| 14.9.114
|
Joins with Reading 14.9.115; surface feels a little rough, back of figurine uneven and has a jagged hole in it. White barely preserved. All over top of base is dark brown deposit (soil?). More of this dark deposit where the top half has broken off.
|
|
| 14.9.16
|
Small dots of deposit on the white slip and also on the fracture edges. The interior red colour appears a little streaky, but this was probably since production.
|
|
| 2006.12.52
|
Two fragments have been rejoined to make this single fragment
|
|
| 25.6.2
|
Intact except for the edge of the rim which is missing on one side. The inside show small areas of general wear, as well as a small patch of what looks like yellow varnish near the broken rim. There is also some white deposit in the reserved disk in the centre, and on one of the handles. The black glaze on the handles has been rubbed away in patches, as has the decoration on the main zone. There is more white deposit on the main zone, some of which runs in circles, showing the gradient of the material. There are cracks on the glaze around the top of the foot, below which are some denser patches of white deposit. This deposit is also evident on the base of the foot and inside it.
|
|
| 26.12.24A-B
|
The flat surface of the knob on the lid has a white deposit on it, which can also be found at the base of the stem, and around one side of the rim. Small cracks in the glaze are evident around the the base of the stem, and small scratches are clear around the surface of the rim. The very edge of the rim has some small chips in it. On the inside of the lid, there is one deep scratch, and a hole, as well as more of the same white deposit. The rim and inside of the main body has got more deposit on it, but this is a brighter white. The gloss also shows signs of wear with scratches and flakes in the surface. Near one handle, there is a chip on the rim. One handle is covered in a yellowish/white deposit. More pale white deposit can be found on the foot and on the black band above it. There are several small scratches and chips in the base of the foot.
|
|
| 34.2.1
|
Intact. There are four noticeable chips in the rim, as well as evidence of wear over the black surface. All over the Kylix are patches of wear and small scratches. The reserved disk in the centre has a lot of grey deposit on it, as does the inside of the rim. This deposit is also evident around the handles, and in small patches along the main zone. At the top of the stem, leading to the base, are lots of cracks and some flaking. There is a chip in the side of the foot, and the well in the base of the foot contains a lot of grey/white deposit.
|
|
| 34.8.2
|
this small lekytos is not intact, it is composed of five big fragments and five very small fragments, some flakes of clay are preserved in a little plastic bag. Bigger fragments are composed of more fragments brought together with glue. The paint is not uniform, is discolored and it is missing in some points. On the inside, in the upper part of the belly, there is a clay excrescence.
|
|
| 35.4.3
|
Intact. The rim of the pot shows two chips on the inside and three on the outside. As well as this, there is a grey deposit, which is evident in small areas all over the piece. The glaze on the inside is worn and there are small scratches all over. The outside also shows signs of wear, with small scratches all over the glaze. At the base of the foot, there is more deposit, but this is a white/cream clolour.
|
|
| 45.10.22
|
There are only 18 fragments preserved from this vessel. These consist of parts of the rim, neck, shoulder and body. a: It is repaired from two fragments, rejoined. Part of the rim (the smallest part of two), neck (including the spring of a triple handle) and shoulder (these consist the second part of this fragment). The fragment is chipped off in many areas (rim: ca. 5 spots/ interior of neck: ca. 10 spots/ neck: ca. 4 spots. There are also gouges on the joining points of the two parts. The upper part (bigger part) of the handle is missing. Apart from tiny bits that have been peeled off from the interior and few deposits, the glaze and colour are preserved in a good condition. b: It consists of three rejoined parts from the vessel's neck. Few bits are missing on the joining point and a spot has even been chipped off, there are deposits and cracking of the colour on the interior, as well as another spot that has been chipped off. Three shallow carvings are also apparent. c: It consists of three parts joined together (two big ones and a small one). Deposits on the interior, three scratches on the exterior, tiny bits that have pitted off and spot that has chipped off from the lower left end. d: Part of the body, colour has fadded away in some spots, and a part has been peeled off. Deposits. e: Part of the body. Deposits but in very good condition, apart from two areas that are chipped off and small bits that are pitted off. f: Part of the body. Apart from deposits in a very good condition. g: Part of the body. Deposits, otherwise in a very good condition. h: Part of the body. Few, tiny bits have been peeled off, also few deposits. i: It consists of two parts of the body. ca. 5 bits have been pitted off and three spots are chipped off; deposits. j: Small fragment in very good condition. k: Small fragment from the body; deposits. l: Small fragment from the body; deposits.
|
|
| 47.2.34
|
Similar in shape and attitude to 47.2.32 and 47.2.33. Intact, although in the worst condition of this group. Nose chipped, right hand ear worn. Concretion on face, back and right hand side.
|
|
| 49.4.1
|
The mouth is a little chipped and the neck has been repaired. There are bits missing from the shoulder, too. The largest part of the white bands has worn away, as has some of the paint on the foot. There are white and gritty deposits in the mouth and under the handle. The glaze below the meander is streaky. There is also colour loss on the back of the body but this appears to be due to firing.
|
|
| 49.8.9
|
Intact, except for tiny chips on the rim and three small gouges on the lower body. The vessel's condition is very good, as the paint is not worn and the glaze remains. There is a dent in the body but this was made during production. Only slight wearing of the purple dots but not so as they become indistinguishable.
|
|
| 51.4.8
|
Complete. The body mended from a number of joining fragments. Glaze flaked off on the top of the rim, body and handles. Small chip on one of the horizontal handles. The main zone decoration remains similarly intact, except for a few scratches on the surface, and in small patches, a misty light grey deposit. There is also some of this deposit around the ends of all three handles. Thinly applied glaze, especially on the back side of the vessel, allowing for the colour of the clay to be seen. On the resting surface of the foot is a chalky white deposit.
|
|
| 60.8.1
|
Intact. One of the handles broken off and restored. Small chip under this handle. Bad quality gloss that is not lustrous. Thinly applied on the exterior of the body and the foot ring. Deposits on the rim, handles and the underside of the foot
|
|
| 61.6.4
|
Complete and intact. Pitted slightly at the back of the body. Surface decoration flaked off on lower part of body and foot at the back
White deposits on left handle; white stain over front of body large white (salt?) deposit. One of the handles also has this white deposit and the upper part of the footring.
|
|
| 78.12.13
|
Intact, part of the base is missing, hairline fracture radiating from this damage. Wash is worn, especially on the decoration and base. Large amount of grey deposit all over, interior and exterior.
|
|
| 79.1.8
|
Complete, decoration very worn, filling hole is irregular; this may be due to it's production. Nozzle tip is blackened; probably from usage. nozzle end is scored with many lines. White deposit in places.
|
|
| E.23.44
|
Intact and complete. The blue glaze is quite worn in some areas, most notably at the top of the crown where it has toally worn away and reveals the original terracotta material. This is slightly true also around the ears.
|
|
| E.62.38
|
Very large chip out of the lip, crack going from edge of that crack, to and along base and then back up the other side of the vase. Another crack joins this crack together along the shoulder. The crack can be seen on the inside of the pot.
|
|
| REDMG:1953.25.77
|
Both nozzles mainly missing, handle missing. Left hand nozzle volute has been restored, small hole from missing fragment, from this hole are radiating hairline fractures to the base. glaze is worn in places, large amount of deposit covering the entirety of the interior and the back portion of the exterior as well as other areas.
|
|
| REDMG:1953.25.98
|
Fragment broken off from a larger item. There is a large amount of white pigment remaining on the suface; this suggests that it was originally white in colour. The nose is quite short, perhaps because it has been worn down.
|
|
| TEMP.2007.2.49
|
Fragment; Damaged by fire, with chipping of decoration probably due to this damage. Munsell colours are for unburnt and burnt parts respectively
|
|