| 14.9.110A
|
Very fragmentary. Part of the body, rim and one handle preserved, pieced together from fragments. Chips around the rim and the body Gloss worn on handle. On the interior gloss is not lustrous, on the exterior is still shiny.
|
|
| 14.9.115
|
Fragment. The surface feels very smooth, but the back is slightly uneven. There is a long crack running down one shoulder and at the edge of the hairline. Little areas of greyish deposit running through contours of body. Once thought to join Reading 14.9.114.
|
|
| 14.9.50
|
Band around rim on top and both sides is fading. Paint faded red from black on the outer surface. Very sharply fracture from vessel. Many surface cracks. The fracture is in two layers and is not a clean break.
|
|
| 14.9.6
|
Fragment. Paint is still clear and not very tarnished.
|
|
| 2003.3.37
|
Interior in in good condition, one of the bands is very faded and only traces remain of the added red. Also a patch of dark brown discolouration. Exterior is heavily discoloured with gray and brown build up, added red is visible underneath
|
|
| 2005.3.19
|
fragment, exterior decoration is slightly chipped, interior is very worn
|
|
| 2005.3.20
|
fragment, paint is very worn on interior and exterior
|
|
| 2005.3.21
|
Fragment, very worn, the possible decoration on the exterior is very worn
|
|
| 2005.3.27
|
Fragment, heavy white deposits, black on neck is very worn, only a couple of patches remain
|
|
| 2005.3.29
|
Fragment, not good, exterior is very faded and has dark brown discolouration, interior is in better condition
|
|
| 2005.3.39
|
Not in good condition, the interior band is very worn and the exterior decoration is very worn and covered by gray deposits
|
|
| 2005.3.40
|
Black decoration is very worn and faded, plus some dark brown deposits on exterior
|
|
| 2006.12.126
|
Fragment; very worn
|
|
| 2006.12.19
|
Fragment; Decoration very worn
|
|
| 2006.12.32
|
Fragment; Decoration very faded
|
|
| 2006.12.51
|
Fragment; decoration very worn
|
|
| 2006.12.57
|
Fragment; very worn decoration
|
|
| 2006.12.62
|
Fragment; decoration on outside very worn
|
|
| 2006.12.69
|
Fragment; very worn decoration
|
|
| 2006.12.77
|
Fragment; decoration very worn
|
|
| 2006.5.36
|
very good, complete
|
|
| 2006.8.4.84
|
Gragment, glaze is very faded, chipped
|
|
| 2007.10.2.315
|
Very worn, but intact
|
|
| 2007.10.2.501
|
Intact, very worn
|
|
| 2007.4.108
|
Very worn decoration; accretion between handle and pot
|
|
| 2007.4.116
|
Fragment; very faded decoration
|
|
| 2007.4.60
|
Fragment, very worn
|
|
| 2007.9.7
|
Fragment, paint on outside surafce very worn, paint on inside surface slightly chipped.
|
|
| 2008.7.100
|
Fragment; completely encrusted in dirt throughout other than a very few small bits where black glaze can be seen.
|
|
| 2008.7.16
|
Fragment broken on five edges very scratched and worn glaze, edges are worn smooth
|
|
| 2008.7.174
|
Fragment; very well worn, especially around broken edges; extensive dirt deposits on remaining decoration.
|
|
| 2008.7.18
|
Fragment. Decoration and glazing in good condition, very minor chipping. "Aegina" handwritten in pencil on the interior.
|
|
| 2008.7.184
|
Fragment; badly worn throughout, decoration very faded, interior badly chipped and caked with dirt.
|
|
| 2008.7.187
|
Fragment; if exterior did have color, it is very badly worn down; heavy dirt throughout.
|
|
| 2008.7.26
|
Fragment. Very slight chipping and wear.
|
|
| 2008.7.61
|
Fragment, chipped and worn. Decoration very chipped.
|
|
| 2008.9.118a
|
Very good, if not perfect condition.
|
|
| 2008.9.118c
|
Very good; basket no longer attached to rest of model, some bits of foam coming detached.
|
|
| 2008.9.18
|
Fragment in 2 halves, glued back together with join vertically down centre. Decoration is very faded.
|
|
| 22.11.1
|
Intact. Chalky white deposits. Colour remains good. Very minimal surface damage.
|
|
| 22.3.26
|
Part of rim (about 1/4) is missing. Several very small chips and scratched areas can be found on the top surface of the plate, as well as one larger part that is gouged out. Also very small chips are visible on the underside of the plate and a patch near the missing rim is unevenly fired (red instead of black).
|
|
| 25.4.2
|
Incomplete. The surface condition is not very good, there are small holes and scratchs all over the surface, in and out, as well as fading on the decoration. The rim shows several chips, and the handles are very uneven. The resting surface of the foot is very chipped and uneven.
|
|
| 25.8.1
|
Much repaired and restored and some re-painting at joins. Surface is very soft and dusty. Paint is nearly compleetly worn off from mouth and foot. Design is still distinguishable.
|
|
| 25.8.6
|
Incomplete, neck and mouth glued back on, most of foot still missing. Decoration glaze has become very worn. The rim of the mouth is chipped, and there is a large hole in one side of the shoulder. Most of the decoration on the body is missing, the band below it, very faded. Foot barely remains.
|
|
| 26.12.23
|
Intact. Band around rim covered in scratches and small areas of wear. Daub in centre also scratched, very centre is chipped, with a small crack in the middle and small areas of white deposit. Scratches also evident on the outside, some blobs also slightly chipped. Bottom of base uneven, with a small crack running across the middle.
|
|
| 26.12.24A-B
|
The flat surface of the knob on the lid has a white deposit on it, which can also be found at the base of the stem, and around one side of the rim. Small cracks in the glaze are evident around the the base of the stem, and small scratches are clear around the surface of the rim. The very edge of the rim has some small chips in it. On the inside of the lid, there is one deep scratch, and a hole, as well as more of the same white deposit. The rim and inside of the main body has got more deposit on it, but this is a brighter white. The gloss also shows signs of wear with scratches and flakes in the surface. Near one handle, there is a chip on the rim. One handle is covered in a yellowish/white deposit. More pale white deposit can be found on the foot and on the black band above it. There are several small scratches and chips in the base of the foot.
|
|
| 26.12.7
|
Repaired from sixteen pieces, although missing a large fragment (6.0) from one side, including one handle. Decoration very worn. Fabric roughened on one side, where it is more orange than on the rest of the vessel. Interior blackened with dirt.
|
|
| 26.12.8
|
Incomplete. Most of neck and all of mouth are missing. The decoration all over is very faded, especially on the body, leaving the surface very smooth. There is a large hole in one side just at the bottom of the main zone. The top and edge of the foot is chipped, on the inside of the resting surface is a small hole. There is a small amount of orange deposit on the resting surface of the foot.
|
|
| 26.12.9
|
Complete and intact. Very small chip on base. Black has faded to reddish brown colour. Paint and gloss worn of on some areas of the body.
|
|
| 26.2.34
|
Top band on underside very badly worn and almost indistinguishable. Surface scratches and discolouration and small deposits at top. White on topside is fading but still visible and the shiny glaze remains on the black/brown.
|
|
| 26.2.56
|
Inside of neck very worn.
|
|
| 26.4.2
|
Complete but stuck back together from eight(?) seperate pieces. The glaze both inside and out is very worn, and the rim shows chipping and flaking. The inside of the pot is not completely smooth and there is a grey/white deposit, especially around the inner rim. Both of the handles have a lot of the same grey/white deposit on them, as well as big worn patches on the glaze. There is more deposit on the outside, especially around the foot. The surface outside is also in fairly bad condition, the surface revealing lots of small scratches and chips. The top of the foot has two significant chips in it but other than that it is in good condition, showing only small cracks running through the glaze in the well on the underneath of the foot.
|
|
| 27.3.8
|
Intact but with deep chips in body. Top half of object very badly worn, and decoration faded.
|
|
| 27.4.3
|
Intact and complete; chips and pink deposits on the rim; pitted surface. On the outer surface, some of the glaze is very faded, especially on the base.
|
|
| 28.6.6
|
Damage to one handle almost breaking the circle. Complete handle has deposits (perhaps from burial). Paint is very worn and in most places only staining remains. For such a fragile rim it is in excellent condition with no chips.
|
|
| 29.11.2
|
Intact. Paint slightly worn in places but overall in very good condition. Bad quality of gloss fired brownish. Gloss applied thinly on the exterior of the mouth and the handle.
|
|
| 30.11.4
|
Complete but repaired. The paint has become very faded on the exterior more than the interior surface. The handles are intact, but the paint is lost. Material is very soft and fine.
|
|
| 30.4.1
|
Incomplete. Two missing handles and pieces glued back together. The decoration has faded and shows red instead of black. On the outside especially, much of the decoration has faded or flaked away. Band around the top of the foot very worn. Some small patches of grey deposit on the surface.
|
|
| 34.10.15
|
Intact. The surface of the rattle is very rough, scratched, with peeling slip and dark grayish-white adhesions. There are three large cracks at the top of the ovoid part.
|
|
| 34.10.16
|
Comprised of two rejoined pieces. Decoration on the front has faded, and resting surface is very uneven, as is the back. There are small scratches all over the surface and small holes at the top of the head. The back reveals lots of small cracks and holes. There is a white deposit on the chest area, which can also be found inside the base, as well as running along the cracks on the back.
|
|
| 34.10.19
|
Complete and intact. The surface of the woman is incredibly smooth, the features of the face nearly worn away. There is a large scratch on the woman's right shoulder. As well as patches of white slip that is still evident, there is a smoky covering to the head, chest and knees. The base is very uneven.
|
|
| 34.10.24
|
Complete but not intact. Top of left arm has broken off and been glued back on. Blue of cloak still faintly visible, but a lot of brown deposit is evident all over the figurine. The top of the head is covered with an even darker deposit, that also encases right shoulder and arm. The swan is also entirely covered by it. Inside the back of the figurine is a whitish deposit, and the surface is very rough, with scratches and air bubbles in it.
|
|
| 34.10.26
|
Intact but not complete. Detail of the hair remains very clear, but the features on the face are less so. The eyes have been worn almost completely away, and the nose has a chip in one side. At the top of the forhead, just where the hair begins, is a hole. The top and back are uneven and show small holes on the surface. There is a small amount of dirty deposit at the base of the neck, and inside the hollow of the head.
|
|
| 34.8.2
|
this small lekytos is not intact, it is composed of five big fragments and five very small fragments, some flakes of clay are preserved in a little plastic bag. Bigger fragments are composed of more fragments brought together with glue. The paint is not uniform, is discolored and it is missing in some points. On the inside, in the upper part of the belly, there is a clay excrescence.
|
|
| 35.4.1
|
Complete but repaired and restored with plaster. Design remains very clear.
|
|
| 35.5.34A-Q
|
The decoration and pattern on all are in good condition and still very visible. The smaller parts are a bit more worn and the black gloss of fragment (e) is patchy in places.
|
|
| 35.5.37
|
Consists of four fragments glued together. A few surface chips, very shallow and small.
|
|
| 35.5.4-5
|
Outside, very worn
|
|
| 38.4.3
|
Complete, appears intact. Paint extremely faded. Inside of mouth has over three small chips. There is one noticeable chip on the outside of the lip. The paint on the neck appears to have been worn away, because a pinkish clay is showing which does not appear to be a fading of the black decoration. There are at least two hairline cracks on the shoulder, with some of the clay worn away. The handles are in good condition with no noticeable chips, whereas the body has several chips and cracks. The base has a few small chips but is in very good condition.
|
|
| 39.9.1
|
Mouth of jug appears to be missing its lip. Handle appears to have originally been black glazed, however now it is very worn. All decoration and figures on jug are quite worn. There is a large chip on the rim of the base, of the jug.
|
|
| 45.10.22
|
There are only 18 fragments preserved from this vessel. These consist of parts of the rim, neck, shoulder and body. a: It is repaired from two fragments, rejoined. Part of the rim (the smallest part of two), neck (including the spring of a triple handle) and shoulder (these consist the second part of this fragment). The fragment is chipped off in many areas (rim: ca. 5 spots/ interior of neck: ca. 10 spots/ neck: ca. 4 spots. There are also gouges on the joining points of the two parts. The upper part (bigger part) of the handle is missing. Apart from tiny bits that have been peeled off from the interior and few deposits, the glaze and colour are preserved in a good condition. b: It consists of three rejoined parts from the vessel's neck. Few bits are missing on the joining point and a spot has even been chipped off, there are deposits and cracking of the colour on the interior, as well as another spot that has been chipped off. Three shallow carvings are also apparent. c: It consists of three parts joined together (two big ones and a small one). Deposits on the interior, three scratches on the exterior, tiny bits that have pitted off and spot that has chipped off from the lower left end. d: Part of the body, colour has fadded away in some spots, and a part has been peeled off. Deposits. e: Part of the body. Deposits but in very good condition, apart from two areas that are chipped off and small bits that are pitted off. f: Part of the body. Apart from deposits in a very good condition. g: Part of the body. Deposits, otherwise in a very good condition. h: Part of the body. Few, tiny bits have been peeled off, also few deposits. i: It consists of two parts of the body. ca. 5 bits have been pitted off and three spots are chipped off; deposits. j: Small fragment in very good condition. k: Small fragment from the body; deposits. l: Small fragment from the body; deposits.
|
|
| 45.10.31
|
very damaged. Came from a lot that had been bombed during the Blitz in 1945
|
|
| 45.6.10
|
Intact but missing a small chip on the rim and a large chip from the foot. One further very small chip on the rim. Surfaces are slightly pitted with red showing through black surfaces.
|
|
| 45.6.27
|
Rim and lip badly chipped and broken on one side. Glaze very worn on surface particularly on lower body and edges, surface scratched and covered in areas with a grey deposit.
|
|
| 45.6.4
|
Intact. Deposits all over making surface very gritty. Some wearing of black bands.
|
|
| 45.6.47
|
Small chip on rim. Glaze worn completely apart from in two very small areas. Areas of grey deposit over surface.
|
|
| 45.6.71
|
Intact, very small hole bottom left hand side and a few small chips. Large amount of white deposit all over the lamp.
|
|
| 47.10.2
|
Incomplete. One handle and part of side missing. Surface of body in fairly good condition, showing only very small chips and small amount of greyish deposit underneath the handles. Inside the remaining handle is small amount of white deposit. The handle itself is slightly bumpy and chipped on the edges.
|
|
| 47.2.14
|
Intact. One handle missing, other handle in three pieces and glued back together. One one side three pieces joined together. Small chips around rim and scratches to the surface. Terracotta itself very fine.
|
|
| 47.2.23
|
Intact. White deposit on rim, paint worn in places. Design still very clear.
|
|
| 48.12.1
|
Intact but gloss very badly worn inside and out. Air bubble type holes, perhaps from firing.
|
|
| 49.1.2
|
Intact, with only slight chips on the base. The design remains very clear and the glaze is shiny and complete. Only the white paint has suffered a little. There are deposits inside the rim.
|
|
| 49.8.1
|
Intact but very small chips along the rim and body of mug. Small areas of paint chipped and deposit areas can also be found on the body as well as the base of the rim. Gloss is not lustrous. At parts on the body, gloss fired brown.
|
|
| 49.8.3
|
Intact and very well preserved. Paint remains clear and there are very few chips in the rim.
|
|
| 49.8.9
|
Intact, except for tiny chips on the rim and three small gouges on the lower body. The vessel's condition is very good, as the paint is not worn and the glaze remains. There is a dent in the body but this was made during production. Only slight wearing of the purple dots but not so as they become indistinguishable.
|
|
| 50.10.3
|
Intact. Preserved in a very good condition. large chip on one of the handles. Glaze flaked at small parts on the rim, on the interior, arund the foot ring. White depositions in the interior of the footring.
|
|
| 51.4.10
|
Intact. Colours and design remains clear. Glaze remains shiny. Very good condition. Small chips on the lower part of the body and the rim. Glaze thinly applied on the eyes on side B and clay can be seen underneath.
|
|
| 51.7.5
|
Complete but repaired at neck. Two small chips on the rim. Small areas of deposit found around the foot. Black very smooth and shiny, as is some of the red.
|
|
| 51.7.8
|
Intact. Gloss is in very good condition, shiny, with slight scratches on rim, neck and body. Surface of underside somewhat eroded, with white deposits.
|
|
| 51.7.9
|
Very worn around handle, mouth and one side of object. Suprisingly clear decorative banding and leaf motif in places. Intact.
|
|
| 56.8.1
|
Intact. Very small chips on the rim. Extensive areas of colour loss mostly around the handle and body of the piece.
|
|
| 57.3.11
|
Deposits. Small chips to top of head. Patches of very pale brown.
|
|
| 57.3.4
|
Paint on outer surface in very good condition with only a small area fading to red and small cracks appearing in surface. Not a clean fracture.
|
|
| 57.7.9
|
Very worn around handle, mouth and one side of object. Suprisingly clear decorative banding and leaf motif in places. Intact.
|
|
| 78.12.11
|
Intact, handle is missing the top half, decoration is very worn. Wash is mostly intact with a white deposit in areas. Very slight darkening around the tip of the nozzle probably from use.
|
|
| 78.12.3
|
Intact, slight chipping around the nozzle obscuring one of the volutes, the other is very faded as is the moulded design. very small amount of grey deposit. Unglazed.
|
|
| 78.12.6
|
Intact and complete, Wash and some of the decoration is very worn. ther area around the nozzle has largly lost most of its wash, however there are traces of black indicating usage. Some white deposit on the base and a small amount on the discus.
|
|
| 79.1.17
|
Complete and intact but surface very worn. Handle and nozzle blackened possibly from burning. White deposit in places. Slight depression on left hand side of the nozzle shaft.
|
|
| 79.1.8
|
Complete, decoration very worn, filling hole is irregular; this may be due to it's production. Nozzle tip is blackened; probably from usage. nozzle end is scored with many lines. White deposit in places.
|
|
| E.2002.8.1
|
Intact and complete, shallow and very small holes in various parts of the body.
|
|
| E.23.22
|
Intact, there is a large chip in the lip and several much smaller ones also. The surface is very coarse and covered in shallow scratches. There is also a noticeable chip missing from the foot. There is a deposit in the bottom of the orifice.
|
|
| E.23.29
|
appears to have no restoration or recent damage. The pottery is very rough with innumerable shallow chips, and there is a large amount of white deposit all over the object, a particularly large patch can be found near the base.
|
|
| E.23.31
|
Intact and complete, the pottery is very blackened in areas, particulary in one area around the base. There are shallow chips throughout the surface.
|
|
| E.23.33
|
Intact. There is a large amount of white deposit all over the artefact, and several shallow chips out of the surface. The surface itself is very rough.
|
|
| E.23.38
|
Intact, it is clear from the top and bottom part of the artefact that it has been removed from a larger object, since they appear to be thinner than the rest of the object and therefore look like 'connectors' of some kind. There appears to be very little degradation of the wood. There are some remnants of a white pigment on the lower half.
|
|
| E.23.43.2
|
Intact and copmplete, there are several impurities in the glaze, most notably a long line of black substance that appears to be stuck to the bead as it very raised from the surface.
|
|
| E.23.47.1
|
Most of the beads have lost their original sheen and several of them have a brown deposit on them. Since there are very few details on any of the beads/amulets it is difficult to say if any have been lost. Several of the objects have lost some of their original colour but all remain intact and complete.
|
|
| E.47.6.7
|
Intact and complete, very shallow scratches all over the object.
|
|
| E.62.12
|
Intact and complete. Very little glaze has been removed but some brown deposit can be found on the underside and in the holes over all parts.
|
|
| E.62.38
|
Very large chip out of the lip, crack going from edge of that crack, to and along base and then back up the other side of the vase. Another crack joins this crack together along the shoulder. The crack can be seen on the inside of the pot.
|
|
| E.62.39
|
Intact, but a large chip is missing from the lip, approximately one quarter missing. There is a crack going from one side to the other, starting and terminating at the shoulder, it goes around the base. Very little deposit.
|
|
| E.62.48
|
Intact if only a fragment. The glyphs are still very clear, except one of the right hand side, the fourt glyph down, that has been rubbed away. There is also a white deposit at the bottom of the object on the right. Overall there has been very little degredation of the wood.
|
|
| E.62.51
|
Intact. On the underside the wood is apparently water damaged and there is some rotting at the end of the cobra where it presumably once joined to the larger object (crown). There is a large crack on the underside near the very top head of the cobra.
|
|
| E.62.59
|
Broken in three (previously written as two) places and a fragment missing. The cracks are very evident and the sealant used has left a glaze on the underside of the pot. There are also several scratches on the base gained through general ware and tear.
|
|
| E.62.60
|
Intact. No major chips or dents (except one dent near the base which is a result of bad workmanship or is designed to allow the pot), very little deposit. The decoration is still very clear.
|
|
| E.63.13C
|
Single fragment. The blue glaze is well preserved, and there is very little visible damage to the surface although it is quite rough to the touch.
|
|
| E.63.13D
|
Single fragment. The blue glaze is well preserved. There are several very shallow scratches on the surface and one large chip missing from the lower of the sculpted lines.
|
|
| E.63.16
|
Intact and complete. Very little glaze has been removed but some brown deposit can be found on the underside detail and more so on the right legs of the beetle.
|
|
| E.63.18
|
The fragment is intact. The ends of the fragment are tainted by a brown deposit. The inscription is very scratched on one side, with one particularly large scratch.
|
|
| E.63.2
|
Intact and complete, inspite of the fact that the surface remains smooth much of the blue pigment is gone and the artefact is now mostly brown. There is very little loss of the carved details.
|
|
| E.65.17
|
Intact and complete, There is very little detail remaining, so it may have been painted on. The glaze has rubbed off and there is a white deposit on the amulet on both sides.
|
|
| E.65.3
|
Complete, but repaired. There three large breaks in the pot that have been repaired but are still very evident near the rim. Although the surphace is still smooth a large amount of the red pigment on the out side has worn away while similar occurances inside have meant that some of the decoration has been lost.
|
|
| E.79.2
|
Intact and complete, there is a large chip missing from the edge of the bowl opposite the channel described above. The surface of the artefact is very rough and there is a large amount of grey deposit on large portions of the plate.
|
|
| L.2011.1.14
|
Very worn and rusted, covered in sediment
|
|
| L.2011.1.17
|
Rusted with sediment build up and very worn
|
|
| L.2011.1.36
|
Fragmented, very worn and covered in light brown sediment inside and out
|
|
| L.2011.1.41
|
fragmented, chipped very worn and covered in a white and grey sediment
|
|
| L.2011.1.43
|
Fragmented, very worn, burnt in one corner and covered in a light brown sediment
|
|
| L.2011.1.46
|
Fragmentary, chipped and worn around the edge as well as on the very top. Two intentional holes on the top of the lid.
|
|
| L.2011.1.48
|
Scorched around the spout, and very worn and covered in beige sediment
|
|
| L.2011.1.50
|
fragmentary, very chipped and worn and covered in grey sediment
|
|
| L.2011.1.53
|
fragmentary, chipped and very worn with patches of light brown sediment
|
|
| L.2011.1.54
|
scorched on one surface and very worn and pitted. Flecked with whitish yellow sediment
|
|
| L.2011.1.64
|
fragmentary and very loose tesserae.
|
|
| L.2013.10.1
|
Intact, very worn with surface damage and grey deposits especially in the incisions
|
|
| L.2013.10.7
|
Intact but deposits on the surface make seeing the iconography very difficult. Poor condition makes it impossible to see if there are any inscriptions. The coin edge is very uneven.
|
|
| L.2013.10.8
|
Intact but with deposits on the surface make seeing the iconography very unclear.
|
|
| L.2016.3.12
|
Fragment with very slight cracks, and deposits on exterior.
|
|
| L.2016.3.29
|
Not very well preserved, almost nothing discernible. Not purged of deposits
|
|
| L.2016.3.31
|
Complete. The head has been broken at neck, the right leg at thigh and the feet have been broken off the base slab, but all of them were pieced together. Few whitish-grey deposits around the feet and neck, and very slight scratches on surface; one big chip on left cheek.
|
|
| REDMG:1935.87.13
|
Intact and complete, save for one medium chip on the rim. Surface very slightly pitted leading to lighter colours showing through black areas.
|
|
| REDMG:1935.87.19
|
Intact but with a couple of small chips on the body. Decoration very worn around mouth; images remain reasonably clear despite erosion of colouring.
|
|
| REDMG:1935.87.24
|
Very good, only a few small bits have been pitted off, particularly at the rim.
|
|
| REDMG:1935.87.4
|
Intact. Paint is dirty thus losing its glaze in most areas and appearing very dull. Large areas of black have worn away, especially on back of oinochoe, below handle. Base has large area of deposit.
|
|
| REDMG:1951.138.1
|
Very small chip on the disk on top of the knob; surface stained.
|
|
| REDMG:1951.146
|
Slightly chipped, especially on base; decoration inside and nearest the top on the outer surface is very worn.
|
|
| REDMG:1953.25.32
|
Missing two chips from the base, and cracked on the underside; glaze dulled in places and cracking around the handle attachments; light grey deposits on side B; added colour very well preserved.
|
|
| REDMG:1953.25.56
|
Intact. Base is a little unstable due to minor chips. Small traces of deposits. Slight scratches but is very good condition on the hole.
|
|
| REDMG:1953.25.88
|
Deposits lie on surface and in hollows beneath shawl. Facial features slightly worn on lower part of face. Material is very soft and crumbly. Some small surface cracks.
|
|
| REDMG:1964.1609.1
|
Intact and complete, moulded decoration very worn, small superficial cracks on the base (these could have been caused during it's making). Large amount of dark deposit on the surface.
|
|
| REDMG:1964.1635.1
|
Deposits on exterior surface and around handle as well as on interior surface. Paint very badly worn.
|
|
| REDMG:1964.1645.1
|
Paint has been very badly eroded. Deposits have built up around area where handle joins body.
|
|
| REDMG:1964.1657.1
|
Complete and intact; areas of deposit around the foot and the main body. There are also scratch marks on the body and a very small chip on the rim.
|
|
| REDMG:1964.1683.1
|
Fragment in good condition with no chips or scratches. Only very small deposits can be seen in the rim.
|
|
| REDMG:1964.1703.1
|
Intact. Some chips to body and rim but only very slight. Some pit holes on the body. Some wheel marks on bottom of foot. Very good condition.
|
|
| TEMP.2002.9.29
|
The paint on the underside is in very bad condition; streaky, dull and flaking away at the edges. The paint on the topside is dull but not flaking. Paint has worn badly from rim. Deposits are on the edges.
|
|
| TEMP.2003.2.4
|
Very worn with a few chips.
|
|
| TEMP.2003.6.10
|
Three fragments of the same vessel's base. It appears that the body has mostly been scraped off around the joining point at the upper parts of the fragments, apart from a bit on b and two bits on c. a) There are adhesives on the interior and few spots have been chipped off. There are three tiny spots on the interior and a spot on the central part of the base, where there are also three cracks. b) Two tiny bits have been chipped off from the interior and a spot looks flaked off from the inner side surface of the foot. There are also traces of adhesives. c) Four very small parts have been chipped off from the interior. There are also traces of adhesives, especially on the interior, as well as two cracks on the central part of the base.
|
|
| TEMP.2003.7.42
|
Single fragment, quite worn and indented on one side, perhaps where a handle attached. Surface very badly scratched. Black deposit in one corner (thickly applied black glaze?)
|
|
| TEMP.2003.7.64
|
Scratches on rim. Black gloss and white paint very worn. Chipped patch where handle would have been, has glue on it. Perhaps the handle was once stuck back on and has been broken off again. Underside of fragment covered in white deposits.
|
|
| TEMP.2003.7.69
|
Handle broken off. Fragment is very worn, scratched, and chipped at parts.
|
|
| TEMP.2007.2.50
|
Fragment of a base, very worn and chipped
|
|
| TEMP.2007.3.51
|
very well preserved; worn around the edges; slight chunk missing on one side
|
|
| TEMP.2007.3.54
|
very worn and frequently handled; chunk missing
|
|
| TEMP.2007.3.55
|
smoothed on one side; very worn; Complete
|
|
| TEMP.2007.3.59
|
well preserved, reatined colour; not very worn, still clear; images complete
|
|
| TEMP.2007.3.60
|
very well preserved; edges slightly worn; chips around the edge but mainly complete
|
|
| TEMP.2007.3.62
|
green weathering; reverse is very worn; complete
|
|
| TEMP.2007.3.63
|
fairly good; reverse is very worn; small chip missing on the edge
|
|
| TEMP.2007.3.64
|
green weathering and rough weathered surface; very worn by weather; complete
|
|
| TEMP.2007.3.67
|
red in colour; very smoothed and worn; complete
|
|
| TEMP.2007.3.69
|
very well preserved; hardly any wear; complete
|
|
| TEMP.2007.3.79
|
red and green discolouration; very worn; complete
|
|