| 11.10.3
|
Complete and intact. There are tiny air bubbles over the surface, as well as small areas of brownish deposit. Detailed markings on face and hands are slightly worn away. The left eyebrow, left eye, nose and mouth however, are all still clearly visible. Material on the resting surface has flaked away in areas. Originally painted red all over.
|
|
| 13.10.11.11
|
Intact, chipping around both holes and pitting all over the body of the bead which is now filled with a white deposit.
|
|
| 13.10.13
|
Intact, missing only small chips from the interior of the lip and the foot. White and black deposits in patches all over.
|
|
| 13.10.2
|
Fragment. Single piece from the centre of the blade of the knife, missing the tip and the lower part, where it would have been attached. Worn and abraded all over, especially on the upper left of the ridged surface. Lighter coloured deposits on the other surface.
|
|
| 13.10.23
|
Intact and complete; the surface has eroded all over, and completely through the body of the vase on its shoulder.
|
|
| 13.10.31
|
Head fragment, facial features worn. Damage to top of head and over right eye.
|
|
| 14.9.105
|
Missing lip. Worn all over surface.
|
|
| 14.9.114
|
Joins with Reading 14.9.115; surface feels a little rough, back of figurine uneven and has a jagged hole in it. White barely preserved. All over top of base is dark brown deposit (soil?). More of this dark deposit where the top half has broken off.
|
|
| 14.9.32
|
White deposits all over fragment. Black paint fading to red at the edges.
|
|
| 16.2.1
|
Incomplete and repaired. Glaze has lost lustre, and much has eroded, especially over the 'tail' end, leaving greyish-buff colour. A later segment has been added to body to replace a missing piece.
|
|
| 2004.10.4
|
Fragment. Chipped with large amount of deposit all over.
|
|
| 2005.3.36
|
reasonable, exterior has dark brown discolouration under handle, and there are numersou stratches over the zigzag
|
|
| 2008.7.12
|
Fragment broken on four sides and badly chipped over surface
|
|
| 2008.7.2
|
Single fragment broken on four sides and chipped all over.
|
|
| 2008.7.3
|
Fragment broken on two sides with worn area over parallel lines and chipped glaze
|
|
| 2008.9.116
|
Rather poor; the entire right enclosing side of the box is missing, some of the plastic shelving is missing, and one of the models of an amphora has fallen over.
|
|
| 22.3.40
|
Most of rim broken off on front and left side; slight break at top attachment of handle. Leaves and berry pattern almost entirely vanished. Glaze slightly chipped all over.
|
|
| 22.9.4
|
A third of the rim is missing; soil deposits situated around cup and white deposits all over.
|
|
| 23.11.26
|
Most of the paint in the lower half has been removed over time. The mouth of the aryballos appears to have had several chunks broken off of it, likely done over time.
|
|
| 23.11.27
|
Well kept, appears to be in one, complete piece, though the outside has had the paint removed in numerous spots. Bottom part has had most of the paint removed, likely caused over time.
|
|
| 23.11.31K2
|
The points of two of the triangular elements are missing. There is a break in the circle of the wreath, where one end has pushed up over the other.
|
|
| 25.4.2
|
Incomplete. The surface condition is not very good, there are small holes and scratchs all over the surface, in and out, as well as fading on the decoration. The rim shows several chips, and the handles are very uneven. The resting surface of the foot is very chipped and uneven.
|
|
| 25.8.5
|
Complete but made up of seven seperate pices stuck back together. The handle has several chips, on the middle and lower tiers. The tip of the highest tier has also been chipped, and all over the handle, the gloss shows evidence of wear, with tiny cracks and scratches. The top of the lid shows a few small flakes and chips, mainly on the decoration, and eratically over the surface, there is brown/grey deposit. The inside of the lid is reserved but still shows patches of dirt and a small amount of grey/white deposit around the rim.
|
|
| 25.9.1
|
One handle missing, the other repaired. Badly damaged all over, with paint flaking badly from the mouth area, body and foot having been repaired extensively and the glaze is a bad condition leaving the clay exposed. Plaster inserted in base to increase stability.
|
|
| 26.12.28
|
Complete. The rim of the neck is chipped and underneath one side of the rim, there is a hole in the neck. There are small holes and scratches over the surface, some deeper scratches around the base. Inside the mouth and on the resting surface of the base is some white deposit.
|
|
| 26.12.29
|
Complete. Body in two rejoined pieces. Knob on the lid is chipped on both sides and has been broken at the base of the knob and stuck back together. Several chips in the rim of the lid and some scratches. The body also has scratches and chips all over the surface, as well as two large chips in the rim of the base.
|
|
| 26.12.30
|
Intact. Flakes of glaze are missing all over the surface, both inside and out, especially around the edge of the handles and the rim. A white deposit is clear not only on the inside of the Kantharos, but also in large quantities on the outside, including the base of the foot.
|
|
| 26.12.8
|
Incomplete. Most of neck and all of mouth are missing. The decoration all over is very faded, especially on the body, leaving the surface very smooth. There is a large hole in one side just at the bottom of the main zone. The top and edge of the foot is chipped, on the inside of the resting surface is a small hole. There is a small amount of orange deposit on the resting surface of the foot.
|
|
| 26.2.68
|
Fragment worn in places; white spots all over the interior, and small chips along the exterior.
|
|
| 26.4.4
|
Restored from many separate pieces. Glaze on the rim is slightly worn, as are the handles. The outer surface is worn. There is a greyish-white deposit in patches all over the surface, especially around the spurs and the reserved area of the main zone, as well as the top of the foot. On the top ridge of the foot, there is a hole. Colour on the inside of the pot has mostly worn away, leaving only more of the same grey deposit. Lid missing.
|
|
| 26.7.12
|
Pin missing. Deposits all over. Chipped in areas.
|
|
| 26.7.14
|
Fragment. The gloss on the rim of the fragment is a little worn and the surface on both sides shows small scratches. On the handle, there are a couple of flakes missing, and a small hole, possibly from an air bubble. The gloss on the inside is much more worn, with big flakes missing, with a couple of substantially longer scratches. There is also a yellow/grey deposit all over the inside of the fragment.
|
|
| 26.7.15
|
Intact. All over shows small areas of wear, on the main zone there are small chips around the base of the handles. Above the stem, on the top of the foot, and inside the handles, there is a small amount of white deposit, including one large patch (which looks like it could have been used to fix a hole).
|
|
| 27.4.12
|
Complete; repaired from seven pieces. The rim is uneven, and contains two small but definite chips. All over the surface are small scratches and patches of wear. The pattern on the rim contains few subtle patches of red, the same colour as patches on the handles. Patterns in the centre of the bowl appear to have rubbed away in patches. Underneath, the patterns remain more prominant, but again small patches of wear are evident, especially around the rim. Inside the foot are greyish white deposits, that are also found underneath the rim in small patches near the handles.
|
|
| 27.4.2
|
Incomplete and repaired in seven pieces. The band on the rim, has mostly been rubbed away and on the inside there is a lot of greyish/white deposit. There are lots of small scratches all over the surface, including one long, deeper one at the base of the pot on the inside. On the outside, the glaze has also been rubbed away in patches, and on the leaves there are patches where it has come away in flakes. The foot is in pretty good condition, except for a white/cream deposit.
|
|
| 29.11.13
|
Missing (part of) head. Large areas of brownish-grey deposit all over body, with areas of white slip showing through in some places and chipped off elsewhere. On stomach, in between two front legs, is a small hole, perhaps from the firing process.
|
|
| 29.11.7
|
Intact. There is one chip on the edge of the rim, as well as a bit of wear. There is evidence of greyish/white deposit most noticeably around the rim and below one of the handles. Main zone in fairly good condition, with the usual evidence of wear and small scratches all over the surface. A large area of the the firing is red instead of black. There is a small whole in the stem of the foot, and some whitish/grey deposit around the edge of the foot and inside the base.
|
|
| 33.4.2
|
Complete but not intact. Rim of foot made up with plaster. Decoration worn in places, small holes and scratches all over surface. Lower bands on foot half missing because of restoration with modern materials, as is one handle.
|
|
| 34.10.16
|
Comprised of two rejoined pieces. Decoration on the front has faded, and resting surface is very uneven, as is the back. There are small scratches all over the surface and small holes at the top of the head. The back reveals lots of small cracks and holes. There is a white deposit on the chest area, which can also be found inside the base, as well as running along the cracks on the back.
|
|
| 34.10.17
|
Complete. The white slip has worn away in places, and there is a smooth grey deposit evident in patches. Also, the munsell colour shows through. The features of the face are still fairly clear, but the eyes seem worn. The surface all over feels smooth, but the base of the neck is slightly uneven and a bit chipped.
|
|
| 34.10.18
|
Complete and intact. The surface is uneven all over, and the red glaze has been rubbed away in areas of prominance; for example, knees, stomach, chest and features of the face. There are indentations and air bubbles around the chest area, and on the back of the figurine. Here, there are also lots of scratches on the surface.
|
|
| 34.10.22
|
Incomplete. Back broken away - had long rectangular opening. Scratches evident all over surface, and white deposit at top of head and down left arm.
|
|
| 34.10.24
|
Complete but not intact. Top of left arm has broken off and been glued back on. Blue of cloak still faintly visible, but a lot of brown deposit is evident all over the figurine. The top of the head is covered with an even darker deposit, that also encases right shoulder and arm. The swan is also entirely covered by it. Inside the back of the figurine is a whitish deposit, and the surface is very rough, with scratches and air bubbles in it.
|
|
| 34.10.27
|
Much colour loss and erosion of relief makes it hard to see. Some small parts have crumbled away at the base. Dark deposits in small amounts all over.
|
|
| 34.2.1
|
Intact. There are four noticeable chips in the rim, as well as evidence of wear over the black surface. All over the Kylix are patches of wear and small scratches. The reserved disk in the centre has a lot of grey deposit on it, as does the inside of the rim. This deposit is also evident around the handles, and in small patches along the main zone. At the top of the stem, leading to the base, are lots of cracks and some flaking. There is a chip in the side of the foot, and the well in the base of the foot contains a lot of grey/white deposit.
|
|
| 34.8.11
|
Intact, tip of nozzle and area of base chipped. Smaller chips all over the lamp. Glaze wearing, white deposit in places.
|
|
| 34.8.15A
|
Intact and complete, some dark marks over the surface. White deposits and one large scratch on underside.
|
|
| 35.4.3
|
Intact. The rim of the pot shows two chips on the inside and three on the outside. As well as this, there is a grey deposit, which is evident in small areas all over the piece. The glaze on the inside is worn and there are small scratches all over. The outside also shows signs of wear, with small scratches all over the glaze. At the base of the foot, there is more deposit, but this is a white/cream clolour.
|
|
| 37.7.3
|
Intact. Some glaze flaked off of handles. White deposits are wide spread over exterior surface.
|
|
| 38.4.3
|
Complete, appears intact. Paint extremely faded. Inside of mouth has over three small chips. There is one noticeable chip on the outside of the lip. The paint on the neck appears to have been worn away, because a pinkish clay is showing which does not appear to be a fading of the black decoration. There are at least two hairline cracks on the shoulder, with some of the clay worn away. The handles are in good condition with no noticeable chips, whereas the body has several chips and cracks. The base has a few small chips but is in very good condition.
|
|
| 42.9.1
|
Almost half of stephane missing on side B, while the decoration of its remaining part is scraped off almost completely.No decoration on the neck. Deep crack from the beginning of the missing stephane down to the Krater's shoulder. Body pitted over entire surface, although side A is in better condition, with the exception of a gouge under the right arm of the left maenad. Incrustations around the chipped base.
|
|
| 45.6.19
|
Decoration worn. Lots of grey and white deposit over surface.
|
|
| 45.6.4
|
Intact. Deposits all over making surface very gritty. Some wearing of black bands.
|
|
| 45.6.42
|
Poorly made/fired. Handle missing, black glaze only visible on lip and upper body completly worn away eleswhere. Surface rough and uneven, grey deposits over surface.
|
|
| 45.6.47
|
Small chip on rim. Glaze worn completely apart from in two very small areas. Areas of grey deposit over surface.
|
|
| 45.6.66
|
Intact, one side of the top of the central tube has chipped away, numerous small chips to the outer body. The black glaze is worn in places. There is a white deposit over areas of the exterior, the interior has a deposit too, wick hole is almost completely blocked with deposit.
|
|
| 45.6.71
|
Intact, very small hole bottom left hand side and a few small chips. Large amount of white deposit all over the lamp.
|
|
| 47.2.29
|
Lower part of body missing. Concretion all over figurine, especially at the back of the head and left hand side of body.
|
|
| 47.2.5
|
Assembled from 3 fragments. Missing one handle, some of the rim adjacent to that handle, and a large patch of the bottom of the bowl, adjacent to and slightly overlapping the stamped decoration. The other handle, previously broken off, with another rim fragment, has been rejoined. Some patches missing and scratches around the body on the interior and exterior, rim, handles over; slight deposits on the exterior.
|
|
| 49.10.2
|
Intact, small chip out of the back of the rim. White deposit all over with areas of blackening around the nozzle and around the rim.
|
|
| 50.10.6
|
Intact. Large piece rejoined from side A, but doesn't obscure decoration. Some pitting and chipping all over body. Small chip in rim by one of the handles.
|
|
| 50.4.22
|
Clay is suffering from corrosion, many deposits over surface. Detail lost on some of the features of the ram. Part of left ear broken. Handle broken and rejoined.
|
|
| 50.4.23
|
Intact, slight anomaly on the left hand side of the nozzle, ware all over the lamp with considerable amounts of wash missing. Outer ring around the discus is misshapen in one place, probably happened in manufacture. Protruding form on the discus has been broken off. Grey deposit in places, blackening at the end of the nozzle, probably from use.
|
|
| 51.1.1
|
Intact. Surface dulled by greyish-white deposits, especially thick at bottom of bowl on interior, small scratches and patches of wear all over.
|
|
| 51.1.4
|
Intact and complete. Surface slightly scratched, especially around rim and on the siren's left wing, with some yellowish-white deposits above the siren. Small scratches over surface, especially around the rim, with adhesive on the underside.
|
|
| 51.4.11
|
Comprised of 7 or more rejoined pieces. Surface worn and scratched, with chips to the rim, half of the left handle broken off, and grayish-white deposits all over..
|
|
| 51.7.1
|
Almost perfect condition except for slight discolouration of black gloss towards foot and a few tiny chips all over the vessel.
|
|
| 58.2.2
|
Deposits all over body, worsening at neck. Small chip to rim. Dent to body.
|
|
| 60.8.3A-B
|
Missing one handle, remaining handle chipped at point. Black worn/misfired (?) to red on lower part of body. Exterior decoration slightly worn and chipped all over. Side of lid chipped, one rejoined piece adjacent to large missing piece.
|
|
| 61.6.1.10
|
Over half the cup is missing, as well as the bottom of the stem and the foot. Slight discolouration on the interior.
|
|
| 61.6.3
|
One handle is missing, and there is a piece broken off the foot. Small scratches all over the surface, both inside and out, as well as a whitish deposit all over.
|
|
| 61.6.4
|
Complete and intact. Pitted slightly at the back of the body. Surface decoration flaked off on lower part of body and foot at the back
White deposits on left handle; white stain over front of body large white (salt?) deposit. One of the handles also has this white deposit and the upper part of the footring.
|
|
| 71.12.3
|
Nail bent over and rusted; one horseshoe panel missing.
|
|
| 73.9.3
|
Fragment. Handle broken at tip, with small patches of wear all over. Scratch on the left side of the handle, pointing towards rim. Only a suggestion of rim remaining. Pinky, grey deposits on inside of rim and suggestion of the same up the outside of the handle.
|
|
| 73.9.7
|
Incomplete, only a small amount of the cup remains, including one handle. Two pieces are glued back together. The glaze on the outside edge of the rim has completley worn away, and there are small scratches all over the surface. Both inside and out, there are traces of a whitish deposit, except on the foot where the deposit is more of a pinky colour.
|
|
| 78.12.12
|
Intact and complete, wash worn all over, especially on the left hand side of the body, small ammount of white deposit.
|
|
| 78.12.13
|
Intact, part of the base is missing, hairline fracture radiating from this damage. Wash is worn, especially on the decoration and base. Large amount of grey deposit all over, interior and exterior.
|
|
| 78.12.16
|
Intact, three small pits in the body of the lamp, none pierce through to the reservoir. wash is worn and chipped all over. Tip of nozzle is blackened, probably due to use. Small amount of grey/white deposit.
|
|
| 78.12.17
|
Intact, small chip on rim, blackening at the end of the wick rest, probably from use. Large amount of white deposit all over.
|
|
| 78.12.7
|
Intact and complete, decoration and wash worn in places. White deposit all over, especially on the interior, nozzle tip blackened, probably due to use.
|
|
| 78.12.8
|
Intact and complete. Wash is worn in most areas, White and grey deposits in patches over the base, handle and nozzle.
|
|
| 79.1.10
|
Intact, missing handle, small hole in the base. Lumpy deposit over areas of the lamp, wash wearing in places. Blackening of the nozzle due to use.
|
|
| 79.1.18
|
Intact, missing a section at the back of the lamp which could be where a handle has been broken off. Small amount of white deposit all over the interior and the exterior.
|
|
| 79.1.2
|
Intact, small section missing from the surface of the lamp on the left hand side causing hairline cracks. White and grey deposits over much of the surface of the interior and the exterior.
|
|
| 79.1.9
|
Back section of body missing, could have once had a handle attached, Chipped all over, small amount of white deposit on the interior.
|
|
| 83.10.1
|
Quite badly worn. It has been glued back together using three fragments. There seems to be a fragment missing at the bottom of the statue, therefore the figurine is incomplete. Most of the features of the statue are badly worn. There are many soil deposits all over the figure. Inside the hollow figurine there appears to be some sort of plant.
|
|
| 83.2.3
|
Fragment covered with black deposit, clearly broken off from another object, and is rough and bumpy, likely owing to damage caused over time.
|
|
| 84.8.3
|
Large chips around rim. Black spotted deposits over surface.
|
|
| E.2003.9.1
|
Base has a large chip in it resulting in a deep whole just above the base; large amounts of white and orange deposit all over the jar.
|
|
| E.23.12
|
There is quite a large chip on one corner, and a chip removed from the same side. There is quite a large amount of black deposit all over the object obscuring it's natural colour.
|
|
| E.23.20
|
Several small chips on lip. Some dark red and black has worn away. There is a large amount of white deposit all over the vase, sometimes in large patches.
|
|
| E.23.27
|
Intact, missing some small chips on the lip. There is a large amount of brown deposit all over the body and there are remnants of a Liverpool label.
|
|
| E.23.29
|
appears to have no restoration or recent damage. The pottery is very rough with innumerable shallow chips, and there is a large amount of white deposit all over the object, a particularly large patch can be found near the base.
|
|
| E.23.33
|
Intact. There is a large amount of white deposit all over the artefact, and several shallow chips out of the surface. The surface itself is very rough.
|
|
| E.47.6.7
|
Intact and complete, very shallow scratches all over the object.
|
|
| E.62.12
|
Intact and complete. Very little glaze has been removed but some brown deposit can be found on the underside and in the holes over all parts.
|
|
| E.62.31
|
Intact, with white deposits all over. There is a large but shallow chip near the base of the pot.
|
|
| E.62.32
|
Intact. There is a large area where the top layer of limestone has worn away revealing the orginal colour of the limestone. There is a large amount of brown deposit all over the artefact.
|
|
| E.62.34
|
One slight chip in the lip, shallow chips all over pot resulting in some of the top layer of clay being removed. Also some white deposit on the pot.
|
|
| E.62.52
|
Intact. There are chips all over the object, some that just remove paint others that take some wood as well, particularly on the the left side of the beetle its self. There is a large white deposit on the right wing whcih has collected where some paint has chipped away.
|
|
| E.62.8
|
Intact and the surface remains smooth although discoloured to red, green, yellow, black, brown and orange. There is still lustre on the surface and the incised lines are still clear except for the two on the outer surface. Two small holes have formed in the folded over rim.
|
|
| E.63.1
|
Fragmentary but intact. There are no major cracks, but there is a large amount of muddy deposit all over the artefact.
|
|
| E.65.16
|
Intact and complete, the glaze has gone abd there is no more painted detail. There are areas of white deposit all over the artefact.
|
|
| L.2011.1.1
|
Single fragment neck, lip and handle intact, broken at the junction between neck and shoulder. White-ish grey deposits all over.
|
|
| L.2011.1.19
|
Coated in rust on both sides, fragmented and broken with cracks all over
|
|
| L.2011.1.25
|
Chipped and scored all over especially on one face, covered in brown sediment and possibly made out of (granite?)
|
|
| L.2011.1.61
|
Chipped at the bottom, white-grey sediment all over.
|
|
| REDMG:1926.99.60
|
(Modern) lacquer over most of surface
|
|
| REDMG:1951.155
|
Intact. Deposits all over, especially on the front. Decoration worn.
|
|
| REDMG:1953.25.101
|
Deposits all over. Small, elongated hole in back of head with a white stone in clay above. Features are worn.
|
|
| REDMG:1953.25.188
|
Intact. Relief features are worn. Pink and grey deposits all over, but mostly on back and base.
|
|
| REDMG:1953.25.44
|
Comprised of four rejoined fragments, missing bottom of bowl, stem and foot, as well as three small chips on rim. Light tan deposits, especially on interior and tops of handles; decoration chipped all over.
|
|
| REDMG:1953.25.72
|
Grey and white deposits all over.
|
|
| REDMG:1953.25.78
|
Handle missing. Surface in good condition, glaze remains all over, a few small chips, one between handle joints has two radiating hairline fractures. Small amount of deposit on interior.
|
|
| REDMG:1958.112.1
|
Comprised of ten or more rejoined fragments (breaks are concentrated around the neck, handle, and foot); stained all over, with pitting and scratches.
|
|
| REDMG:1964.1601
|
Intact, slight chips around the filling hole andthe handle. Black glaze is worn off in large areas over the lamp on the exterior and interior. Small ammount of whie deposit.
|
|
| REDMG:1964.1610.1
|
Intact, many small chips in the surface, grey deposit over large amounts of the exterior and interior. Large amount of blackening around the nozzle, probably from use. Remains of a modern candle in the reservoir.
|
|
| REDMG:1964.1612.1
|
End of nozzle completely broken off, Handle has numerous chips, glaze is worn and chipped in places. White deposit over the base, handle and nozzle.
|
|
| REDMG:1964.1614.1
|
Nozzle tip missing, wash and decoration are both worn. Small amount of deposit all over, blackening around the wick hole may have been produced though use.
|
|
| REDMG:1964.1618.1
|
Right side of nozzle tip is missing. Large amount of white-grey deposit all over.
|
|
| REDMG:1964.1621
|
Worn gloss; whitish-grey deposits all over.
|
|
| REDMG:1964.1660
|
Intact. Slight grey deposits all over.
|
|
| REDMG:1964.1674
|
Comprised of four rejoined pieces; both handles broken off; light yellowish brown deposits all over (darker on the interior), obscuring all decoration except in the middle of one side.
|
|
| REDMG:1964.1713.1
|
Chips to rim. Surface has air bubble holes all over. Some flakes of clay removed inside. Grey deposits on underside.
|
|
| REDMG:1964.1719.1
|
Over half of the object is missing, but the half that remains is in good condition with no significant damage. Some deposits have collected in base.
|
|
| REDMG:2004.95.1
|
Restored (foot and handle) smoothed over with plaster (especially clear at join of handle to body and neck) with repainting (especially on handle). White glue remains where the foot was (more recently?) rejoined. Surface scratched and stained a dark orange (perhaps intentionally); dent just above foot.
|
|
| T.2012.11.28
|
Fragmentary and mildly chipped across its face and the edges, with small parts of paint having been rubbed off over time.
|
|
| TEMP.2002.9.28
|
Large flake missing from topside over zigzags. Thin deposits on edges. Black fading to red.
|
|
| TEMP.2003.6.26
|
Fragment worn in places. There are white spots all over the interior, and small chips along the exterior.
|
|
| TEMP.2003.7.29
|
Intact, complete. Surface chips all over figure.
|
|
| TEMP.2003.7.30
|
Intact, complete, paint has faded all over figurine, a chip on the left side of the head, and also on the right arm.
|
|
| TEMP.2003.7.31
|
Intact. Part of the left arm is missing, and the majority of the right arm has been broken off. There are surface scrapings all over the figure.
|
|
| TEMP.2003.7.74
|
Well kept overall, though inner section has a few points where the paint has been chipped away slightly,and the line at the top also appears to have been worn away over time. Edges on the right side are slightly chipped.
|
|
| TEMP.2003.8.4
|
Single fragment with grey deposits over surface.
|
|
| TEMP.2007.2.56
|
Fragment of a rim, glaze worn away, traces of white all over
|
|
| TEMP.2007.3.56
|
discolouration, worn all over; on obverse, text and image worn and on reverse, text on left is clear but right hand side is worn; complete
|
|
| TEMP.2007.3.57
|
frequently handled; worn all over; complete
|
|
| TEMP.2007.3.66
|
green weathering; fairly worn all over; complete
|
|
| TEMP.2007.3.70
|
discolouration; smooth all over; complete
|
|
| TEMP.2014.9.19
|
Fragment missing. Multiple small chips and scratches all over interior and exterior.
|
|