There are 71 objects for which Condition contains → wash
2004.10.1 There are cracks on the body of the flask and on the foot where repair marks are visible. The black slip is worn. Fingerprint marks are still visible in the wash.
2008.7.102 Fragment, chipped along edges. Black wash worn on one side.
2008.7.104 Fragment, chipped along edges. Wash is scratched. Illegible handwritten pencil marks on interior.
2008.7.105 Fragment, chipped along edges. Wash is worn away and scratched.
2008.7.106 Fragment, chipped at edges. Wash is chipped, scratch along centre of exterior. 'Orvieto' handwritten in pencil on interior.
2008.7.107 Fragment, chipped. Wash has small chips.
2008.7.108 Fragment, chipped at edges. Wash is chipped and faded.
2008.7.117 Fragment , chipped at edges. Wash on interior and exterior has almost entirely worn away.
2008.7.119 Fragment, chipped at edges. Wash is worn, especially on interior.
2008.7.120 Fragment, chipped at edges. Long scratches on exterior wash. Wash chipped on interior.
2008.7.123 Fragment, chipped at edges. Wash on exterior is heavily scratched. Interior is chipped and scratched. On interior are illegible handwritten pencil marks and 'III' handwritten in ink.
2008.7.126 Fragment, chipped at edges. Wash on exterior is chipped and scratched. On interior is handwritten in ink: '31 M IV 1-15' and '8L5'.
2008.7.129 Fragment, chipped at edges, wash on interior is chipped, some scaratches on exterior. On interior is handwritten in ink: '1930 E4-3 I-II'.
2008.7.131 Fragment, chipped at edge. There are some small chips to the wash. There are some small intersecting lines hand-drawn in pencil on interior.
2008.7.133 Fragment, heavily chipped around edges. Wash has some small chips and scratches. Handwritten in pencil on interior is: 'I-II'.
2008.7.136 Fragment, chipped. Large v-shaped scratch on the interior. Wash is almost entirely worn away on the exterior.
2008.7.138 Fragment, chipped. The wash is almost entirely worn away, leaving just small spots.
2008.7.141 Fragment, heavily chipped on exterior, leaving only a rectangular raised section. Wash is almost entirely worn away.
2008.7.142 Fragment. Wash on exterior is chipped and scratched.
2008.7.145 Fragment, chipped. Cream wash and greyish-black overpaint are heavily chipped.
2008.7.147 Fragment. Wash on interior and exterior is heavily chipped. Both ridges are chipped away at one end.
2008.7.149 Fragment, chipped. Exterior a deep scratch towards the centre, and the darker wash is wearing away to reveal a different wash beneath.
2008.7.151 Fragment. Wash is chipped.
2008.7.159 Fragment, chipped at edges. Wash on interior, and desgin on exterior is worn. On interior, 'Hern Ar' is handwritten in pencil.
2008.7.59 Chipped and worn. Wash chipped. 'Aphrodite' and 'Aegina' handwritten in pencil on two different edges of fragment.
2008.7.84 Fragment, chipped and worn. Wash chipped.
2008.7.98 Fragment, chipped along edges. Wash ischipped and worn.
2008.7.99 Fragment, heavily chipped on two faces. Black wash is chipped.
2008.9.1 Fragment, chipped at edges. Extensive white spotting on interior. Exterior wash is worn away in places.
2008.9.12 Fragment, wash on interior and decoration on exterior are faded.
2008.9.13 Fragment, wash on interior and decoration on exterior chipped.
2008.9.22 Fragment, wash and overpainting is faded.
2008.9.9 Fragment, wash is heavily chipped and worn away, paricularly on exterior.
26.7.8 Complete and intact. Small chip on spout mouth, and slight dent to one side. Wash worn in places, small amount of deposit.
45.6.68 Intact, chip off the body opposite to the spout; Handle missing ? Nozzle slightly blackened suggesting use. Wash worn in certain areas, white deposit on the surface and inside the lamp.
50.4.23 Intact, slight anomaly on the left hand side of the nozzle, ware all over the lamp with considerable amounts of wash missing. Outer ring around the discus is misshapen in one place, probably happened in manufacture. Protruding form on the discus has been broken off. Grey deposit in places, blackening at the end of the nozzle, probably from use.
50.4.24 Comprised of two fragments rejoined with B72 glue. Wash has faded considerably in places, small amount of residue; handle slightly chipped.
50.4.25 Complete, but with nozzle glued back on with B72 glue. A few cracks on the discus, wash wearing in places. Small hole where spout joins discus.
78.12.1 Intact, top part of the vertical handle is missing, small hole in the left hand side of the body, chip on the edge of the base. Wash is worn in places, with a small amount of white deposit around decoration. Some blackening around spout.
78.12.10 Complete and intace, moulded designs worn. Wash worn and white deposits in places, black marks on the base.
78.12.11 Intact, handle is missing the top half, decoration is very worn. Wash is mostly intact with a white deposit in areas. Very slight darkening around the tip of the nozzle probably from use.
78.12.12 Intact and complete, wash worn all over, especially on the left hand side of the body, small ammount of white deposit.
78.12.13 Intact, part of the base is missing, hairline fracture radiating from this damage. Wash is worn, especially on the decoration and base. Large amount of grey deposit all over, interior and exterior.
78.12.14 Intact, small hole in left hand side of the body, wash fading in places with a large amount of white deposit on the body and on the discus. Chip on surface of discus.
78.12.15 Intact, chip on the base, underside of the nozzle and at the wick hole, small amount of chipping on the surface of the discus. Wash becoming worn in places, small amount of white deposit, mainly on the underside and on the interior.
78.12.16 Intact, three small pits in the body of the lamp, none pierce through to the reservoir. wash is worn and chipped all over. Tip of nozzle is blackened, probably due to use. Small amount of grey/white deposit.
78.12.19 Intact , hairline cracks on the surface of the shoulder, wash worn on the discus. Folds of clay still apparent from the joining of the upper and lower discus. Small amount of discolouration and blackening on the nozzle, probably due to use.
78.12.21 Intact, upper right half of nozzle is missing, long hairline crack reaching down into the centre of the base from ths damage. Signs of use visible on nozzle. Fracture around the edge of the discus continuing along the nozzle to the wick hole. Brownish red wash is worn, large amount of white-grey deposit
78.12.4 Intact and complete, some of the wash has worn in places. There is a large amount of white/grey deposit, including an amount making the filling hole smaller.
78.12.5 Intact, wash is worn and there are slight chips on the shoulder. Slight blackening at the tip of the nozzle, probably from use.
78.12.6 Intact and complete, Wash and some of the decoration is very worn. ther area around the nozzle has largly lost most of its wash, however there are traces of black indicating usage. Some white deposit on the base and a small amount on the discus.
78.12.7 Intact and complete, decoration and wash worn in places. White deposit all over, especially on the interior, nozzle tip blackened, probably due to use.
78.12.8 Intact and complete. Wash is worn in most areas, White and grey deposits in patches over the base, handle and nozzle.
78.12.9 Intact. Handle completely missing, left side of the nozzle is missing. Wash is worn and chipped in places, large amount of white-grey deposit mainly on the base and the interior, blocking air hole.
79.1.10 Intact, missing handle, small hole in the base. Lumpy deposit over areas of the lamp, wash wearing in places. Blackening of the nozzle due to use.
79.1.12 Intact, small chip to the end of the spout. Wash is wearing, especially at the back of the lamp. large amount of deposit visible through the wick hole. Small amount of deposit on the exterior, more on the base. Nozzle tip blackened, possibly from use.
79.1.16 Intact, upper portion of handle missing, filling hole shape slightly obscured by missing area of discus. Wash worn in most place, superficial chips in the body blackening along the left side of the shoulder, nozzle and all though the interior.
79.1.4 Intact, chipped on the moulded ring around the discus, decoration worn. Wash is fading especially on the underside. Tip of nozzle blackened, probably from use.
79.1.6 Intact, worn wash and worn decoration. Nozzle blackened probably due to use.
79.1.7 Intact and complete, brownish to black wash waring in places. White deposit on the base and blackening around the nozzle, probably due to use.
REDMG:1951.160.1 Nearly intact, with a large piece rejoined to the rim. Rim slightly scratched and red surface slightly worn; light grey deposits cover the underside. Red wash on figures seems to be wearing off.
REDMG:1953.25.79 Intact, two small chips on the left side of the foot. Wash worn, especially on the back and right hand side of the body. Small amount of white deposit around the foot and on the interior.
REDMG:1958.37.1 Intact and complete. Wash and paint are worn in places, some white deposit on the body.
REDMG:1964.1603.1 Intact, wash mostly worn off, small amount of pitting on the base. Large amount white - grey deposit on the interior, lesser amount on the exterior.
REDMG:1964.1604.1 Large part of handle missing, most of the wash has worn off. Slight hairline crack in the base, rust coloured mark on the front right of the body.
REDMG:1964.1605.1 Intact, chip in filling hole rim, top of wick hole, left side of nozzle, left side of body and two chips on the foot. Wash worn and chipped.
REDMG:1964.1606 Complete and intact, red wash worn in places, white deposit on exterior and heavily on the interior. Blackening aruond the nozzle due to use.
REDMG:1964.1607.1 Intact, wash is worn and there are numerous chips. Tip of nozzle is slightly blackened, due to use. Small amount of pale deposit.
REDMG:1964.1608.1 Intact, chips all around the edge of the foot, on the left hand side of the shoulder, filling hole rim, on the top of the nozzle and at the end of the nozzle. Wash worn and chiped in places, deposit mostly on interior.
REDMG:1964.1614.1 Nozzle tip missing, wash and decoration are both worn. Small amount of deposit all over, blackening around the wick hole may have been produced though use.
REDMG:1964.1668.1 Part of the rim and foot are missing, surface of the body is uneven, and most of the wash is worn.