| 11.10.3
|
Complete and intact. There are tiny air bubbles over the surface, as well as small areas of brownish deposit. Detailed markings on face and hands are slightly worn away. The left eyebrow, left eye, nose and mouth however, are all still clearly visible. Material on the resting surface has flaked away in areas. Originally painted red all over.
|
|
| 14.9.106
|
Gloss worn and flaked, especially around rim. Small chip on foot. Gloss is not lustrous.
|
|
| 14.9.18
|
White paint on interior surface has become discoloured and there is a large area of deposit. Surface of exterior is also damaged where paint had flaked away.
|
|
| 14.9.38
|
Small areas of paint have flaked away from the surface allowing reserved clay to show through. Larger flake from rim. Streaky red inside. Free from deposits.
|
|
| 14.9.48
|
Red paint nearly entirely worn from rim. Some surface damage to the outer surface as paint has flaked away. Some dark deposits on the outer surface too.
|
|
| 14.9.5
|
Paint flaked away inside mouth. Slight chip in rim. The clay has discoloured maybe due to age of firing. Black deposits inside.
|
|
| 2008.7.101
|
Single fragment. Surface worn, especially near handle and shoulder; scratches and encrustation on the body just below the shoulder; paint has flaked off throughout, especially on the handle; dirt. "Rhitsona" handwritten in pencil on the interior of the shoulder.
|
|
| 26.2.19
|
Underside has badly worn paint as it has flaked off, although traces of white can be seen. On the topside some of the paint has discoloured to brown. Paint has worn away from rim.
|
|
| 26.2.39
|
On underside paint has faded to red in some areas and in others the paint has flaked away. The topside has lost much of its white dots and bands. Small bits arte flaking away as well. Black meander faded to red.
|
|
| 30.4.1
|
Incomplete. Two missing handles and pieces glued back together. The decoration has faded and shows red instead of black. On the outside especially, much of the decoration has faded or flaked away. Band around the top of the foot very worn. Some small patches of grey deposit on the surface.
|
|
| 34.10.6
|
Intact. Poorly fired. Paint has since flaked off. Some deposits at base inside.
|
|
| 34.8.3
|
Neck and handle rejoined. Small chips to shoulder; small areas of white slip have flaked away.
|
|
| 37.11.5
|
Handle has been repaired; rim chipped; Gloss flaked off at places on the body, handles and the resting surface; small crack in centre of underside. Intact but assembled from 2 pieces. One handle, part of rim and body assembled.
|
|
| 37.11.6
|
Intact; slight chips on rim and footring; much of the glaze flaked off, especially on the exterior; large amounts of white deposit on interior, handles, and exterior. At alrge parts glaze is not lustrous. On one of the handles, glaze is fired light brown.
|
|
| 37.7.3
|
Intact. Some glaze flaked off of handles. White deposits are wide spread over exterior surface.
|
|
| 38.4.9
|
Comprised of six rejoined pieces, slightly chipped between joins (especially on handles). Some parts of surface flaked off, especially on white decoration. Slight white deposit on interior and exterior of bowl and top of stop.
|
|
| 39.1.1
|
Most of black glaze flaked off from upper part of vase.
|
|
| 45.6.16
|
Black gloss is still shiny at parts. Large flakes of clay have come away from the lower part of the body. Paint flaked off on mouth, handle, on a large part of the body decoration, shoulder and foot.
|
|
| 45.6.18
|
Large chip taken from body but not creating a hole. Paint around mouth and handle has flaked off. Bad quality glaze fired brown on the top of the rim, handle and neck.
|
|
| 45.6.5
|
Intact but clay has flaked on one side of body where there are also white and grey deposits. Paint has worn badly on handle and sides.
|
|
| 45.9.1
|
Possibly repaired. Paint is in bad condition and surface feels rough as paint has flaked away. Glaze has been lost and the paint on the foot and inside the mouth is untidy and streaky.
|
|
| 46.9.1
|
Intact. Gloss has lustre and white design is undamaged. Small chips on body and top of the rim. Black gloss flaked off handle.
|
|
| 47.2.10
|
Glaze remains shiny on the exterior. Flaked off the lower part of the body, underside and on the top of the rim. chips on around the base and on the underside.
|
|
| 47.2.7
|
Mended from a number of joining fragments. Small parts filled in with plaster (especially on left side. Gloss flaked off on part of the handle,rim and body. It is not lustrous. Towards the foot, thinly applied gloss that leaves parts of the clay to be seen.
|
|
| 47.2.8
|
Rim and side of bowl comprised of three rejoined pieces, although lustre and stamped design remain clear. White deposition on the ring foot. Gloss flaked off from part of the rim and the body. Gloss is not lustrous.
|
|
| 48.12.10
|
Mouth missing. Some flakes of paint from body have left a rough surface. Part of the white paint flaked off. Gloss is silvered on the lower part of the body. A small chip on shoulder. Gloss flaked off the handle and part of the decoration on the body.
|
|
| 48.12.4
|
Part of mouth missing. Paint badly worn. flaked on most part. Scratches on the body.
|
|
| 48.12.5
|
Intact. Much of paint flaked off. Small chip to lip.
|
|
| 48.4.1
|
Complete, but stuck back together from six seperate pieces. The rim shows one definite chip, and several small ones. The leaves on top of the rim have worn away in patches. The main zone also shows patches of wear, the surface revealing different colours, some paler clay, and some more orange. A white deposit is evident on the thick black band above the foot as well as some small scratches. The thin black band around the rim of the foot has mostly worn away. Inside, the black has scratches and flaked away to reveal the reserved clay. There is also more white deposit on the inside walls of the pot.
|
|
| 48.5.2
|
Major repair work done on one side and to neck consisting of nine pieces. Large chip to foot. Small chips to body. On most part of the figure decoration, handles, foot and mouth, black is fired to brownish. The gloss has flaked off from part of the figures, mouth and neck. White deposits around the mouth.
|
|
| 50.10.3
|
Intact. Preserved in a very good condition. large chip on one of the handles. Glaze flaked at small parts on the rim, on the interior, arund the foot ring. White depositions in the interior of the footring.
|
|
| 50.5.6
|
Intact. Paint appears extremely dull and matt despite being badly worn. Flaked off from most part of the decoration. Peach colour on small areas inside and corresponding exterior surface. A number of chips on the lower part of the base. The larger allows the clay inclusions (white stones) to show through.
|
|
| 51.1.3
|
Chips on both the exterior and the interior of the rim. Chips on the body. Cracks are apparent on the body of the krater and two large fragments on the body have been filled in. The gloss is not lustrous and was flaked off the rim, on the top of one of the handles and part of the body and the foot.
|
|
| 51.4.8
|
Complete. The body mended from a number of joining fragments. Glaze flaked off on the top of the rim, body and handles. Small chip on one of the horizontal handles. The main zone decoration remains similarly intact, except for a few scratches on the surface, and in small patches, a misty light grey deposit. There is also some of this deposit around the ends of all three handles. Thinly applied glaze, especially on the back side of the vessel, allowing for the colour of the clay to be seen. On the resting surface of the foot is a chalky white deposit.
|
|
| 51.4.9
|
Chips on the shoulder, body. Glaze on the rim large part of the foot and handle flaked off. Red colour faded. Occasional scratches on the body.
|
|
| 56.8.3
|
Large chip on the rim. Glaze flaked off at parts of the interior, on the handles and the rim. Gloss is not lustrous and it is not well applied on the lower part of the body.
|
|
| 56.8.7
|
Glaze flaked off the stem, base, undeside and the interior. It has been fired reddish brown. Remains of a label on underside.
|
|
| 56.8.8
|
The vase is reconstructed from many fragments. Bits have peeled and pitted off, and there are a few gouges. Gloss is lustreless, parts flaked off on the interior, handles, foot. At parts of the rim and the handles fired brownish.
|
|
| 60.1.5
|
Intact and complete; slightly scratched and chipped on body. Glaze flaked off mouth, neck, handle and ring foot.
|
|
| 60.8.2
|
Complete and intact, but in fairly bad condition. It has been badly fired, which has left the glaze patchy, especially on the back of the body. Fired to reddish brown. Around the rim of the mouth, the glaze has been worn and scratched away to reveal the reserved clay, as it has around the handles. The decoration on the main zone is still fairly visible, but is worn in patches and flaking around the edges. At many parts, clay flaked off. Around the top of the foot is greyish white deposit, also evident around the handles. There is a large chip in the foot. White has faded.
|
|
| 61.6.4
|
Complete and intact. Pitted slightly at the back of the body. Surface decoration flaked off on lower part of body and foot at the back
White deposits on left handle; white stain over front of body large white (salt?) deposit. One of the handles also has this white deposit and the upper part of the footring.
|
|
| 71.6.3
|
Complete but repaired. Figures remain clear but the black glaze has become streaky. Paint surface flaked away inside by one handle revealing the clay.
|
|
| 74.7.3
|
Small chip on rim, where gloss is worn; Good quality black gloss; Gloss flaked off rim and around the ring of the foot; white deposits on inside and on handle. Red misfired line around the ring of the foot probably caused during the firing in the kiln.
|
|
| 76.6.1
|
Lip and frontal part of the neck is chipped. Handle assempled from three fragments. Black paint is dull and has been flaked off largely. The surface has a 'dusty' appearance.
|
|
| REDMG:1935.87.11
|
Large chip missing from rim on one edge. Some gloss worn inside the cup where portions have flaked.
|
|
| REDMG:1935.87.2
|
Complete and intact. The amphora is in good condition, showing little signs of wear, as the glaze has flaked in little patches. There is one small chip on the rim and a few around the foot. There is a little bit of greyish deposit around the top of the foot and the rim of the mouth. On the resting surface of the foot is a small amount of brown deposit.
|
|
| REDMG:1935.87.31A
|
Complete but repaired; decoration has mostly flaked off.
|
|
| REDMG:1935.87.8
|
Intact. Paint inside has flaked away in small areas. Glaze remains shiny on exterior.
|
|
| REDMG:1953.25.23
|
Mouth missing. The surface has flaked away on much of the object, and it is pitted at the back; base and top of foot are chipped.
|
|
| TEMP.2003.6.10
|
Three fragments of the same vessel's base. It appears that the body has mostly been scraped off around the joining point at the upper parts of the fragments, apart from a bit on b and two bits on c. a) There are adhesives on the interior and few spots have been chipped off. There are three tiny spots on the interior and a spot on the central part of the base, where there are also three cracks. b) Two tiny bits have been chipped off from the interior and a spot looks flaked off from the inner side surface of the foot. There are also traces of adhesives. c) Four very small parts have been chipped off from the interior. There are also traces of adhesives, especially on the interior, as well as two cracks on the central part of the base.
|
|
| TEMP.2003.6.8
|
Seven fragments that belong to the same vessel. There is white plaster on both sides of each fragment. b) Adhesives on the exterior. The black gloss has been peeled off at some areas. e) Adhesives, especially on the external left side of the fragment. f) Small bits have been pitted off, and a shallow scratch on the lowest part of the body and a cracking on the central part of the resting surface. g) Looks like it has been flaked off from the vessel.
|
|