| 13.10.27
|
Intact, small piece missing from one side of the wick rest. White deposit in places, blackening around the wick rest, probably from use. Unglazed.
|
|
| 14.9.16
|
Small dots of deposit on the white slip and also on the fracture edges. The interior red colour appears a little streaky, but this was probably since production.
|
|
| 14.9.72
|
Some loss of paint on outer surface. Some surface damage to underside probably caused at time of fracture.
|
|
| 2005.7.17
|
Fragment. Poor. Decorated braid severely eroded and has spaces where previously there were probably wool (?) tapestry areas. A red-brown substance (dried body fluids?) adheres to the fragment.
|
|
| 34.10.7
|
Complete and intact, but surface worn and dulled, with some scratches and losses to glaze. Underside shows a deep groove (probably misfiring), with white deposits; brown patches on underside.
|
|
| 45.10.20
|
There are six fragments probably from the body of the same closed-shape vase (amphora). i) Small bits of the colour have been peeled off and few small spots have been pitted off. ii) The fragment has been burnt. Tiny bits are pitted off. iii) The colour has faded away and has been peeled off from spots. Chips are missing from the edges. iv) The colour has faded away on the contour of the motives. v) The fragment is burnt. Bits of colour have been pitted off. vi) Bits of the colour have been pitted off, especially at the top and right side of the fragment.
|
|
| 45.10.9
|
Ten fragments that probably belong to the same vessel. a) Tiny bit of the vessel's lower neck, part of the shoulder and the spring of the handle, which is missing. There are scratches on the exterior and two bits that have been chipped off. Deposits and plaster? on the interior. (The rest of the fragments are from the vessel's body) b) Should be rejoined to c. White plaster on the exterior and traces of it on the interior. A small bit has been chipped off. c) Should be rejoined to b. White plaster on the exterior and traces f it on the interior d) Few deposits on both sides and a small bit that has been pitted off from the exterior. e) Few deposits on the interior and traces of white plaster. A tiny bit has been chipped off from the exterior. f) White plaster and deposits on the interior. Two bits have been chipped off from the exterior. g) The decoration appears as if it has been scraped off and there is a spot that has been chipped off from the exterior. h) A small spot has been chipped off. Deposits and traces of plaster on the interior. Added white colour has fadded away. i) There are adhesives on both sides and white plaster on the exterior. The decoration looks as if it has been scraped off, a tiny bit has been pitted off and a small spot has been chipped off. j) Traces of white plaster, especially on the interior. There is a small spot that has been pitted off.
|
|
| 50.4.23
|
Intact, slight anomaly on the left hand side of the nozzle, ware all over the lamp with considerable amounts of wash missing. Outer ring around the discus is misshapen in one place, probably happened in manufacture. Protruding form on the discus has been broken off. Grey deposit in places, blackening at the end of the nozzle, probably from use.
|
|
| 74.7.3
|
Small chip on rim, where gloss is worn; Good quality black gloss; Gloss flaked off rim and around the ring of the foot; white deposits on inside and on handle. Red misfired line around the ring of the foot probably caused during the firing in the kiln.
|
|
| 78.12.11
|
Intact, handle is missing the top half, decoration is very worn. Wash is mostly intact with a white deposit in areas. Very slight darkening around the tip of the nozzle probably from use.
|
|
| 78.12.16
|
Intact, three small pits in the body of the lamp, none pierce through to the reservoir. wash is worn and chipped all over. Tip of nozzle is blackened, probably due to use. Small amount of grey/white deposit.
|
|
| 78.12.17
|
Intact, small chip on rim, blackening at the end of the wick rest, probably from use. Large amount of white deposit all over.
|
|
| 78.12.19
|
Intact , hairline cracks on the surface of the shoulder, wash worn on the discus. Folds of clay still apparent from the joining of the upper and lower discus. Small amount of discolouration and blackening on the nozzle, probably due to use.
|
|
| 78.12.5
|
Intact, wash is worn and there are slight chips on the shoulder. Slight blackening at the tip of the nozzle, probably from use.
|
|
| 78.12.7
|
Intact and complete, decoration and wash worn in places. White deposit all over, especially on the interior, nozzle tip blackened, probably due to use.
|
|
| 79.1.4
|
Intact, chipped on the moulded ring around the discus, decoration worn. Wash is fading especially on the underside. Tip of nozzle blackened, probably from use.
|
|
| 79.1.6
|
Intact, worn wash and worn decoration. Nozzle blackened probably due to use.
|
|
| 79.1.7
|
Intact and complete, brownish to black wash waring in places. White deposit on the base and blackening around the nozzle, probably due to use.
|
|
| 79.1.8
|
Complete, decoration very worn, filling hole is irregular; this may be due to it's production. Nozzle tip is blackened; probably from usage. nozzle end is scored with many lines. White deposit in places.
|
|
| 87.2.1
|
Right foreleg and part of tail missing. Left foreleg has been restored. Traces of white slip. The once probably black colour of the decoration is now brown/red. The surface of the figurine is worn and scratched in places.
|
|
| E.23.11
|
Intact and complete, with many scratches on the top of the trapezoid. There is a large black deposit on the base, which viscous to the touch so is probably quite recent.
|
|
| E.23.46
|
Dents to surface and deposits inside what was once probably hollow. Some initial signs of deterioration around the hole in the centre.
|
|
| REDMG:1964.1610.1
|
Intact, many small chips in the surface, grey deposit over large amounts of the exterior and interior. Large amount of blackening around the nozzle, probably from use. Remains of a modern candle in the reservoir.
|
|
| REDMG:1964.1613.1
|
Missing most of the nozzle, small amount of wick hole visiably blackened, probably from use. Large amount of white - grey deposit on the interior, small amount on the exterior, concentrated mostly around the discus.
|
|
| REDMG:1964.1619.1
|
Intact, large chip on the left side of the nozzle, score from the rim to the filling hole, large number of small chips. Grey deposit in areas, small amount of blackening around the nozzle, probably from use.
|
|
| TEMP.2002.9.16
|
Nose is missing (as it probably is from the original). Hair is uneven as parts of the cast are missing from one side. Cast is placed on a black stand, also made of plaster.
|
|
| TEMP.2003.6.3
|
Two fragments probably from the same vessel. (a) Many spots have been pitted off and there are remains of adhesives after some form of restoration. (b) A thick layer of white plaster (after some form of restoration) has been peeled off from some areas and it is cracked, deposits, remains of adhesives and accumulation of residue, especially on the interior.
|
|
| TEMP.2007.2.41
|
Fragment of a rim, white plaster on exterior and interior, probably from an earlier restoration
|
|
| TEMP.2007.2.49
|
Fragment; Damaged by fire, with chipping of decoration probably due to this damage. Munsell colours are for unburnt and burnt parts respectively
|
|