| 2003.8.66
|
Single fragment, chipped on inside edge of rim. Numerous scratches can be found on the outside, as well as on the inside. The outside is also slightly chipped on the under part of the rim.
|
|
| 2005.3.36
|
reasonable, exterior has dark brown discolouration under handle, and there are numersou stratches over the zigzag
|
|
| 2008.7.125
|
Rim of spout partly chipped; only remnants of body of pot on one side directly under tip of spout; exterior: "I" written in pen on spout; "[Theta symbol]30[Gamma symbol]320-280" written in pen above break line of spout and body of pot
|
|
| 2008.7.44
|
Rim fragment broken on 2 sides; interior: chip in LH side of rim, "Aegina Aphrodite" written in pencil under rim; exterior: smaller chip in RH side of rim
|
|
| 22.3.43
|
Intact. Paint worn on mouth. Chips on base. Scratch on shoulder under handle.
|
|
| 25.6.3
|
Intact. Streaky glaze. Paint cracking from handle. White deposits under handle and base.
|
|
| 27.4.5
|
Intact. The rim, inside of the bowl and handles, all show evidence of wear, and there are considerable patches where all of the glaze has been removed. There are also small chips to be found on the handles, and on the inside of the rim. Where the glaze has been rubbed away, it has revealed a grey colour. There is also a thin crack running from the edge of the rim, to half way down the first black band. The well in the centre of the bowl is also slightly worn, to reveal a whitish grey colour, as well as a small crack running across the side. On the underside of the bowl, there is more evidence of general wear, including a chip just under the rim next to one of the handles. The bottom rim of the foot also reveals small chips, as well as a crack running across the middle.
|
|
| 30.11.2
|
Intact. Some deposits under handles
|
|
| 34.8.12
|
The handle has been rejoined to the lid, whose colour has been peeled off from many spots (underneath). The body has been reconstructed by 6 fragments. There are some bits missing at the joining points of the fragments, as well as from the incurved surface of the rim. Few bits have been chipped off from the base. The colour is wearing off from many spots, especially at the body. The deposits under the lid and inside the body almost obscure the glaze.
|
|
| 42.9.1
|
Almost half of stephane missing on side B, while the decoration of its remaining part is scraped off almost completely.No decoration on the neck. Deep crack from the beginning of the missing stephane down to the Krater's shoulder. Body pitted over entire surface, although side A is in better condition, with the exception of a gouge under the right arm of the left maenad. Incrustations around the chipped base.
|
|
| 45.6.15
|
Paint worn on mouth and body and base. Deposits under handle and on base.
|
|
| 48.12.3
|
Intact but missing several large chips from the rim, one from the handle joint, from the foot. Interior pitted so red fabric shows through. White deposits on the interior in the area under one handle.
|
|
| 49.12.1
|
Intact and complete. The surface is marred with scratches, gray deposits, especially in the bowl, under the handle, and on the foot; and slight chips, especially to the foot.
|
|
| 49.4.1
|
The mouth is a little chipped and the neck has been repaired. There are bits missing from the shoulder, too. The largest part of the white bands has worn away, as has some of the paint on the foot. There are white and gritty deposits in the mouth and under the handle. The glaze below the meander is streaky. There is also colour loss on the back of the body but this appears to be due to firing.
|
|
| 49.8.8
|
Intact. Small chip on the neck. Gloss is shiny and picture remains clear. On the back side of the body, gloss is faded. Paint worn on handle and under mouth rim. White paint has faded. white deposits on the top of the foot. Colour remains clear.
|
|
| 50.4.15
|
Grey deposit inside bowl. Glaze chipped in places and worn around rim and handles. Crack running around one side of bowl ending under handles intersecting mid-way with crack running to rim. Triangular chip on rim next to handle approximately 2cm on each side.
|
|
| 51.1.2
|
The vessel is reconstructed by many fragments and has been repaired (it has been conservated and parts of the shoulder and body have been filled in). Some bits of the colour have been peeled off (rim, handle, neck, body) and there are some small spots that are pitted off (rim, body). Lastly, there is a gouge under one of the side handles and another one on the central part of the base.
|
|
| 60.8.1
|
Intact. One of the handles broken off and restored. Small chip under this handle. Bad quality gloss that is not lustrous. Thinly applied on the exterior of the body and the foot ring. Deposits on the rim, handles and the underside of the foot
|
|
| 71.12.6
|
Large parts of bronze have broken away from the sides of the curved section. The most important aspect to note is the deterioration in colour to blue, green, black and brown. Only in a couple of areas does the true colour of the bronze show through. Deposits under the handle where it joins the body. Small hole to one side of the curved section.
|
|
| REDMG:1935.87.34
|
Complete but foot has been repaired. Ruddled figures are fading and now orange. Paint around foot is eroding. Deposits at mouth and inside and especially under base.
|
|
| REDMG:1951.152
|
Deposits under rim; white ground dulled and decoration otherwise scratched and faded in places.
|
|
| REDMG:1951.156.1
|
Foot is restored; missing one chip on right side of shoulder; deposits on mouth, lip, and under handle; surface decoration has faded.
|
|
| REDMG:1953.25.40
|
Comprised of five rejoined pieces, missing only a small chip from the rim; grayish-white deposits on rim, under handle, and resting surface.
|
|
| REDMG:1953.25.57
|
Slightly darkened on the shoulder under the handle.
|
|
| REDMG:1953.25.66
|
Lip, mouth and one handle missing, while the remaining handle has been rejoined. The base is chipped in two places; black glaze eroded. Gray deposits under the handle.
|
|
| REDMG:1964.1682.1
|
Small white deposits under handle and on interior surface.
|
|