
| REDMG:1964.1718
|
Surface slightly stained on interior, where much of the surface has eroded away; white deposits around lip on interior and on exterior. There are fingerprints on the base and one side of the vase is lower than the other.
|
|
| REDMG:2004.98.1
|
Comprised of 8 rejoined pieces (although shoulder and body are intact), rejoined, with added resin, paint, and modern accretions around the neck and handle. Stains and yellowish-gray deposits on side and base.
|
|
| TEMP.2002.7.1
|
Intact. The rim suffers from several chips, one in particular quite large, opposite one of the handles. There is also evidence of wear on the glaze, as there is on the inside of the bowl. On the band inside the bowl can be found three deeper scratches, as well as the occasional small hole. The handles of the bowl also reveal small chips on their glaze, as well as small scratches. The band which leads down to and envelops the top of the foot, contains small scratches, and where it meets the foot are lots of small cracks in the glaze. There is also some yellowy/grey deposit, which we can also see on the base of the foot. The base is chipped slightly in places and there are small scratches in the glazed bands.
|
|
| TEMP.2002.9.1
|
Complete, but worn. There is one small chip on the rim and considerable wear. The handles are intact and one is chipped. The black gloss has faded in parts.
|
|
| TEMP.2002.9.16
|
Nose is missing (as it probably is from the original). Hair is uneven as parts of the cast are missing from one side. Cast is placed on a black stand, also made of plaster.
|
|
| TEMP.2002.9.29
|
The paint on the underside is in very bad condition; streaky, dull and flaking away at the edges. The paint on the topside is dull but not flaking. Paint has worn badly from rim. Deposits are on the edges.
|
|
| TEMP.2003.6.10
|
Three fragments of the same vessel's base. It appears that the body has mostly been scraped off around the joining point at the upper parts of the fragments, apart from a bit on b and two bits on c. a) There are adhesives on the interior and few spots have been chipped off. There are three tiny spots on the interior and a spot on the central part of the base, where there are also three cracks. b) Two tiny bits have been chipped off from the interior and a spot looks flaked off from the inner side surface of the foot. There are also traces of adhesives. c) Four very small parts have been chipped off from the interior. There are also traces of adhesives, especially on the interior, as well as two cracks on the central part of the base.
|
|
| TEMP.2003.6.13
|
Two uneven parts of a double handle. The glaze appears greenish or streaky at places and there are spots that the colour looks peeled off. There are also traces of white plaster.
|
|
| TEMP.2003.6.14
|
Two joining fragments of the lower part of the body of an amphora. White plaster on both sides (thicker on the interior). There are areas where the colour has been peeled off, as well as some pitting off from the left edge of the fragment. There are also adhesives.
|
|
| TEMP.2003.6.17
|
Fifteen fragments that belong to the same kylix. There are parts of the rim and body (a,b,g,k,l,m,n) of the body (c,h,i,j,o) and of rim, body and part of the handles (d,e,f). a) Should be rejoined to b. Interior: Layer of white plaster and small bits that have been pitted off. Exterior: Traces of white plaster and a spot that has been chipped off. b) Should be rejoined to a and c. Interior: White plaster and a large spot that has been chipped off. Exterior: Traces of white plaster and small spots that have been chipped off from the left and bottom edge of the fragment. c) Should be rejoined to b. Interior: White plaster and two areas that have been chipped off from the top edge of the fragment. Exterior: White plaster and two small spots that have been chipped off. d) Should be rejoined to e. There are two spots that have been chipped off from the rim and bottom part, as well as some pitting off (rim). Exterior: White plaster and a large spot that has been chipped off from the upper part of the body. The handle is also missing, apart from its lowest part. e) Should be rejoined to d. Interior: There are two spots (rim, bottom) that have been chipped off. Exterior: Traces of white plaster and a spot on the left that has been chipped off. Most of the handle is also missing. f) Should be rejoined to g and h. Interior: There is a layer of white plaster, few tiny bits that have been pitted off and a spot on the left that has been chipped off. Exterior: There is white plaster, a spot that has been chipped off from the top right side and some peeling off of the colour on the handle, whose largest part is also missing. g) Should be rejoined to f and h. Tiny bits that have been pitted off from the exterior. h) Should be rejoined to f and g. Traces of white plaster on the exterior. i) Interior: Layer of white plaster. Exterior: Traces of white plaster. j) White plaster on the interior. k) Interior: Layer of white plaster. Exterior: tiny bits that have been pitted off and slight traces of plaster. l) Could be rejoined to n. Interior: White plaster and a spot that has been pitted off. Exterior: White plaster and some bits that have been pitted off. m) Interior: Layer of plaster and a large spot that has been chipped off from the bottom left edge. Exterior: Traces of white plaster and a spot that has been chipped off from the bottom right edge. n) Could be rejoined to l. Interior: White plaster. Exterior: Traces of white plaster, some pitting off and a large spot that has been chipped off from the decorated area. o) Traces of white plaster on both sides.
|
|
| TEMP.2003.6.23
|
Nine fragments of the same vessel's shoulder (a and b) and body. a) Interior: The upper part seems to have been left reserved, but glazed?, but the lower part is streaky black. There are some bits that have been pitted off. Exterior: Traces of white plaster. There are two small spots that have been chipped off from the bottom of the fragment and some bits that have been pitted off from the joining point of the neck to the shoulder. b) Should be rejoined to c. Interior: Streaky black and two small spots have been chipped off. There are many bits that have been pitted off at the bottom of the fragment. Exterior: Traces of white plaster. There are tiny bits that have been pitted off. c) Should be rejoined to b. Interior: Streaky black, and a spot that has been chipped off. Exterior: Two small spots have been chipped off from the left bottom of the fragment. d) Interior: Has been scraped off. e) Interior: There are spots that have been chipped off. Exterior: There are two large spots that have been chipped off. f) Interior: Streaky black and several bits have been pitted off. g) Interior: Half of the surface has been scraped off and on the rest there are several bits that have been pitted off. Exterior: One small spot has been pitted off. h) Interior: There are large areas that have been scraped and few bits that have been chipped off. i) Interior: Part of the surface has been scraped off and there are bits that have been pitted off on the rest of the surface. Exterior: Two deep, short scratches?
|
|
| TEMP.2003.6.26
|
Fragment worn in places. There are white spots all over the interior, and small chips along the exterior.
|
|
| TEMP.2003.6.3
|
Two fragments probably from the same vessel. (a) Many spots have been pitted off and there are remains of adhesives after some form of restoration. (b) A thick layer of white plaster (after some form of restoration) has been peeled off from some areas and it is cracked, deposits, remains of adhesives and accumulation of residue, especially on the interior.
|
|
| TEMP.2003.6.6
|
a) Should be rejoined to b. It consists of part of the rim, one handle (the other one is missing) and body of the vessel. Small bits have been pitted off, as well as parts of the colour on some areas. The glaze also seems to be scraped off, apart from the surfaces decorated with palmettes. There are traces of white plaster (on the exterior), especially at the upper part of the handle's springs. b) Should be rejoined to a and c. Part of the rim and body of the vessel. The area above the decoration on the body seems scraped off. c) Should be rejoined to b. It consists of part of the rim, one of the springs of the other handle (that is missing) and part of the vessel's body. White plaster is apparent on most of the external surface. Traces of adhesives? exist on the internal surface of the rim d) Part of the rim and body of the vessel. Adhesives on the rim (interior and exterior). e) Part of the vessel's lower body. Tiny bits have been pitted off from both sides and colour has fadded away on some areas. f) Part of the vessel's resting surface. The foot is missing and there are adhesives and white plaster on the joining point of the foot with the base.
|
|
| TEMP.2003.7.31
|
Intact. Part of the left arm is missing, and the majority of the right arm has been broken off. There are surface scrapings all over the figure.
|
|
| TEMP.2003.7.49
|
Intact. Both sides of the coin are worn down, and the sides are chipped. There appears to be some small bits of green weathering around the coin.
|
|
| TEMP.2003.7.74
|
Well kept overall, though inner section has a few points where the paint has been chipped away slightly,and the line at the top also appears to have been worn away over time. Edges on the right side are slightly chipped.
|
|
| TEMP.2007.2.49
|
Fragment; Damaged by fire, with chipping of decoration probably due to this damage. Munsell colours are for unburnt and burnt parts respectively
|
|
| TEMP.2007.3.74
|
Slightly worn; edges are chipped
|
|
| TEMP.2007.3.82
|
Red in colour with slight green weathering; failry worn; edges are chipped all the way around
|
|
| Temp.2022.7.1
|
body and handle are intact, without cracks: missing a piece of the neck edge (a little fragment is inside the jug)
|
|
| temp.2022.7.1
|
body and handle are intact, without cracks; missing a piece of the neck edge (a little fragment is inside the jug)
|
|
| temp.2022.7.2
|
body is intact, neck is partially intact, the mouth and the rim are absent
|
|
| temp.2022.7.4
|
the body is intact, part of the upper neck is broken but fragments are all inside the jar
|
|
| temp.2022.7.5
|
the body and the two handles are intact, the neck is partially broken, five fragments of the neck are inside the jug, no cracks
|
|